K-0835 サブミクロンCu薄膜のはく離強度特性に及ぼす界面端近傍の特異応力場支配域の影響(S09-3 界面の特異性)(S09 特異点解析と強度評価への適用)

概要

論文の詳細を見る
The delamination tests are conducted for multi-films, Cu/TiN, on a Si-substrate with different thickness of Cu (50nm, l00nm and 500nm), and the effect of stress-singular region on the strength at the Cu/TiN interface edge is examined. In the tests, the stress-singular region is about 5nm, 10nm, and 40nm, respectively. The critical stress intensity in the specimen with the thinner Cu is larger in the one with the thicker Cu. It is found that the delamination in all tests takes place when the stress at γ<100nm reaches about 18〜19MPa. This signifies that the region of γ<100nm characterize the interface toughness and the size is larger than the stress-singular region in the specimen.
一般社団法人日本機械学会の論文
2001-08-22