カリウム・コロイドを含むヨウ化カリウム単結晶における電界発光(III)

概要

論文の詳細を見る
In order to investigate the phenomenon of electroluminescence,EL,in KI single crystals containing potassium metal colloids it is essential to clarify the formation processes of the colloids during thermal annealing treatment.In the previous report a simple measurement system for the observation of the photoacoutic signal(PAS)was fabricated.Through PAS measurements we could obtain an information about the behavior of potassium metal colloids existing near specimen surfaces in the course of the thermal annealing treatments.The potassium metal colloids existing in the bulk of the speciments,however,may play a dominant role in the electroluminescence phenomenon.In order to make clear the aggregation andor the dissolving processes of the potassium metal colloids in the bulk of the specimens various measurements of the optical absorption of the specimens subjected to the isothermal annealings were performed.It was found that isothermal annealing treatment at 90℃ for 48 hours of densely colored KI specimen could supply a specimen containing potassium metal colloid of dominant size of about 30nm.Using this specimen detailed EL observations were carried out as a function of the applied field strength.Brief discussion is given concerning the characteristic behavior of the potassium metal colloids from the point of view of defect aggregation processes.カリウム・コロイドを含むKI単結晶における電界発光の機構を明らかにするために，これまでにコロイドの導入法の確立とその評価法について研究成果の報告を行った。カリウム・コロイドに関する諸物性と関連付けて電界発光現象の機構の詳細を考察するに際して，試料中に存在するカリウム・コロイドの形状・大きさ・分布状態を知る必要がある。本研究では，付加着色法によってF中心を高濃度（～10＾18個／cm＾3）に注入した試料を用いて詳細な等温焼鈍実験を行った。その結果，約350℃の温度で乾燥窒素ガス雰囲気中，2時間焼鈍した後急冷をすることによって，主としてFとF＿2のみを含む試料が得られることがわかった。さらに，90℃の温度で最高72時間までの焼鈍過程を光学吸収測定を行うことにより追跡した。その結果，ほぼ48時間の熱処理で直径30nm程度のカリウム・コロイドが優勢的に形成されることがわかった。この試料を用いて電界発光の観測をも行い，これまでに得た結果と合わせて，格子欠陥凝集の立場を基礎として発光機構についての検討並びに考察を行った。
大阪教育大学の論文

カリウム・コロイドを含むヨウ化カリウム単結晶における電界発光(III)

スポンサーリンク

概要

著者

関連論文

スポンサーリンク