Photo-catalytic Decomposition of Tetrachloroethylene (C_2Cl_4) by Plasma Sprayed TiO_2 Coatings(Materials, Metallurgy & Weldability)
スポンサーリンク
概要
- 論文の詳細を見る
TiO_2 coatings were prepared on a stainless mesh net by plasma spraying using agglomerated TiO_2 powder. Since TiO_2 powders are well known as photo-catalytic materials, the photo-catalytic TiO_2 coatings on mesh net are used for purification of water containing tetrachloroethylene (C_2Cl_4). It was found that TiO_2 agglomerated powders could be deposited on mesh net and approximately 35% anatase ratio could be obtained by 400A plasma spraying. It was possible to obtain approximately 100μm thicknesses on the stainless mesh net substrate when plasma spraying was carried out at 800A, while the coating thickness drastically decreased at 400A. In terms of photo-catalytic properties, retaining the anatase phase ratio in the TiO_2 coatings is essential to achieve photo-catalytic decomposition of 10ppm C_2Cl_4 solution. It was found that the anatase ratio decreased gradually with increasing arc current and pass count, while the coating thickness increased with increasing arc current. This means that 0.2μm agglomerated powders showed a lower susceptibility to heat effects and provided higher photo-catalytic activity. It was cleared that the anatase ratio had large influence on the photo-catalytic activity. These coatings showed photo-catalytic degradation of C_2Cl_4 solution. As a result of photo-catalytic experiments, it was shown that tested C_2Cl_4 solution is decomposed in moderately shorter times, to the extent that 10ppm C_2Cl_4 was decomposed to less than 1ppm after 7.2ks of 400A plasma sprayed coating. Thermal spraying on stainless mesh net could imply both new applications and possibilities for photo-catalytic degradation of C_2Cl_4 solution.
- 大阪大学の論文
著者
-
OHMORI Akira
Osaka University
-
Ohmori A
Osaka Univ. Osaka Jpn
-
NAKADE Katsuyuki
Osaka University
-
Ohmori A
National Institute For Materials Science
-
Nakade K
Osaka University
-
Mizutani Satoshi
Osaka University
-
YASUOKA Junichi
Osaka University
関連論文
- Studies on Corrosion Behavior of Ceramic Sprayed Stainless Steels (Report II) : Utilization of Anodic Polarization Curves to Evaluate Corrosion Tendency(Materials, Metallurgy & Weldability)
- Studies on Corrosion Behavior of Ceramic Sprayed Stainless Steels (Report I) : Electrochemical Approach on Ceramic Sprayed Coatings(Materials, Metallurgy & Weldability)
- Spreading of BAg-5 on Pre-Flux Coated Stainless Steel Plate : Function of Fluxes Mixed with NiCl_2 or FeCl_3
- Effect of Annealing on Tensile Properties of Ultrafine-Grained Steels Fabricated by Grooved Warm Rolling
- Serration of Grain Boundary in Ni-30Fe Alloy through High Temperature Deformation
- Dynamic Restoration Process of Ni-30Fe alloy during Hot Deformation
- Effect of Deformation Temperature and Strain Rate on Evolution of Ultrafine Grained Structure through Single-Pass Large-Strain Warm Deformation in a Low Carbon Steel
- Strain-hardening due to Dispersed Cementite for Low Carbon Ultrafine-grained Steels
- 低炭素鋼の高Z大歪加工における超微細粒組織の形成
- Dynamic Restoration Process of Ni-30Fe Alloy during Hot Deformation
- 温間圧延によって製造した超微細フェライト+セメンタイト組織鋼板の特性
- セメンタイト粒子分散による低炭素超微細粒鋼のひずみ硬化設計
- Strength - Ductility Balance of the Ultrafine - grained Ferrite and Cementite Structure
- Effect of Warm Deformation Temperature on Formation of Ultrafine - grained Ferrite Structure for a Low Carbon Si - Mn Steel
- Electric Field Assisted Treatment of Various Plasma Sprayed ZrO_2 Coatings(Physics, Process, Instruments & Measurements)
- Influence of Plasma Spray Conditions on the Structure of Al_2O_3 Coatings(Surface Processing)
- Fracture Behavior of Plasma Sprayed Ceramic Coatings in Scratch Test(Physics, Process, Instrument & Measurement)
- Research on Characteristics of Filler Metal and Flux Influencing on the Toughness of a Carbon Steel Weld : Minor Elements and Alloying Elements Influencing on the Toughness of Weld(Materials, Metallurgy & Weldability)
