Ferromagnetic tunneling junctions with various thicknesses of the first ferromagnetic layer were fabricated. Co and Ni_<80>Fe_<20> were used as the first ferromagnetic layer, and their thicknesses were varied between 10 and 200Å. The voltage and temperature dependence of the tunneling magnetoresistance (TMR) ratio and conductance characteristic were investigated for these junctions. A drastic decrease in the conductance near the zero bias in the conductance-voltage characteristics (zero-bias anomaly) was observed in some junctions. A rapid decrease in the TMR ratio below 5 mV and 50 K was also observed in the same junctions. A slight decrease in the TMR ratio above 10 mV and 100 K was observed in all junctions. We investigated the origin of the voltage and temperature dependence of the TMR ratio by taking account of the magnetic impurity and magnon effect.
- 社団法人日本磁気学会の論文
- 1999-04-15
著者
-
大兼 幹彦
東北大学大学院工学研究科応用物理学専攻
-
宮崎 照宣
東北大学大学院工学研究科応用物理学専攻
-
手束 展規
東北大工
-
手束 展規
東北大学大学院工学研究科材料物性学
-
手束 展規
東北大学大学院工学研究科
-
宮崎 照宣
東北大学大学院 工学研究科
-
大兼 幹彦
東北大学大学院工学研究科
関連論文
- ホイスラー合金系ハーフメタルCo_2MnSiを用いた高感度磁気抵抗素子の開発(ハードディスクドライブおよび一般)
- ホイスラー合金系ハーフメタルCo_2MnSiを用いた高感度磁気抵抗素子の開発(ハードディスクドライブ及び一般)
- 超高密度磁気メモリ (特集2 ユビキタス社会を拓く次世代電子デバイス)
- [特別招待講演]超ギガビット磁気メモリ基盤技術の開発(MRAM,不揮発メモリ,メモリ,一般)
- 3-2 スピンエレクトロニクス技術の発展と固体磁気メモリへの応用 : 3. ナノ電子材料(ナノテクノロジーの光とエレクトロニクスへの応用)
- スピンポンピングによるスピン流の創出と物理現象
- 26aVD-7 垂直磁化Pt/Co/Pt三層膜における時間分解磁気光学効果(スピン流・スピンホール,領域3,磁性,磁気共鳴)
- Co_2FeMnSiホイスラー合金の磁気緩和定数
- 高アニール耐性・高反平行結合強度を有する積層フェリ構造の開発
- Co_2MnSiを電極とする微小二重トンネル接合の作製と評価