Novel Method for Generating Large Mesopores in an Amorphous Silica-Alumina by Controlling the Pore Size with the Gel Skeletal Reinforcement and Its Catalytic Cracking Properties as a Catalyst Matrix

スポンサーリンク

概要

• 論文の詳細を見る
• 2011-06-05

著者

• 那須 弘行

  三重大学大学院

• 那須 弘行

  Faculty Of Engineering Mie University

• Ishihara Atsushi

  Department Of Chemistry For Materials Faculty Of Engineering Mie University

• HASHIMOTO Tatsunori

  Department of Electronics, Kyushu University

• Ishihara Atsushi

  Division Of Applied Life Sciences Graduate School Of Agriculture Kyoto University

• Hashimoto T

  Department Of Chemistry For Materials Faculty Of Engineering Mie University

• Nasu Hiroyuki

  Department Of Industrial Chemistry Faculty Of Engineering Mie University

• Hashimoto T

  Niigata Univ. Niigata Jpn

• Hashimoto Tadanori

  Department Of Chemistry For Materials Faculty Of Engineering Mie University

• NAKAJIMA Kohei

  Division of Chemistry for Materials, Graduate School of Engineering, Mie University

• HIRADO Motoki

  Division of Chemistry for Materials, Graduate School of Engineering, Mie University

• HASHIMOTO Tadanori

  Division of Chemistry for Materials, Graduate School of Engineering, Mie University

• NASU Hiroyuki

  Division of Chemistry for Materials, Graduate School of Engineering, Mie University

• Hirado Motoki

  Division Of Chemistry For Materials Graduate School Of Engineering Mie University

• Nakajima Kohei

  Division Of Chemistry For Materials Graduate School Of Engineering Mie University

• Hashimoto Tadanori

  Division Of Chemistry For Materials Graduate School Of Engineering Mie University

• Nasu Hiroyuki

  Division Of Chemistry For Materials Graduate School Of Engineering Mie University