- Characteristics of Metal Electroplating to Plasma Sprayed Ceramic Coatings(Physics, Process, Instrument & Measurement)
- Untersuchungen der SchweiBguteigenschaften in Abhangigkeiten vom Basizitatsgrad der 50kg/mm^2 Grad agglomerierten UP-SchweiBpulver(Materials, Metallurgy & Weldability)
- Basic Studies on Plasma Sprayed Ceramics Coatings (Report 1) : Erosion Mechanism at ACT-JP Process(Materials, Metallurgy & Weldability)
- Laser Surface Alloying of Plasma Sprayed Coatings with Steel Substrate
- Liquid Mn Sintering of Plasma-Sprayed Ceramic Coating(Physics, Process, Instrument & Measurements)
- Bonding of Si_3N_4 to SS400 Steel with Activated Coating Layers Made by Low-Pressure Plasma Spraying(Physics, Process, Instruments & Measurements)
- Penetration Behavior into Connected Porosities of Plasma Sprayed Al_2O_3 Coatings with Liquid Mn
- Bonding of Al_2O_3 to SS41 Steel with LPC Plasma Sprayed Cu-Ti Two-layer Coatings(Surface Processing)
- Photoresponse of Plasma Sprayed TiO_2-Rutile Semiconductor(Physics, Process, Instruments & Measurements)
- Formation of YBaCu-O System Superconductor by Thermal Spraying(Materials, Metallugy & Weldability)
- Photoanodic Properties of Plasma Sprayed TiO_2 Coatings(Surface Processing)
- Electrical Conductivity of Titanium Oxide (Rutile) Plasma Sprayed Coatings(Physics, Process, Instrument & Measurement)
- Plasma Sprayed Y-Ba-Cu-O System Superconductor
- Solid-State Reaction Bonding of Alumina to Cu-4Ti Alloy(Materials, Metallurgy & Weldability)
- Thermal Shock Resistance of ZrO_2-8wt.%Y_2O_3 Coatings Prepared by Plasma Laser Hybrid Spraying Technique(Materials, Metallurgy & Weldability)
- Charakteristiken der Kavitationserosion von Sialon(Materials, Metallurgy & Weldability)
- Spreading of BAg-5 on Pre-Flux Coated Stainless Steel Plate (Report II) : Function of Fluxes Mixed with CuCl or CoCl_2(Welding Physics, Processes & Instruments)
- Influence of Sigma Phase on Hydrogen Induced Cracking of Duplex Stainless Steel(Materials, Metallurgy & Weldability)
- Effect of Strain on Ultrafine Ferrite Grains formed by Single-Pass Large Strain-High Z Deformation
- A trical to fabricate a 25mm - thick plate with ultrafine - grained ferrite structure
- Structual Studies of Poly(Fluoroalkyl Methacrylate)s and Poly(Fluoroalkyl α-Fluoroacrylate)s
- Three-Dimensional Reconstruction of Fracture Surface Using Area Matching Algorithm(Physics, Processes, Instruments & Measurements)
- Interfacial Phenomena During Field Assisted Bonding of Zirconia to Metals
- Solid State Reaction Bonding of Non-Oxide Ceamics to Metals (Report I) : Bonding of Si_3N_4 to Al Alloys(Materials, Metallurgy & Weldability)
- Pressure and Field-Assisted Bonding of Glass to Aluminum(Materials, Metallurgy & Weldability)
- Characterization of the Structure of Plasma-Sprayed Metallic Silicide Coatings(Materials, Metallurgy & Weldability)
- Studies on Vacuum Brazing (Report II) : Removal of oxide film from stainless steel surface and brazing alloy spreading mechanism(Welding Physics, Process & Instrument)
- Studies on Vacuum Brazing (Report I) : Removing of oxide film from carbon steel surface and brazing alloy spreading mechanism(Welding Physics, Processes & Instruments)
- A Study of the Photo-Catalytic Character of Plasma Sprayed TiO_2 Coatings(Physics, Processes, Instruments & Measurements)
- Control of Oxygen Concentration in Plasma Sprayed TiO_2 Coating by CO_2 Laser Irradiation(Materials, Metallurgy & Weldability)
- Eigenschaften von Flammenjetgespritzten Schichten(Physics, Process & Instrument)
- Influence of Processing Conditions on the Thermal Spraying Coating(Materials, Metallurgy & Weldability)
- Photo-catalytic Decomposition of Tetrachloroethylene (C_2Cl_4) by Plasma Sprayed TiO_2 Coatings(Materials, Metallurgy & Weldability)
- New Approach for Advanced Zirconia Thermal Barrier Coatings by Plasma-Laser Hybrid Spraying Technique(Materials, Metallurgy & Weldability)
- Synthesis of Al_2O_3-AlN Coatings by Low Pressure Plasma Spraying and Nitriding(Physics, Process, Instrument & Measurements)
