Direct Measurements of Densities of Nickel-rich Nickel-Manganese Alloys
スポンサーリンク
概要
- 論文の詳細を見る
The present short note reports the density data measured at room temperature on face-centered cubic nickel-rich Ni-Mn alloys. The specimens were cylindrical rods, about 2mm in diameter and about 140mm long, prepared from electrolytic nickel and electrolytic manganese. The nominal manganese compositions were 6.0, 11.0, 17.0, 22.0 and 27.0 weight percent. The density measurements were made, by using the weighing-in water method, at room temperature (13~14℃) after quenching from 600℃. The results of the measurements show that the density of nickel decreases linearly and rapidly with increasing addition of manganese. The density values calculated from the data of lattice constants of Ni-Mn specimens quenched from 1000℃, as measured by Koster and Rauscher, are in good agreement with the measured data within the limits of experimental error.
- 東北大学の論文
著者
-
Taniguchi Satoshi
(now)the Hitachi Central Research Laboratories
-
Yamamoto Mikio
The Research Institute For Iron Steel And Other Metals
関連論文
- Origin of Superparamagnetism in the CsCl-Type Compounds, Fe_Ti_, near the Stoichiometric Composition
- Ferromagnetism in Fe_2Sc with the Hexagonal MgZn_2-Type Structure
- Resistance Minimum in Iron-Titanium Compounds, Fe_Ti_, with the CsCl-Type Structure
- Thermohysteresis Phenomena of the Electrical Resistivity in the Laves Phase Compounds in Fe-Ti System
- Curious Behavior of the Electrical Resistivity of the Laves Phase Compound Fe_2Ti
- Thickness and Orientation Dependence of Plastic Behaviors of Iron Whiskers
- Thickness and Orientation Dependence of Plastic Behaviors of Iron Whiskers
- Plastic Deformation of Copper and Iron Whiskers
- The Thickness Dependence of Plastic Behaviors of Copper Whiskers
- The Thickness Dependence of Plastic Behaviors of Copper Whiskers
- Plastic Deformation of Iron Whiskers
- Ferromagnetism in the Laves Phase Compound Fe_Hf_ Annealed at 1000℃
- Ferromagnetic Properties of the Intermetallic Compound with the Hexagonal Leves-Phase Structure in Cobalt-Titanium System
- Ferromagnetic Properties of the Intermetallic Compound with the Hexagonal Laves-Phase Structure in Cobalt-Titanium System
- Magnetic Properties of Cobalt-Titanium Alloys with the CsCl-Type Structure
- Magnetic Properties of Cobalt-Titanium Alloys with the CsCl-Type Structure
- Magnetic Properties of the Stoichiometric Laves Phase Compound in Cobalt-Titanium System
- Magnetic Behavior of the Laves Phase Compound in Fe-Ta Binary System
- Exchange Anisotropy in Single Crystals of Cu-Mn Alloys
- Exchange Anisotropy in Single Crystals of Cu-Mn Alloys
- Influence d'Oxygen sur les Proprietes Magnetiques du Compose da la Phase Laves de Fer et Titane
- Crystal Structures and Magnetic Properties of the Intermetallic Compound Fe_2 Zr
- On the Formation of Striation-Type Substructure in Copper Crystals
- Residual Resistance Ratio of Zone-refined Copper after Oxidation
- Plastic Deformation of Foil Copper Crystals. II : Electron Microscopical Study
- Plastic Deformation of Foil Copper Crystals. I : Study of Work-Hardening Behavior
- Work-hardening of Foil Crystals of Copper
- Several Experiments on the Memory Effect in αFe_2O_3
- Magnetic Annealing Effect in α Fe_2O_3
- Domain Patterns on Ferromagnetic Pyrrhotite Crystal
- The Additional Magnetic Anisotropy Induced by Magnetic Anneal in Ferromagnetic Face-Centered Cubic Solid Solutions : Part I. Dependence of the Induced Magnetic Anisotropy on the Temperature and Duration of Magnetic Anneal, on the Measuring Temperature, an
- Orientation Dependence of the Uniaxial Ferromagnetic Anisotropy Induced by Magnetic Annealing in 20% Co-Ni Single Crystals
- Ferromagnetic Domain Structure as Affected by the Uniaxial Anisotropy Induced in a 40 Percent Co-Ni Single Crystal
- Dislocation Etch Pits on Nickel Single Crystals
- Surface Structures and Corresponding Light Figures Revealed by Water-etched Rochelle Salt Crystals
- Magnetic Properties of the Stoichiometric Laves Phase Compound in Cobalt-Titanium System
- Annealing Effects of the Compression Induced Magnetic Anisotropy in Fe_3Al Alloys
- Magneto-Plastic Effect in Nickel Single Crystals
- Magneto-Plastic Effect in Nickel Single Crystals
- Plastic Deformation of Nickel Single Crystals in an Alternating Magnetic Field
- Magnetostriction Constants of Face-Centered Cubic Nickel-Copper and Nickel-Cobalt Alloys
- Anelasticity of Ferromagnetics : Magneto-Elastic Relaxation in Nickel
- Growing Sapphire Single Crystals by the Vernouil Method Using Town Gas and Their Some Crystallographic Features
- Some Observations on Etch Pits and Light Figures Revealed by Chemically Etched Lithium Fluoride Crystal
- Ferromagnetic Domain Patterns on Nickel Crystals. II : Domain Patterns on General Surfaces of Unmagnetized Crystals
- Ferromagnetic Domain Patterns on Nickel Crystals. I : Domain Patterns on the Magnetically Important Surfaces of Unmagnetized Nickel Crystals
