成品焼結鉱の CaCl_2 水溶液中への浸漬処理(焼結鉱)(<特集>製銑技術の拡大と高度化)

概要

論文の詳細を見る
The immersion of sinter into CaCl_2 aqueous solution and subsequent drying have been carried out. The immersion treatment of sinter was carried out at room temperature under the normal pressure and in vacuum. The CaCl_2 concentration of aqueous solution was changed from 1.0 to 10.0wt%. The effect of immersion treatment on the reducibility index (RI) and reduction degradation index (RDI) of sinter have been studied. The main results obtained are as follows : 1) On the immersion under the normal pressure, RI decreased only slightly and RDI decreased remarkably with increase of CaCl_2 concentration in solution. 2) On the immersion in vaccum, RI maintained the value of original sinter and RDI decreased more than the value on the immersion under the normal pressure. 3) Decrease of RDI of sinter was caused by the delay of the reduction rate due to adhered CaCl_2 layer in pore surface and resultant decrease of the amount of cracked magnetite particles.
社団法人日本鉄鋼協会の論文
1987-11-01