Reaction Spray by Laser-Plasma Jet : Synthesis of TiN Coatings(Physics, Process, Instruments & Measurements)
スポンサーリンク
概要
- 論文の詳細を見る
The synthesis of TiN coating has been investigated with using the laser-plasma spraying, Ti sprayed coating was formed by N_2 plasma jet, and it was irradiated with CO_2 laser beam in a low pressure nitrogen atmosphere. Main results obtained was summarized as follows: Ti sprayed coating can be more nitrized with irradiation of CO_2 laser in N_2 atmosphere, and the nitridation degree of the Ti sprayed coating was increased with the increasing of the laser output and number of the laser irradiation times. The hardness of the TiN coating obtaied was about 1300HV.
- 大阪大学の論文
著者
-
ARATA Yoshiaki
Osaka University
-
Hirano Satoru
Osaka University
-
OHMORI Akira
Osaka University
-
Hirano S
Osaka Univ. Osaka Jpn
-
Zhang Yue-chang
Osaka University
関連論文
- Plasma Arc Welding of Centrifugal Cast Steel Pipe (HK-40) (Report III)
- High Rate Sputtering of Corrosion-Resistant Alloys(Welding Physics, Processes & Instruments)
- Mechanical Properties on Electron Beam Welds of Constructional High Tension Steels (Report V)
- Studies on Corrosion Behavior of Ceramic Sprayed Stainless Steels (Report II) : Utilization of Anodic Polarization Curves to Evaluate Corrosion Tendency(Materials, Metallurgy & Weldability)
- Studies on Corrosion Behavior of Ceramic Sprayed Stainless Steels (Report I) : Electrochemical Approach on Ceramic Sprayed Coatings(Materials, Metallurgy & Weldability)
- Transient Arc Diagnosis with OMA(Welding Physics, Processes & Instruments)
- High Power Microwave Plasma Beam as a Heat Source (Report IV) : Application to Cutting
- Solidification Crack Susceptibility of Aluminum Alloy Weld Metals (Report III) : Effect of Straining Rate on Crack Length in Weld Metal
- Solidification Crack Susceptibility of Aluminum Alloy Weld Metals (Report II) : Effect of Straining Rate on Cracking Threshold in Weld Metal during Solidification
- Solidification Crack Susceptibility of Aluminum Alloy Weld Metals (Report I) : Characteristics of Ductility Curves during Solidification by Means of the Trans-Varestraint Test