Aluminum Brazing Filler Metals for Making Aluminum to Titanium Joints in a Vacuum(Physics, Process, Instrument & Measurement)
スポンサーリンク
概要
- 論文の詳細を見る
A spread test on Ti-base metal and a clearance filling test on Al/Ti joint were performed under vacuum condition to investigate the appropriate composition of aluminum filler metals. The spread area on Ti-base metal depended on the surface area of titanium in a brazing furnace due to an effective gettering action of titanium. Magnesium bearing brazing sheets were also effective getter materials. Al-10Si-Mg alloy was the most suitable filler metal for vacuum brazing of Al/Ti joints, and it made sound fillets at 600℃. Al-10〜12.5Cu-5〜8Sn and Al-20Ag-10Cu filler metals were also applicable at brazing temperatures of 600〜620℃. The joint strength is however, only a half of that of the Al-10Si-Mg filler metals.
- 大阪大学の論文
著者
-
Okamoto Ikuo
Osaka University
-
Okamoto Ikuo
Welding Research Institute Of Osaka University
-
TAKEMOTO Tadashi
Osaka University
-
Takemoto Tadashi
Department of Experimental Radiology, Shiga University of Medical Science
-
Takemoto Tadashi
Department Of Experimental Radiology Shiga University Of Medical Science
-
Takemoto T
Osaka Univ. Osaka Jpn
-
NAKAMURA Hideyuki
Osaka University
-
Nakamura H
Osaka University:(present Office)ube Industries Ltd.
関連論文
- Wetting and Reaction Products Formed at the Interface Between SiC and Cu-Ti Alloys
- Wetting of Silicon Carbide by Copper-Titanium Alloys(Physics, Process, Instrument & Measurement)
- Physical Meaning of Wetting Curve Traced by Meniscograph Wettability Tester (Report II) : Kinetic Consideration of Flux Action in Soldering(Welding Physics, Process & Instrument)
- Physical Meaning of Wetting Curve Traced by Meniscograph Wettability Tester(Welding Physics, Process & Instrument)
- High Rate Sputtering of Corrosion-Resistant Alloys(Welding Physics, Processes & Instruments)
- Studies on Dissolution of Metal Element from Flux (Report II) : Dissolution of Ag to Molten Zn-Cd Alloys
- Studies on Flux Action of Silver Brazing (Report I) : Metallic Chlorides
- Spreading of BAg-5 on Pre-Flux Coated Stainless Steel Plate : Function of Fluxes Mixed with NiCl_2 or FeCl_3
- THE ORIGIN AND THE EVOLUTION OF THE THIOESTER-CONTAINING PROTEIN(Physiology,Abstracts of papers presented at the 74^ Annual Meeting of the Zoological Society of Japan)
- FUNCTIONAL INVESTIGATION OF THE DRP/DHP/CRAM/UNC-33 FAMILY IN PLANARIANS, DUGESIA JAPONICA(Developmental Biology,Abstracts of papers presented at the 74^ Annual Meeting of the Zoological Society of Japan)
- Studies on Flux Action of Soldering (Report VII) : Flux Action of various Silver and Copper Salts on Ni and Fe plates
- Studies on Flux Action of Soldering (Report VI) : Effect of Metal Salts on Dissolution of Zn in Molten Sn
- Studies on Flux Action of Soldering (Report V) : Reaction of Flux and Wetting
- Studies on Flux Action of Soldering (Report IV) : Inorganic Metal Salts
- Studies on Flux Action of Soldering (Report III) : Organic Metal Salts
- Studies on Flux Action of Soldering (Report II) : Amine Hydrochloride
- Estimations of Some Unknown Viscosities and Self-diffusivities for Liquid Metals
- Trial Product of Dynamic Co-Axial Cylinder (DCC) Viscometer for Molten Metals, Slags and Salts to 1200℃
- A Phenomenological Theory of Viscosities of Liquids
- Ultrasonic Brazing of Alumina to Copper Using Zn-Al Filler(Materials, Metallurgy & Weldability)
- Influence of Brazing Condition on Shear Strength of Alumina-Kovar Joint Made with Amorphous Cu_Ti_ Filler Metal
- Corrosion Behavior of Amorphous Fe-Cr-Zr Alloys
- Effect of Chromium Addition on Corrosion Resistance of Amorphous Co-Zr Alloys
- Flow of Brazing Filler Metal and Flux
- Studies on Dissolution of Metal Element from Flux (Report-I) : Dissolution of Ag to Molten Tin and Tin Base Binary Alloys
- Reaction of Fused Salts with Molten Zn-Sn and Zn-Cd Alloys (1)
- 3'-Blocking Damage of DNA as a Mutagenic Lesion Caused by Hydrogen Peroxide in Escherichia coli
- Effect of Hole in Brazing Sheet on Vacuum Brazability of Aluminum Tubes
