Effect of Nanotopography on Chemical Mechanical Polishing : Polishing Depth, Pad, Slurry and Interlayer Film Dependencies

スポンサーリンク

概要

• 論文の詳細を見る

• The impact of nanotopography was studied in oxide chemical mechanical polishing (CMP). In order to investigate the film removal depth and polishing pad dependencies, oxide films on wafers were repeatedly polished using two types of polishing pads having different compressibility (soft pad and hard pad). The power spectral density (PSD) of the film thickness variations got closer to that of nanotopography during CMP. We proposed a transfer function defined as the ratio of PSD of the film thickness variation to that of nanotopography. The calculated transfer functions clearly showed that nanotopography has an impact on film thickness variation for longer wavelengths as the removal depth gets larger and when using the hard pad. In addition, single-side-polished (SSP) wafers prepared using six different methods were examined following unpatterned oxide CMP. We found a clear and positive correlation between the standard deviation of the nanotopography profile and that of the film thickness variation after CMP. Through this correlation, the slurry type dependency (commercial silica and ceria slurry) of nanotopography was also investigated. With each optimized condition, ceria slurry caused greater film thickness variation due to nanotopography than silica slurry after unpatterned oxide CMP.

• 社団法人電子情報通信学会の論文
• 2002-06-24

著者

• Paik U

  Department Of Ceramic Engineering Hanyang University

• Park J‐g

  Nano-soi Process Laboratory Hanyang University

• Park Jea-gun

  Nano-SOI Process Laboratory, Hanyang University

• KATOH Takeo

  Nano-SOI Process Laboratory, Hanyang University

• Park Jea-gun

  Nano-soi Process Laboratory Hanyang University

• KATOH Takeo

  Advanced Semiconductor Material and Device Development Center, Hanyang University

• Kwack Kae-dal

  Nano Soi Process Laboratory Hanyang University

• Kwack Kae-dal

  Advanced Semiconductor Material And Device Development Center Hanyang University

• PARK Jea-Gun

  Advanced Semiconductor Material and Device Development Center, Hanyang University

• PARK Jin-hyung

  Advanced Semiconductor Material and Device Development Center, Hanyang University

• PAIK Ungyu

  Advanced Semiconductor Material and Device Development Center, Hanyang University

