<論文>高強度を有する急速凝固P/Mアルミニウム合金の耐摩耗性
スポンサーリンク
概要
- 論文の詳細を見る
High- strength P/M (powder metallurgy) aluminum alloys of Al-Ni-Y-Co, Al-Si-Ni-Ce and Al-Ti-Fe-TM(TM : Cr, Mo, V, Zr) systems were prepared by extrusion of rapidly solidified powders which were produced by high-pressure He gas atomization. It was found that wear resistance of the P/M aluminum alloys thus prepared was better than that of the conventional aluminum alloys. Al_<89>(Ni_<0.33>Y_<0.54>Co_<0.13>)_<11> alloy had the best wear resistance among the P/M aluminum alloys studied in this experiment. In order to investigate the cause of the difference of wear properties in those P/M aluminum alloys, wear traces and wear particles were analyzed by EPMA, SEM, TEM and Micro-Vickers hardness measurement. It was found that the hard oxide layer was formed on the surface of the wear trace in Al_<89>(Ni_<0.33>Y_<0.54>Co_<0.13>)_<11> alloy. However, in the case of Al_<78.5>Si_<19>Ni_2Ce_<0.5> alloy, wear particles were included in the surface of the wear trace. It is considered that the oxidation of wear surface and the stability of the formed oxide layer significantly influenced wear resistance of the P/M aluminum alloy.
- 1999-06-30
著者
-
井村 徹
愛知工業大学機械工学科
-
岩田 博之
愛知工業大学工学部電子工学科
-
高木 誠
愛知工業大学工学部機械学科
-
高木 誠
愛知工大
-
河村 能人
東北大学金属材料研究所
-
井村 徹
愛知工業大学 工学部 機械学科
-
河村 能人
Dep. Of Materials Sci. Kumamoto Univ.
-
岩田 博之
愛知工業大学
-
高木 誠
愛知工業大学
-
大田 英伸
愛知工業大学大学院
-
大田 英伸
名大院
-
岩田 博之
愛工大
関連論文
- RBS/Cを用いた水素イオン注入欠陥の評価
- 超高速プラズマ照射とレーザー超急冷による表面改質(一般研究)
- IDCロボットコンテスト
- TiO_2/SiO_2複合ナノ粒子の水熱合成とその光触媒性能
- Zr基金属ガラスの超塑性変形と微構造
- 単層カーボンナノチューブ探針の作製と高配向焼結グラファイトの加工
- 406 Pt基金属ガラスの高速超塑性(材料力学-機能材料)
- 過冷却液体領域を持つZr基金属ガラスの変形組織
- 低温での黒鉛結晶生成に対する鉄およびニッケルの役割
- レールガン溶射における被膜形成機構
- Al/アモルファス半導体系二層膜の結晶化とパターン形成
- 非線形電子回路のカオス的ダブルスクロール・アトラクタのエルゴート性
- HI NICALONを強化材とした一方向繊維強化Si_3N_4複合材の機械的特性
- 準結晶を含むAl-V-Fe-M(M=Ti, Cr, Si)合金P/M材の組織と耐熱強度
- Al-Cr-R (R=Ce, Mm) 系合金P/M材の機械的性質
- Al/Ge二層膜におけるフラクタル状パターン形成の in-situ SEM 観察
- Al/アモルファスGe二層膜の結晶化に伴うフラクタル状パターン形成
- 低温水素イオン注入により導入されたシリコン結晶欠陥の特性分析
- プロトン剥離現象における不純物依存性
- プロトン注入シリコンの加熱その場観察(プロジェクト研究)