関連論文

• RF-スパッタリング法により作製したCdSe微粒子ドープガラス薄膜の微細構造と光学的特性
• 非線形光学ガラス(光計測,光ファイバセンシング及び一般)
• ゾル-ゲル法と溶融法で作製した二成分系チタンノリン酸塩ガラスの構造研究
• ゾル-ゲル法で造られるシリカガラス繊維の引っ張り強度に及ぼす予備熱処理の影響 : ゲル-ガラス変換過程における構造変化との関連
• ゾル-ゲル法で作製されたナトリウムゲルマン酸塩ガラスの構造 : 溶融法で作製されたガラスとの比較
• PbO-GeO_2ガラス中のGeの配位状態のEXAFS研究 : 構造と光学非線形性の関係
• 電気的にポーリングしたGe-Sガラス系からの第二高調波発生
• 熱ポーリングしたPbO-Bi_2O_3-Ga_2O_3ガラスからの第二高調波発生
• 蒸発凝縮法によるナノサイズ粒子からなる銀薄膜の作製とその線形及び非線形光学特性
• 硝酸を触媒としたゾルーゲル法で調製したアルミナゲルの結晶化挙動 : 800℃での完全なα化
• 熱ポーリング処理したPbO-GeO_2ガラスからの第二高調波発生
• ゾル-ゲル法によるFe-ZrSiO_4顔料の合成
• CuClをドープしたSiO_2ガラス薄膜の量子サイズ効果
• コンクリート廃材の炭酸化反応によるカルシウム源のリサイクルと二酸化炭素の固定
• ゾルーゲル法による希土類含有ジルコン顔料の調製
• 電気的にポーリングしたPbO-SiO_2ガラスからの第2高調波発生
• 硫化物ガラスの三次非線形光学特性 : La_2S_3-Ga_2S_3及びMS-La_2S_3-Ga_2S_3(MS=PbS, Ag_2S及びNa_2S)系ガラス
• ガラス材料の三次の非線形光学効果
• ゾル-ゲル法で得られたBi_2O_3-TiO_2-Nb_2O_5-TiO_2非晶質膜の三次の非線形光学効果
• 500℃付近でα-Al_2O_3へ変化するアルミナゲルのゾル-ゲル法による調製
• LiX-Li_2O-TeO_2及びAgX-Ag_2O-TeO_2(X=Cl, Br, I)ガラスの三次の光学非線形性
• rf-スパッタリング法による半導体微粒子ドープガラス薄膜の作製とその光学的性質
• No.8 ゾル-ゲル法を用いて調製したゼオライト含有シリカ-アルミナの接触分解特性(重質油,改質,触媒)
• No.6 キュリーポイントパイロライザーを用いたVGOの接触分解反応の解析(重質油,改質,触媒)
• Compact Electron Cyclotron Resonance Plasma-Etching Reactor Employing Permanent Magnet : Etching
• Compact Electron Cyclotron Resonance Plasma-Etching Reactor Employing Permanent Magnet
• Si Etching with Low Ion Energy in Low-Pressure Electron Cyclotron Resonance Plasma Generated by Longitudinal and Multipole Magnetic Fields
• High Etch Rate Modes in Microwave Plasma Etching of Silicon in High Magnetic Fields : Etching and Deposition Technology
• High Etch Rate Modes in Microwave Plasma Etching of Silicon in High Magnetic Fields
• Influence of Halogen plasma Atmosphere on SiO_2 Etching Characteristics : Etching
• Influence of Halogen Plasma Atmosphere on SiO_2 Etching Characteristics
• No.61 2価カルボン酸を用いて調製した非晶質シリカ-アルミナによる炭化水素の接触分解反応(重質油・バイオマス・コプロセッシング(3))
• No.5 PEGを用いて調製した新規炭素担持ニッケル触媒による水熱ガス化反応(改質・処理・クリーン化(2))
• 気相法を用いた銀微粒子とチタニア微粒子からなる薄膜の作製とその光学特性
• シリカ基板上に沈着させた銀微粒子の光学特性に及ぼすチタニア微粒子の影響
• 局所場表面プラズモン共鳴を利用した光学センサのシリカコーティングによるサイクル特性の向上
• ナノサイズ銀微粒子を用いたSPRセンサの開発
• 高周波スパッタリング法により作製したCdSe含有SiO_2ガラス薄膜の三次の非線形光学効果における微粒子粒径の影響
• Highly Efficient Optical Second Harmonic Generation in Poled Ti-Doped Silica Glasses
• Effect of γ-Irradiation on Optical Second Harmonic Intensity of Electrically Poled Silica Glass
• Preparation and Magnetooptical Properties of Cd_Mn_xTe Microcrystal-Doped SiO_2 Glass Thin Films
• Thermodynamic Estimation of Oxidation Ability of Various Gases Used for the Preparation of Superconducting Films at High Vacuum
• Superconductivity in a New Oxide System of Eu-La-Ce-Cu-O
• Preparation of a Bi-Sr-Ca-Cu-O High-T_c Superconductor by the Reaction of a Cu-Free Precursor with Cu Plate
• Red-to-Yellow Electroluminescence from CdSe Microcrystal-Doped Indium Tin Oxide Thin Films
• Second-Harmonic Generation from Thermally Poled Mixed Alkali Silicate Glasses Containing Various Alkaline-Earth Oxides
• Second-Order Optical Nonlinearity in Electrically Poled Silicate Glass Containing Ga_2O_3
• Second Harmonic Generation from Surface Crystallized Li_2O-Ta_2O_5-SiO_2 Glass
• Observation of Electroluminescence from CdSe-Microcrystal-Embedded Indium Tin Oxide Film
• Second-Harmonic Generation from Electrically Poled Niobium Alkali Silicate Glasses
• Second Harmonic Generation in Poled Tellurite Glasses
• Influence of the OH Content on Second Harmonic Generation from Electrically Polarized SiO_2 Glasses
• Effects of Kinetic Inductance on the Performance of a Flux-Flow-Type Josephson Amplifier
• Reticle Critical Dimension Latitude for Fabrication of 0.18 μm Line Patterns
