Control of Interfacial Reaction of HfO2/Ge Structure by Insertion of Ta Oxide Layer

概要

論文の詳細を見る
As means to control interface reactions between HfO2 and Ge(100), chemical vapor deposition (CVD) of ultrathin Ta-rich oxide using Tri (tert-butoxy) (tert-butylimido) tantalum (Ta-TTT) on chemically-cleaned Ge(100) has been conducted prior to atomic-layer controlled CVD of HfO2 using tetrakis (ethylmethylamino) hafnium (TEMA-Hf) and O3. The XPS analysis of chemical bonding features of the samples after the post deposition N2 annealing at 300°C confirms the formation of TaGexOy and the suppression of the interfacial GeO2 layer growth. The energy band structure of HfO2/TaGexOy/Ge was determined by the combination of the energy bandgaps of HfO2 and TaGexOy measured from energy loss signals of O 1s photoelectrons and from optical absorption spectra and the valence band offsets at each interface measured from valence band spectra. From the capacitance-voltage (C-V) curves of Pt-gate MIS capacitors with different HfO2 thicknesses, the thickness reduction of TaGexOy with a relative dielectric constant of 9 is a key to obtain an equivalent SiO2 thickness (EOT) below 0.7nm.