- Erosion of Pure Copper by Copper Phosphorus Brazing Filler Metals containing Tin and Silver : Copper Phosphorus Brazing Filler Metals with Low Melting Temperature (Report V)(Physics, Process, Instrument & Measurement)
- Spreading of Copper Phosphorus Brazing Filler Metals with Low Melting Temperature containing silver and/or Tin : Copper Phosphorus Brazing Filler Metals with Low Melting Temperature (Report IV)(Physics, Process, Instrument & Measurement)
- Liquidus Surface of Quaternary Copper Phosphorus Brazing Filler Metals with Silver and Tin : Copper Phosphorus Brazing Filler Metals with Low Melting Temperature (Report III)(Materials, Metallurgy & Weldability)
- Phase Diagrams of Cu-Ag-P and Cu-Sn-P Ternary Brazing Filler Metals : Copper Phosphorus Brazing Filler Metals with Low Melting Temperature-Report II(Materials, Metallurgy & Weldability)
- High Temperature Corrosion of Nickel Based Heat Resistant Alloys and their Diffusion Brazed Parts(Materials, Metallurgy & Weldability)
- Laser Metallization of Ceramics
- Heat-Resistant Brazing of Ceramics (Report I) : Brazing of SiC Using Ni-Ti Filler Metals(Physics, Process, Instrument & Measurement)
- An Approach to Viscosity Calculations of Molten Iron and Its Dilute Binary Alloys
- Amorphous Alloy and Its Application to Joining
- Joining of Alumina to Copper Using Amorphous Cu-Ti Filler Metal(Materials, Metallurgy & Weldability)
- Joining of Al_2O_3 to SUS 304 with Ti Foil
- Wetting of Zirconia by Cu-Zr Alloys
- Reaction of Iron-based Alloys with Molten Lead-free Solder(Materials, Metallurgy & Weldability)
- Sacrificial Anode Type Al-10Si-1Mg Brazing Filler Metals for Suppression of Corrosion of Brazed 3003 Aluminum Alloy(Materials, Metallurgy & Weldability)
- Brazing of Si_3N_4 to Metals with Al-Cu Filler Metals(Physics, Process, Instrument & Measurement)
- Brazing of Si_3N_4 to Metals with Al Filler (Report II) : Si_3N_4/Fe, Ni, Cu, Al or SUS304 Joint(Physics, Process, Instrument & Measurement)
- Brazing of Si_3N_4 to Metals with Al Filler (Report I) : Si_3N_4/Si_3N_4 and Si_3N_4/Ti or Nb Joints(Materials, Metallurgy & Weldability)
- Intermediary Layer of Titanium Oxide in Al_2O_3/Cu Joint Using Amorphous Cu-Ti Filler Metals
- Formation of Hercynite (FeAl_2O_4) at Interface of Al_2O_3/Steel Joint
- Conditions for the Measurement of Surface Tension of Solders with a Wetting Balance Tester(Materials, Metallurgy & Weldability)
- Vacuum Brazing Tests on Powder Aluminum Brazing Filler Metals(Materials, Metallurgy & Weldability)
- Effect of Flux Composition on Wettability in Soldering of Aluminum(Materials, Metallurgy & Weldability)
- Effect of Curvature on Fillet Formation during Aluminum Brazing(Materials, Metallurgy & Weldability)
- Strength of Titanium Joints Brazed with Aluminum Filler Metals(Physics, Process, Instrument & Measurement)
- Aluminum Brazing Filler Metals for Making Aluminum to Titanium Joints in a Vacuum(Physics, Process, Instrument & Measurement)
- Appiication of Amorphous Cu-Ti Filler Metal to Joining of Silicon Nitride
- Joining of Silicon Nitride Using Amorphous Cu-Ti Filler Metal(Materials, Metallurgy & Weldability)
- Joining of SiC Using Amorphous Ti Base Filler Metal(Materials, Metallurgy & Weldability)
- Joining of Silicon Nitride to Metals or Alloys Using Amorphous Cu-Ti Filler Metal(Materials, Metallurgy & Weldability)
- Non-oxide Ceramics (Si_3N_4, SiC) Joint Made with Amorphous Cu_Ti_ and Ni_Ti_ Filler Metals
- Analysis of Temperature Field with Equiradial Cooling Boundary around Moving Heat Sources : Heat Conduction Analysis for Estimation of Thermal Hysteresis during Underwater Welding(Welding Physics, Processes & Instruments)
- Spreading of BAg-5 on Pre-Flux Coated Stainless Steel Plate (Report II) : Function of Fluxes Mixed with CuCl or CoCl_2(Welding Physics, Processes & Instruments)
- H_2S Gas Corrosion Resistance of Copper Joints Brazed with Low Melting Temperature Copper Phosphorus Brazing Filler Metals(Mechanics, Strength & Structural Design)