- 低温水素イオン注入シリコンの欠陥構造分析 (放射線とイオンビームによる物質構造の研究と改質・合成)
- Hイオン注入されたシリコンの欠陥分布観察(プロジェクト研究)
- 435 H^+注入されたSiの加熱剥離挙動(O.S.9. 機能薄膜創成と物性)
- 高ドーズ水素イオン注入シリコンの物性とそのSOI製作への応用
- 水素イオン注入により発生したシリコン結晶内プレートレットのTEM観察
- 水素イオン注入欠陥のその場加熱観察
- 水素イオン注入欠陥層のプレートレット分布評価
- Al-Ag/Ge系二層膜の組織変化とパターン形成
- Deformation Behavior of Pt-based Metallic Glass at Elevated Temperatures
- Crystallization of Zr_Al_Ni_5Cu_ Bulk Metallic Glass Composites Containing ZrC Particles
- Microstructure of Superplastic Zr_Al_Ni_Cu_ Metallic Glass
- Elevated-Temperature Al-Ti-Fe-Cr Alloys with High Ductility at High-Strain-Rates
- ESDパルスの周波数スペクトラム測定法
- 715 Y_2O_3 添加部分安定化 ZrO_2 における正方晶-単斜晶変態の本性(セラミックス, 萌芽・境界技術, 日本鉄鋼協会第 113 回(春季)講演大会)
- カーボンナノチューブ探針を用いた高アスペクト比ナノスケール穴加工法の開発
- ショットピーニングによって生成したナノ結晶相の疲労強度に及ぼす影響
- ショットピーニングによって発生する表面層の実体
- SiCウィスカ/Al複合材料の超塑性特性に及ぼすMgとCuの影響
- 溶湯攪拌法で作製したAlM/ZK51マグネシウム合金複合材料の高速超塑性
- AIN粒子強化マグネシウム合金複合材料の超塑性
- クローズドP/Mプロセスの開発と高比強度非平衡材料の創製
- アモルファス合金粉末の固化成形
- パルス大電流を利用する超高速プラズマ溶射の研究(4) -Ti-Al金属間化合物被膜の形成-
- ホットプレス法によるFe-Zr-B系非晶質粉末の固化成形
- カーボンナノチューブ探針を用いた高アスペクト比ナノスケール穴加工法の開発
- 引き上げ法によるカーボンナノチューブ探針の簡易作製
- Pt貴金属ガラスの変形挙動のその場観察
- SiC粒子分散Al-Ti-Fe-Cr急速凝固粉末冶金複合材
- 528 Pt 基金属ガラスの高速超塑性変形挙動
- ZrC粒子を含むZr55AlloNisCu30バルク金属ガラス複合材料のナノ結晶化挙動(プロジェクト研究)
- 415 Zr基金属ガラス及びその複合材料のトライボロジー特性(機能材料)
- 高強度を有する急速凝固P/Mアルミニウム合金の耐摩耗性
- 急速凝固P/M Al-Ti-Fe-TM合金の耐摩耗性と耐熱性
- 高強度P/Mアルミニウム合金の摩耗特性
- 準結晶を含むガス噴霧Al-7.8%V-4%Fe合金粉末の押出成形と耐熱強度
- 高清浄環境下における超急冷粉末冶金連続プロセスとそれを用いた新材料の開発
- メカニカルグラインデング処理したAl-7.9%V-4%Fe合金粉末の押出成形と耐熱強度
- 準結晶を含むガス噴霧Al-Cr系合金粉末の押出し成形と機械的性質
- 3p-N-8 バルクの非晶質合金の音速
- SPMによる引掻き試験でシリコン単結晶に生じた微構造変化のTEM観察
- シリコン単結晶のマイクロ磨耗
- シリコン単結晶のマイクロ摩耗特性と摩耗組織
- Effect of Heat Treatment on Impact Toughness of Aluminum Silicon Eutectic Alloy Processed by Rotary-Die Equal-Channel Angular Pressing
- Observation of High Dose H^+ Implanted Damaged Layer
- Fabrication of Josephson Junctions by Focused Electron Beam Irradiation
- Fabrication of DC Supereonducting Quantum Interference Devices with Hybrid Structure of Polycrystalline Y_1Ba_2Cu_3O_x Films and Epitaxial Y_1Ba_2Cu_3O_x Films
- 集束イオンビーム励起化学気相法によるマイクロ構造体の作製と機械的性質の評価