- Spraying of TiN by a Combined Laser and Low Pressure Plasma Spray System(Physics, Process, Instruments & Measurements)
- Laser Processing of Plasma Sprayed Coatings
- Forschung in Bezug auf die Lotbruchigkeit von Kohlenstoffstahl (Bericht 3) : EinfluB der Zuggeschwindigkeit auf die Lotbrilchigkeit(Materials, Metallurgy & Weldability)
- Study on Liquid Metal Embrittlement of Carbon Steels (Report 2) : Effect of Erosion of Carbon Steel in Liquid Metals on LME(Materials, Metallurgy & Weldability)
- Study on Liquid Metal Embrittlement of Steels (Report 1) : Penetration Behavior of Liquid Metals
- Study on Liquid Metal Embrittlement of Carbon Steels (Report 1) : Penetration Behavior of Liquid Metal(Welding Physics, Processes & Instruments)
- Some Fundamental Research of New Type Powder Oxygen Cutting Method for Stainless Steel(WELDING PHYSICS, PROCESSES AND INSTRUMENTS)
- A Study on Tunneling Flow of Filler Metal in Aluminum Brazing(Welding Physics, Processes & Instruments)
- Examination of Plasma Spray Parameters for YBa_2Cu_3O_ Coatings(Surface Processing)
- WC-Co High Energy Thermal Sprayed Coatings : Structures and Mechanical Properties(Materials, Metallurgy & Weldability)
- Occurrence of Non-Wetted Parts in Dip Soldering (Report-1)(Welding Physics, Processes & Instruments)
- Studies on Brazability of Electric Contact Chip Materials (Report I) : Effect of Surface Preparation of Sintered Tungsten Alloys on Wetting of BAg Filler Metals
- Bonding of Alumina using Cupreous Oxide as Insert Material
- Production Method of High Purity Copper for Semiconductor Use and Evaluation of the Quality (Report I)(Materials, Metallurgy & Weldability)
- Cr_3C_2-Ni-Cr coating properties of HVOF-YAG hybrid spraying and its strengthening mechanism(Physics, Processes, Instruments & Measurements)
- Improvement of Plasma-Sprayed ZrO_2 Coatings by Cr_2O_3 Penetration and Evaluation of Cavitation Erosion(Physics, Processes, Instruments & Measurements)
- Surface Modification of Recycled PET Plate by Particle Implantation and Deposition with Plasma Spraying(Materials, Metallurgy & Weldability)
- Fabrication and Properties of TiO_2 Photo-Catalytic Coatings by Thermal Spraying with TiO_2-Al Agglomerated Powder(Materials, Metallurgy & Weldability)
- The Formation Behavior of TiO_2 Thermal Sprayed Coatings Using Nano-Powders and Their Photo-Catalytic Properties(Materials, Metallurgy & Weldability, INTERNATIONAL SYMPOSIUM OF JWRI 30TH ANNIVERSARY)
- Effect of Agglomerated TiO_2 Powders with Nanostructure on Microstructure of Thermal Sprayed TiO_2 coatings(Materials, Metallurgy & Weldability)
- Characterization of Graded Ti Silicide Coating Formed by Thermal Diffusion Treatment of Low Pressure Plasma Sprayed Silicon Coating on Titanium Substrate(Materials, Metallurgy & Weldability)
- Studies on Vacuum Brazing (Report III) : Effect of manganese added in sliver-copper brazing alloy on brazability(Welding Physics, Process & Instrument)
- Al_2O_3 Diffusion Bonding Using TiH_2 Powder Interlayer(Materials, Metallurgy & Weldability)
- Reaction Spray by Laser-Plasma Jet : Synthesis of TiN Coatings(Physics, Process, Instruments & Measurements)
- Photocatalytic Activity and Photo-absorption of Plasma Sprayed TiO_2-10%Fe_3O_4 Coatings(Materials, Metallurgy & Weldability)
- Fabrication of TiO_2 Photocatalytic Coatings on PET by Plasma Spraying(Materials, Metallurgy & Weldability, INTERNATIONAL SYMPOSIUM OF JWRI 30TH ANNIVERSARY)
- Zu den Faktoren Welche die Adhasion Lichtbogengespritzter Schichten Beeinflussen(Welding Physics, Process & Instrument)
- Fusing of Sprayed Ni-base Coatings by Induction Heating(Physics, Process, Instruments & Measurements)
- Phase Composition and Photocatalytic Activity of TiO_2-Fe_3O_4 Coatings Prepared by Plasma Spraying Technique(Materials, Metallurgy & Weldability, INTERNATIONAL SYMPOSIUM OF JWRI 30TH ANNIVERSARY)
- Evaluation of Composite TiO_2-FeTiO_3 Coatings Prepared by Plasma Spraying Technique(Materials, Metallurgy & Weldability)