- Copper Phosphorus Brazing Filler Alloys with Low Melting Temperature (Report I) : Effect of Tin Addition
- Interaction between Supersonic Jet and Burning Iron Wall in Oxygen Gas Cutting (Part II) : Combustion Stability and Flame Cutting Mechanism(Welding Physics, Process & Instrument)
- Interaction between Supersonic Jet and Burning Iron Wall in Oxygen Gas Cutting (Part I) : Shock Wave Behaviour and Combustion Phenomena(Welding Physics, Process & Instrument)
- Bonding Behavior between Niobium and Reaction-Sintered SiC(Materials, Metallurgy & Weldability)
- Pressure and Field-Assisted Bonding of Glass to Aluminum(Materials, Metallurgy & Weldability)
- Studies on Flux Action of Soldering (Report-1) : Stearic Acid
- Stress Corrosion Cracking Mechanism of Cu-4% Ti Alloy(Welding Mechanics, Strength & Design)
- Forschung in Bezug auf die Lotbruchigkeit von Kohlenstoffstahl (Bericht 3) : EinfluB der Zuggeschwindigkeit auf die Lotbrilchigkeit(Materials, Metallurgy & Weldability)
- Study on Liquid Metal Embrittlement of Carbon Steels (Report 2) : Effect of Erosion of Carbon Steel in Liquid Metals on LME(Materials, Metallurgy & Weldability)
- Study on Liquid Metal Embrittlement of Carbon Steels (Report 1) : Penetration Behavior of Liquid Metal(Welding Physics, Processes & Instruments)
- Some Fundamental Research of New Type Powder Oxygen Cutting Method for Stainless Steel(WELDING PHYSICS, PROCESSES AND INSTRUMENTS)
- A Study on Tunneling Flow of Filler Metal in Aluminum Brazing(Welding Physics, Processes & Instruments)
- Analysis of Temperature Distribution with Radial Symmetrical Cooling Terminal around Moving Heat Source
- Vacuum Brazing of Aluminum Using Al-12%Si System Filler Alloy
- Vacuum Brazing of Aluminum Using Al-12%Si System Filler Alloy
- Electrochemical Actions of Flux for Soldering
- Selection of Optimum Cu Content in Cu Bearing Tin-Lead Solder(Materials, Metallurgy & Weldability)
- Wetting of Alumina by Molten Aluminum and Aluminum-Copper Alloys(Welding Physics, Process & Instrument)
- Occurrence of Non-Wetted Parts in Dip Soldering (Report-1)(Welding Physics, Processes & Instruments)
- Joining Al_2O_3 to Al_2O_3 by Brazing
- Stress Corrosion Cracking and Anodic Dissolution Behavior of 5083 Aluminum Alloy(Materials, Metallurgy & Weldability)
- Studies on Brazability of Electric Contact Chip Materials (Report I) : Effect of Surface Preparation of Sintered Tungsten Alloys on Wetting of BAg Filler Metals
- Soldering Temperature and Wetting Temperature
- Effect of Iron Content in Brazing Filler Metals on Corrosion of Brazed Aluminum(Materials, Metallurgy & Weldability)
- Wetting of Silicon Nitride by Copper-Titanium or Copper-Zirconium Alloys(Welding Physics, Process & Instrument)
- Bonding of Alumina using Cupreous Oxide as Insert Material
- Corrosion Behaviour of Silver Brazed Stainless Steel in Chloride Solutions(Materials, Metallurgy, Weldability)
- Vacuum Brazing of Aluminum (Report-I) : Effect of Surface Treatment
- Corrosion Mechanism of Silver Brazed Stainless Steel Joint in Chloride Solutions(Materials, Metallurgy, Weldability)
- Vacuum Brazing of Aluminum (Report-II) : Effect of Emery Paper Grinding
- Cutting of Stainless Steel by New Type Powder-Oxygen Cutting Method
- Fundamental Characteristics of the Hollow Cathode Arc as Welding Heat Source(Physics, Processes, Instruments & Measurements, INTERNATIONAL SYMPOSIUM OF JWRI 30TH ANNIVERSARY)
- Brazability of Aluminum using Al-Si Filler Alloys with Different Compositions and Microstructures
- Effect of Bismuth Addition to Brazing Sheet Claddings on Fluxless Brazability of Aluminum(Welding Physics, Process & Instrument)
- Brazability and Erosion by Molten Filler Alloy of Aluminum Base Plates with Intermetallic Compounds(Materials, Metallurgy & Weldability)
- Parallel Gap Resistance Welding of Lead Wires to Metal Spray Coating Films
- Studies on Flux Action of Soldering (Report VIII) : Dissolution and Adsorption Effect
- Relation Between Spreading Area and Penetration Height in Soldering : On Wetting
- The Crystallization Kinetics of Glassy Fe_ Ni_ P_