Low-Contact Resistance Poly-Metal Gate Electrode Using TiN/Thin TiSi_2/Poly-Si Structure
スポンサーリンク
概要
- 論文の詳細を見る
A low-contact resistance poly-metal gate system consisting of TiN/thin TiSi_2/poly-Si is described. A poly-metal gate is one of the candidates for the next generation of metal-oxide-semiconductor field effect transistor (MOSFET) gate structures. The characteristics between the barrier metal and the poly-Si are important in achieving a high-performance poly-metal gate structure. In this study, the inserting of a thin TiSi_2 layer between the TiN and the poly-Si produced a low-contact resistance between the TiN and the poly-Si, which was an acceptable improvement. The thinner the inserted TiSi_2, the lower the contact resistance. In n- and p-channel MOSFETs with a TiN/TiSi_2 (5 nm)/poly-Si gate structure having a gate oxide thickness of 4 nm, the lateral diffusion of the gate dopant was suppressed. This occurred because the inserted TiSi_2 was thin enough to prevent the gate dopants from moving through the TiSi_2.
- 社団法人応用物理学会の論文
- 1999-04-30
著者
関連論文
- Fabrication and Delay Time Analysis of Deep Submicron CMOS Devices
- Ti Salicide Process for Subquarter-Micron CMOS Devices (Special Issue on Quarter Micron Si Device and Process Technologies)
- Wafer Cleaning with Photoexcited Chlorine and Thermal Treatment for High-Quality silicon Epitaxy : Beam Induced Physics and Chemistry
- Advanced SOI Devices Using CMP and Wafer Bonding
- Coulomb Interaction Effect Correction in Electron-Beam Block Exposure Lithography
- Quantum-Size Effect from Photoluminescence of Low-Temperature-Oxidized Porous Si
- Synchrotron-Radiation-Induced Modification of Silicon Dioxide Film at Room Temperature : Beam Induced Physics and Chemistry
- Synchrotron-Radiation-Induced Modification of Silicon Dioxide Film at Room Temperature
- Synchrotron Radiation-Assisted Removal of Oxygen and Carbon Contaminants from a Silicon Surface
- Evaluation of Photoemitted Current from SiO_2 Film on Silicon During Synchrotron Radiation Irradiation
- Chemical Structures of Native Oxides Formed during Wet Chemical Treatments
- Synchrotron Radiation-Assisted Silicon Film Growth by Irradiation Parallel to the Substrate
- Evaluation of Shot Position Error in Electron Beam Lithography Using Overlay Metrology with 'One-Shot' Inspection Mark
- Impact Ionization in 0.1 μm Metal-Oxide-Semiconductor Field-Effect Transistors
- Trap Assisted Leakage Mechanism of 'worst' Junction in Giga-bit DRAM Using Negative Word-Line Voltage
- Impact of Metal Gate/High-k Interface in Mo Metal Gated MOSFETs with HfO_2 Gate Dielectrics
- Low Contact Resistance Poly-Metal Gate CMOS Using TiN/Thin TiSi_2/Poly-Si Structure
- Low-Contact Resistance Poly-Metal Gate Electrode Using TiN/Thin TiSi_2/Poly-Si Structure
- Process Integration Issues on Mo-Metal-Gated MOSFETs with HfO2 High-k Gate Dielectrics
- Highly Reliable Dynamic Random Access Memory Technology for Application Specific Memory with Dual Nitrogen Concentration Gate Oxynitrides Using Selective Nitrogen Implantation
- Wafer Cleaning with Photoexcited Chlorine and Thermal Treatment for High-Quality Silicon Epitaxy