Second Harmonic Generation of Thermally Poled ZnCl_2-B_2O_3-TeO_2 Glasses and Its Mechanism
スポンサーリンク
概要
- 論文の詳細を見る
- 2005-08-10
著者
-
Kashima K
Division Of Material Chemistry Faculty Of Engineering Kyoto University
-
Kimiya K
Mie Univ. Jpn
-
Kamiya Kanichi
Department Of Chemistry For Materials. Faculty Of Engineering. Mie University
-
那須 弘行
三重大学大学院
-
那須 弘行
Faculty Of Engineering Mie University
-
NASU Hiroyuki
Department of Chemistry for Materials, Faculty of Engineering, Mie University
-
HASHIMOTO Tadanori
Department of Chemistry for Materials. Faculty of Engineering. Mie University
-
HASHIMOTO Tatsunori
Department of Electronics, Kyushu University
-
Kamiya Kanichi
Department Of Chemistry For Materials Faculty Of Engineering Mie University
-
Hashimoto T
Department Of Chemistry For Materials Faculty Of Engineering Mie University
-
Nasu Hiroyuki
Department Of Industrial Chemistry Faculty Of Engineering Mie University
-
Nasu Hiroyuki
Department Of Chemistry For Materials Faculty Of Engineering Mie University
-
Takeda Hirofumi
Department Of Chemistry For Materials Faculty Of Engineering Mie University
-
NAGAIKE Yuki
Department of Chemistry for Materials, Faculty of Engineering, Mie University
-
Nagaike Yuki
Department Of Chemistry For Materials Faculty Of Engineering Mie University
-
Hashimoto Tadanori
Department Of Chemistry For Materials Faculty Of Engineering Mie University
-
Nasu Hiroyuki
Division Of Chemistry For Materials Graduate School Of Engineering Mie University
関連論文
- 非線形光学ガラス(光計測,光ファイバセンシング及び一般)
- ゾル-ゲル法と溶融法で作製した二成分系チタンノリン酸塩ガラスの構造研究
- ゾル-ゲル法で造られるシリカガラス繊維の引っ張り強度に及ぼす予備熱処理の影響 : ゲル-ガラス変換過程における構造変化との関連
- 電気的にポーリングしたGe-Sガラス系からの第二高調波発生
- 熱ポーリングしたPbO-Bi_2O_3-Ga_2O_3ガラスからの第二高調波発生
- 蒸発凝縮法によるナノサイズ粒子からなる銀薄膜の作製とその線形及び非線形光学特性
- 硝酸を触媒としたゾルーゲル法で調製したアルミナゲルの結晶化挙動 : 800℃での完全なα化
- 熱ポーリング処理したPbO-GeO_2ガラスからの第二高調波発生
- ゾル-ゲル法によるFe-ZrSiO_4顔料の合成
- CuClをドープしたSiO_2ガラス薄膜の量子サイズ効果