カリウム・コロイドを含むヨウ化カリウム単結晶における電界発光(II)

概要

論文の詳細を見る
In order to investigate the phenomenon of electroluminescence in KI single crystals containing potassium metal colloids it is essential to obtain an information as to the formation mechanism of potassium metal colloids in crystals.A simple measurement system for the detection of the photoacoustic signal(PAS)was fabricated to study the nature of the potassium colloids in the thermal annealing processes.In comparison the intensities revealed in PAS measurements with the results obtained from the optical absorption measurements,it was found that both results agree well semi-quantitatively.The iso-thermal annealing processes at about 85℃ of densely colored KI specimens were monitored by PAS measurements.It was seen that there exists an optimum annealing time,around 120min,to obtain the potassium metal colloids of size 20-30nm.Furthermore,by the elongation of the annealing time more than 200min,the PAS intensities were decreased according as the t^-12 law.Brief discussion is given concerning the characteristics of potassium metal colloids in the electrolytically colored KI crystals in terms of the defect aggregations.カリウム・コロイドを含むKI単結晶における電界発光現象の機構を明かにするためには，KI単結晶中におけるカリウム・コロイドの形成に関する知見を得ることをが必須である。この目的を遂行するために，簡単な光音響信号（PAS）測定装置を試作し，熱処理過程中におけるカリウム・コロイドの性質を調べた。本装置を用いて得た結果と光学吸収測定装置により得た結果とを比較することにより両者が半定量的ではあるがよく一致することが明かになった。85℃における等温焼鈍過程をPAS解析を行うことによって追跡した。その結果，20―30nmのカリウム・コロイドを形成するのには120分間程果の焼鈍が最適であり，また，200分以上の長時間焼鈍では時聞の－1／2乗則に従い上記サイズのカリウム・コロイドが消滅していくことが判明した。これらの結果を格子欠陥凝集過程の立場から検討を行った。
大阪教育大学の論文

カリウム・コロイドを含むヨウ化カリウム単結晶における電界発光(II)

スポンサーリンク

概要

著者

関連論文

スポンサーリンク