ガラスレンズ成形金型材料用アモルファス合金のコンビナトリアル探索 : 結晶化開始温度,機械特性の評価

概要

論文の詳細を見る
New compositions of a Pt-Zr-Ni amorphous alloy as a mold material for glass lens production were searched using a new combinatorial synthesis called the combinatorial arc plasma deposition (CAPD). First, 3,267 thin film samples of 1 mm x 1 mm size were deposited by CAPD. The phase and composition of 883 samples of the thickness more than 500 nm were evaluated and 312 amorphous samples were found. Secondly, six amorphous samples expected to have a high crystallization temperature (Tx) and a high tensile strength (σ_B) were deposited using a sputtering system because CAPD samples were too small and thin to evaluate mechanical property such as σ_B,Young's modulus, elastic limits and anti-sticking with melted glass. Finally, Pt_<50>Zr_<36>Ni_<14> was found as a new mold material of a high Tx (985 K), a high σ_B (2.12 GPa) and anti-sticking. The new mold material was also expected to have a high resistance to oxidation at a high temperature range of glass molding.
社団法人精密工学会の論文
2008-03-05