- プラスチック用導電性充填剤としての研磨粉に関する研究(1) : エポキシ樹脂への利用と磁場の効果
- 炭酸ガスアークプラズマ気流中のCFRP材の耐熱試験(電磁流体,一般講演)
- SPMを用いたSi単結晶のナノ加工と表面の構造変化
- SPMを用いたSi単結晶のナノ加工と表面の構造変化
- 2122 カーボンナノチューブ探針を用いた高アスペクト比ナノスケール加工法の開発(S29-1 マイクロ/ナノ加工の動向と可能性(1),S29 マイクロ/ナノ加工の動向と可能性)
- 原始的構造解析システムの現状と課題
- 極微小電流計測型ナノプローブその場観察システムの開発
- 743 金属微粒子の融点(急冷薄帯, 噴霧粉, 粉体製造, 粉末冶金, 萌芽・境界技術, 日本鉄鋼協会第 114 回(秋季)講演大会)
- FIB-CVDによるマイクロ構造体の作製と機械的性質の評価
- Destruction and Recovery of Superconductivity in Bi-Pb-Sr-Ca-Cu-O Synthesized under High Pressure
- Direct Observation of Crystallization Process from Amorphous Y-Ba-Cu-O Film by means of Optical Microscopy
- 透過型電子顕微鏡法によるα-Si_3N_4ウイスカーの微細構造の解析(セラミックスの微細構造)
- S1904-1-4 炭酸ガスアークプラズマフリージェット流中の炭化ケイ素材料の加熱実験(大気突入・減速技術(1),社会変革を技術で廻す機械工学)
- High Pressure Hot-Pressing of Y_1Ba_2Cu_3O_ Superconductor
- Preparation and Characterization of Grain Boundary Josephson Junction from Amorphous Thin Film
- Ternary Phase Diagram of the YO_-BaO-CuO System and the In Situ Observation of Crystal Growth
- Direct Observations of Melting and Solidification of Bi-Pb-Sr-Ca-Cu-O Compound
- Resputtering Effect on Y_1Ba_2Cu_3O_ Thin Films Prepared by RF-Magnetron Sputtering
- Preparation of Bulky Bi(Pb)-Sr-Ca-Cu-O Superconductor by Magnetized Twin-Roll
- High-Pressure Synthesis of a Bi-Pb-Sr-Ca-Cu-O Superconductor
- High Hydrostatic Pressure Consolidation of Amorphous Ti-37.5 at%Si Powder Prepared by Mechanical Alloying and Mechanical Properties of the Compact
- 非晶質相の結晶化を利用して作製した高強度P/Mアルミニウム合金
- 428 イオンビーム支援蒸着法を用いて形成したC-N系薄膜のトライボロジー特性 : Arイオンアシスト効果(O.S.9. 機能薄膜創成と物性)
- X線トポグラフィ-による金属の融解,凝固過程の動的観察
- MA-超高圧成形により作製したTi-37. 5at%Siバルク体の組織と機械的特性
- MNM-P1-2 スパッタリング法によるTi-Ni形状記憶合金ナノスケール薄膜の作製と評価(合同ポスターセッション P1 単結晶・多結晶シリコンの疲労寿命評価とメカニズムの解明)
- MNM-4A-6 CNT探針を用いたSTMによるカーボン材料の高アスペクト比ナノスケール加工(セッション 4A ナノ材料と熱工学)
- MNM-3A-7 電圧印加に伴うナノスケール加工現象のTEM内その場観察(セッション 3A 単結晶・多結晶シリコンの疲労寿命評価とメカニズムの解明)
- MNM-1B-6 TEMによる水酸アパタイトのマイクロ/ナノ摩耗プロセスの解明(セッション 1B 情報・精密機器におけるマイクロ・ナノテクノロジー1)
- ナノ及び原子的尺度における微構造の変化の電子顕微鏡による解析
- カーボンナノチューブを用いた高アスペクト比ナノ加工とTEM内その場観察による加工原理の解明
- 原子的構造解析システムの現状と課題(2)
- その場電顕観察法