Reliability of Low-Temperature Poly-Si Thin Film Transistors with Lightly Doped Drain Structures
スポンサーリンク
概要
- 論文の詳細を見る
We have investigated the hot carrier degradation of n-ch poly-Si lightly doped drain thin film transistors (LDD-TFTs) under dynamic stress with various annealing conditions after LDD doping. Degradation of ON current was observed in the LDD-TFT. Observation with an emission microscope suggested the generation of hot electrons under dynamic stress. We have successfully clarified the relationship between the annealing temperature of the LDD region and hot carrier degradation. The thin film transistor with higher annealing temperature showed higher reliability. From the crystal analysis by Raman spectroscopy, it was determined that many defects were generated in the LDD region after doping. This shift of Raman peak indicated that residual stress caused by LDD doping is relieved by restructuring of the crystal network when the annealing temperature was over 500°C. Based on the results by electrical measurements and the Raman analysis, we have found that the degradation is strongly affected by the crystallinity of the LDD region.
- Published by the Japan Society of Applied Physics through the Institute of Pure and Applied Physicsの論文
- 2003-07-15
著者
-
Furuta Mamoru
Toshiba Matsushita Display Technology Co. Ltd.
-
URAOKA Yukiharu
Graduate School of Materials Science, Nara Institute of Science and Technology
-
Fuyuki Takashi
Graduate School Of Material Science Nara Institute Of Science And Technology
-
Uraoka Y
Nara Inst. Of Sci. And Technol. Nara Jpn
-
Uraoka Yukiharu
Graduate School Of Materials Science Nara Institute Of Science And Technology
関連論文
- Investigation of Near-Interface Traps Generated by NO Direct Oxidation in C-face 4H-SiC Metal-Oxide-Semiconductor Structures
- Novel Stacked Nanodisk with Quantum Effect Fabricated by Defect-free Chlorine Neutral Beam Etching
- A New Silicon Quantum-Well Structure with Controlled Diameter and Thickness Fabricated with Ferritin Iron Core Mask and Chlorine Neutral Beam Etching
- Evaluation of Crystallinity in 4H-SiC{0001} Epilayers Thermally Etched by Chlorine and Oxygen System
- Floating Nanodot Gate Memory Devices Based on Biomineralized Inorganic Nanodot Array as a Storage Node
- Analysis of Photoelectrochemical Processes in α-SiC Substrates with Atomically Flat Surfaces
- Electron Injection into Si Nanodot Fabricated by Side-Wall Plasma Enhanced Chemical Vapor Deposition
- Fabrication of Anodic Oxidation Films on 4H-SiC at Room Temperature Using HNO_3-Based Electrolytes
- Role of Hydrogen in Dry Etching of Silicon Carbide Using Inductively and Capacitively Coupled Plasma
- Degradation in Low-Temperature Poly-Si Thin Film Transistors Depending on Grain Boundaries