• Standing Wave Effect of Various Illumination Methods in 0.25 μm KrF Excimer Laser Lithography
• Study of Submicron SrTiO_3 Patterning
• Low-Temperature Etching of 0.2 μm Al Patterns Using a Sio_2 Mask
• Reduction of Beam Divergence Angle by Low-Refractive-Index Layers Introduced to Real-Refractive-Index-Guided GaAlAs High-Power Laser Diodes
• 120 mW High-Power Low-Noise GaAlAs Multiple-Quantum-Well Laser Diodes with a New Real Refractive Index Guided Self-Aligned Structure
• Chromosome arm location of the genes for the biosynthesis of hordatines in barley
• Jasmonate-induced Changes in Flavonoid Metabolism in Barley (Hordeum vulgare) Leaves(Organic Chemistry)
• Occurrence and Characterization of 2-Hydroxy-1,4-benzoxazin-3-one and Indole Hydroxylases in Juvenile Wheat
• Occurrence of hordatines, the barley antifungal compound, in a wheat-barley chromosome addition line
• Specific Heat of a Regenerator Material Er_3Ni
• Magnetic Field Influence on Er_3Ni Specific Heat
• Specific Heat of ErNi in Magnetic Fields and Its Performance as Regenerator Material in Gifford-McMahon Refrigerator at Cryogenic Temperatures
• Indole-3-acetic acid biosynthesis in Aciculosporium take, a causal agent of witches' broom of bamboo
• Stress-induced second harmonic generation in silica glass
• Luminescent properties of amorphous Al_2O_3 prepared by sol-gel method
• Second Harmonic Generation of Thermally Poled ZnCl_2-B_2O_3-TeO_2 Glasses and Its Mechanism
• Second Harmonic Generation from YAl_3(BO_3)_4-Containing Glass-Ceramics Prepared by Thermal Poling of Y_2O_3-Al_2O_3-B_2O_3 Glasses
• Reduction of Threading Dislocations in GaN on Sapphire by Buffer Layer Annealing in Low-Pressure Metalorganic Chemical Vapor Deposition
• ナノプロジェクト研究最前線 ナノガラス研究の最新動向・成果
• ニューガラス関連学会 第20回国際ガラス会議参加報告--ナノガラスシンポジウム
• 大きな二次及び三次の非線形効果をもつガラスの組成設計(第56回日本セラミック協会学術賞受賞研究総説)
• 銀微粒子を分散させた非線形光学材料の開発
• 2価および3価カルボン酸を用いて調製したシリカ–アルミナのn-ドデカン接触分解におけるマトリックスとしての触媒特性
• Induction of N-Hydroxycinnamoyltyramine Synthesis and Tyramine N-Hydroxycinnamoyltransferase (THT) Activity by Wounding in Maize Leaves
• Species-Specific Glucosylation of DIMBOA in Larvae of the Rice Armyworm
• Critical Dimension Controllability Evaluation Based on Process Error Distribution for 150 nm Devices
• 熱ポーリング処理による珪酸および珪酸塩ガラスからの第2高調波発生 (特集 強い電場とガラスの応答)
• 非線形光学ガラスの原理と応用 (特集 「機能ガラス材料」)
• Novel Method for Generating Large Mesopores in an Amorphous Silica-Alumina by Controlling the Pore Size with the Gel Skeletal Reinforcement and Its Catalytic Cracking Properties as a Catalyst Matrix
• 1-5-2 キュリー・ポイント・パイロライザーを用いたゼオライト含有シリカ-アルミナ触媒によるVGO接触分解反応の解析(1-5 重質油,Session1 石炭・重質油等,研究発表)
• 2価および3価カルボン酸を用いて調製したシリカ-アルミナのn-ドデカン接触分解におけるマトリックスとしての触媒特性
• No.52 有機テンプレートを炭素骨格に用いたNi触媒の調製と水熱ガス化反応における担体の効果(研究発表)
• No.22 ゲル骨格補強法による非晶質シリカ-アルミナの調製と接触分解特性の解析(研究発表)
• Second Harmonic Generation of Thermally Poled ZnCl2–B2O3–TeO2 Glasses and Its Mechanism
• ゲル骨格補強法を用いた大きなメソ多孔性物質の調製と接触分解特性の解析
• 微粒子ドープガラスの新しい応用 : 半導体微粒子ドープガラス薄膜の三次の非線形光学効果を中心として
• バルクガラスからの第2高調波発生 (1994年の化学-8-)
• 3次非線形光学半導体微粒子ド-プガラスの作製・評価および新しい応用 (非線形光導波路材料とデバイス応用)
• No.17 階層構造をもつゼオライト含有シリカ-アルミナ触媒の調製とその接触分解反応特性の解析(重質油・コプロセッシング)
• 1-4-1 アルミニウムトリ-sec-ブトキシドを補強剤とするゲル骨格補強による非晶質シリカ-アルミナの調製と接触分解特性の解析(1-4 重質油、接触改質,Session 1 石炭・重質油等)
• 3-7-1 新規炭素担持NiおよびRu触媒の調製とフェノール水の水熱ガス化反応(3-07 水熱・超臨界,Session 3 バイオマス等)
• Second Harmonic Generation from YAl3(BO3)4-Containing Glass-Ceramics Prepared by Thermal Poling of Y2O3–Al2O3–B2O3 Glasses
• The Influence of Matrix on Quantum Size Confinement of Semiconductor Microcrystals Doped in Glass Thin Films Prepared by RF-Sputtering

もっと見る 閉じる

スポンサーリンク