• Park Jea-gun

  Advanced Semiconductor Material And Device Development Center Hanyang University

• Park Jea-gun

  Advanced Semiconductor Material & Device Development Center Hanyang University

• Katoh Takeo

  Nano-soi Process Laboratory Hanyang University

• Kwack Kae-dal

  Advanced Semiconductor Material & Devices Development Center Hanyang University

関連論文

• Non-volatile Memory Fabricated with Al Nanocrystals Embedded in Conductive-Low-Molecular-Organic Layers(Session 3 Emerging Devices and Technologies I,AWAD2006)
• Non-volatile Memory Fabricated with Al Nanocrystals Embedded in Conductive-Low-Molecular-Organic Layers(Session 3 Emerging Devices and Technologies I,AWAD2006)
• Dependence of pH, Molecular Weight, and Concentration of Surfactant in Ceria Slurry on Saturated Nitride Removal Rate in Shallow Trench Isolation Chemical Mechanical Polishing
• Effects of Abrasive Size and Surfactant Concentration on the Non-Prestonian Behavior of Ceria Slurry in Shallow Trench Isolation Chemical Mechanical Polishing
• Effect of Molecular Weight of Surfactant in Nano Ceria Slurry on Shallow Trench Isolation Chemical Mechanical Polishing (CMP)
• Effects of Grain Size and Abrasive Size of Polycrystalline Nano-particle Ceria Slurry on Shallow Trench Isolation Chemical Mechanical Polishing
• Reduction of Large Particles in Ceria Slurry by Aging and Selective Sedimentation and its Effect on Shallow Trench Isolation Chemical Mechanical Planarization
• Effect of Calcination Process on Synthesis of Ceria Particles, and Its Influence on Shallow Trench Isolation Chemical Mechanical Planarization Performance
• The Effect of Cerium Precursor Agglomeration on the Synthesis of Ceria Particles and Its Influence on Shallow Trench Isolation Chemical Mechanical Polishing Performance
• Agglomerated Large Particles under Various Slurry Preparation Conditions and Their Influence on Shallow Trench Isolation Chemical Mechanical Polishing
• A Reverse Selectivity Ceria Slurry for the Damascene Gate Chemical Mechanical Planarization Process
• Influence of Physical Characteristics of Ceria Particles on Polishing Rate of Chemical Mechanical Planarization for Shallow Trench Isolation
• Effect of Slurry Surfactant on Nanotopography Impact in Chemical Mechanical Polishing
• Effects of Physical Characteristics of Cerium Oxide of Plasma-Enhanced Tetraethylorthosiliate Removal Rate of Chemical Mechanical Polishing for Shallow Trench Isolation
• Effects of Abrasive Morphology and Surfactant Concentration on Polishing Rate of Ceria Slurry
• Dependence of Nanotopography Impact on Abrasive Size and Surfactant Concentration in Ceria Slurry for Shallow Trench Isolation Chemical Mechanical Polishing
• Surfactant Effect on Oxide-to-Nitride Removal Selectivity of Nano-abrasive Ceria Slurry for Chemical Mechanical Polishing
• The Nanotopography Effect of Improved Single-Side-Polished Wafer on Oxide Chemical Mechanical Polishing : Semiconductors
• Effect of Dispersant Addition during Ceria Abrasive Milling Process on Light Point Defect (LPD) Formation after Shallow Trench Isolation Chemical Mechanical Polishing (STI-CMP)
• Spectral Analyses on Pad Dependency of Nanotopography Impact on Oxide Chemical Mechanical Polishing : Semiconductors
• Extended Defects and Pile-Up of Interstitial Oxygen in Silicon Wafer Due to MeV-Level Nitrogen Ion Implantation
• Nanotopography Impact and Non-Prestonian Behavior of Ceria Slurry in Shallow Trench Isolation Chemical Mechanical Polishing (STI-CMP)
• 14-O-26 Influence of Passivating Agents on the Dissolution Behavior of Barium Titanates in an Aqueous Medium
• The Stability of Nano Fwned Silica Particles and Its Influence on Chemical Mechanical Planarization for Interlayer Dielectrics
• Effect of Nanotopography on Chemical Mechanical Polishing : Polishing Depth, Pad, Slurry and Interlayer Film Dependencies
• Effect of Nanotopography on Chemical Mechanical Polishing : Polishing Depth, Pad, Slurry and Interlayer Film Dependencies
• Dependency of Precipitation of Interstitial Oxygen on Its Crystal Nature in Czochralski Silicon Wafer
• Spectral Analyses of the Impact of Nanotopography of Silicon Wafers on Oxide Chemical Mechanical Polishing : Semiconductors
• Effect of Chemicals and Slurry Particles on Chemical Mechamical Polishing of Polyimide
• Crystal Originated Particle Induced Isolation Failure in Czochralski Silicon Wafers
• Advanced Czochralski Single Silicon Crystal Growth (特集:21世紀を担うバルク単結晶) -- (シリコン)
• Micro Defect Size in Si Single Crystal Grown by Czochralski Method
• Effect of Organic Additive on Surface Roughness of Polycrystalline Silicon Film after Chemical Mechanical Polishing
• Effects of the Physical Characteristics of Cerium Oxide on Plasma-Enhanced Tetraethylorthosiliate Removal Rate of Chemical Mechanical Polishing for Shallow Trench Isolation
• Dependence of Non-Prestonian Behavior of Ceria Slurry with Anionic Surfactant on Abrasive Concentration and Size in Shallow Trench Isolation Chemical Mechanical Polishing
• A Reverse Selectivity Ceria Slurry for the Damascene Gate Chemical Mechanical Planarization Process
• Influence of Physical Characteristics of Ceria Particles on Polishing Rate of Chemical Mechanical Planarization for Shallow Trench Isolation
• Effect of Molecular Weight of Surfactant in Nano Ceria Slurry on Shallow Trench Isolation Chemical Mechanical Polishing (CMP)
• Effects of Grain Size and Abrasive Size of Polycrystalline Nano-particle Ceria Slurry on Shallow Trench Isolation Chemical Mechanical Polishing
• Nanotopography Impact and Non-Prestonian Behavior of Ceria Slurry in Shallow Trench Isolation Chemical Mechanical Polishing (STI-CMP)
• Dependence of Nanotopography Impact on Abrasive Size and Surfactant Concentration in Ceria Slurry for Shallow Trench Isolation Chemical Mechanical Polishing
• Effects of Abrasive Morphology and Surfactant Concentration on Polishing Rate of Ceria Slurry
• Dependency of Precipitation of Interstitial Oxygen on Its Crystal Nature in Czochralski Silicon Wafer
• Nature of Surface and Bulk Defect Induced by Low Dose Oxygen Implantation in Separation by Implanted Oxygen Wafers
• Nonvolatile Polymer Memory-Cell Embedded with Ni Nanocrystals Surrounded by NiO in Polystyrene

もっと見る 閉じる

スポンサーリンク