- Light Figure Phenomena Revealed and Crystal Faces Developed by Chemical Etching in Silicon Crystal
- The Relationship between the Growth Shape and Growth Anisotropy in Cubic Crystals
- On the Growth and Dissolution Shapes of Spherical Shell Crystals and the Shapes of Etch Pits on Crystals
- Weak Field Behaviour of the 〓E Effect in Ferromagnetic Cubic Solid Solution Alloys
- Direct Measurements of Densities of Nickel-rich Nickel-Manganese Alloys
- Composition, Temperature, and Ordering Dependence of Magnetostriction Constants in Nickel-Manganese Alloys
- Temperature Distribution around the Resting or Moving Solid-Liquid Interface in a Rod
- Growing of Single Crystals of Zinc, Bismuth and White Tin by the Bridgman Method
- The Influence of Heat-Treatment on the Magnetic Properties of Face-Centered Cubic Nickel-Cobalt Alloys
- Magnetic Hysteresis in Annealed Nickel-Cobalt Alloys
- The 〓E-Effect and Young's Modulus in Nickel-Cobalt Alloys
- Dependence on the Growing Conditions of the Degree of Successful Growth and Orientation in Single Crystals Grown from the Melt
- Direct Measurements of Density of Nickel-rich Nickel-Manganese Alloys
- A Note on a Theory of the Uniaxial Ferromagnetic Anisotropy Induced by Cold Work or by Magnetic Annealing in Cubic Solid Solutions
- The Density, Magnetic Properties, Young's Modulus, and 〓E-Effect, and Their Changes Due to Quenching in Ferromagnetic Iron-Aluminium Alloys. I : The Density and Magnetic Properties
- The Density, Magnetic Properties, Young's Modulus, and 〓E-Effect, and Their Change Due to Quenching in Ferromagnetic Iron-Aluminium Alloys. II : Young's Modulus and the 〓E-Effect
- Magnetostriction Constants of Nickel-Copper and Nickel-Cobalt Alloys
- On the Magnetostrictive Constants of Face-Centered Cubic Nickel-Cobalt Alloys
- The Light-Figure Phenomenon Revealed and Crystal Planes Developed by Etching in Tetragonal Tin Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. II : Orientation Determination by Light Figures
- The Light-Figure Method as Compared with the Back-Reflection Laue Method for Determining Orientations of Metal Single Crystals
- Electron Microscope Observations of Slip Bands of KCI Whiskers
- Production of Single Crystals of Iron-Aluminium Alloys by the Strain-Anneal Method
- Light Figures of Zinc Crystals
- Composition, Temperature and Ordering Dependence of Magnetostriction Constants in Nickel-Manganese Alloys
- Longitudinal Magnetostriction in Nickel-Cobalt Alloys
- Several Experiments concerning the Production of Iron Single Crystals by the Recrystallization Method
- Light Figures of Bismuth Single Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. III : Orientation Determination by Light Figures
- Orientation Determination of Zinc Crystals by the Light-Figure Method
- A Note on the Formation of Etch Pits on Crystals
- Light Figures of Bismuth Single Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. I : Preliminary Investigations
- Light-Figure Phenomena Revealed and Crystal Faces Developed by Chemically Etched Nickel-Copper Alloy Crystals
- Orientation Determination of Crystal Grains by Light Figures
- Composition, Temperature and Ordering Dependence of the Magnetostriction Constants in Nickel-rich Nickel-Manganese Alloys
- Influence of Order-Disorder on Creep of a Superlattice Alloy
- On the Solution-Body Phenomenon and Anisotropy of Solution Rate in Tetragonal Tin Crystal
- On the Solution-Body Phenomenon and Anisotropy of Solution Rate in Zinc Crystal
- Further Studies on the Orientation Determination of Cubic Metal Crystal Rods by the Light-Figure Method
- Orientation Determination of Cubic Crystal Plates by the Light-Figure Method
- Light-Figure Phenomenon Revealed and Crystal Planes Developed by Chemical Etching in Zinc Single Crystals
- The Light-Figure Phenomenon Revealed and Crystal Planes Developed by Etching in Tetragonal Tin Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. I : The Light-Figure Phenomenon Revealed and Crystal Planes Developed b
- A Study on the Strain-Free Cutting of Metal Single Crystals
- The 〓E-Effect, Young's Modulus, and Magnetic Properties in Ferromagnetic Nickel-Copper Alloys
- On the Production of Single Crystals of Zinc, Bismuth and Tin by Sucking Up from Their Melts
- Ferromagnetic Behavior of Nickel-Cobalt Alloys
- On the Solution-Body Phenomenon and Anisotropy of Solution Rate in Bismuth Crystals
- Light Figures of Bismuth Single Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. II : Light Figures
- Light-Figure Phenomena Revealed and Crystal Faces Developed by Chemical Etching in Copper and α-Brass Crystals
- Theory of the Wiedemann Effect
- The Solution Anisotropy and Shape of Solution Body in Crystals
- Temperature Distribution around the Rest or Moving Solid-Liquid Interface in a Rod
- Weak Field Behaviour or the ΔE Effect in Ferromagnetic Cubic Solid Solution Alloys
- Theory of the Wiedemann Effect
- Fatigue Properties of Zinc Single Crystals and Polycrystals