均一沈殿法による単分散TiO2粉末の作製 (微粒子粉末材料とプロセス技術<特集>)
スポンサーリンク
概要
- 論文の詳細を見る
For obtaining monodispersed Ti0<SUB>2</SUB> particles, precipitaion from homogeneous solution (PFHS) method using urea as precipitant was applied at 343K for the formation of titanium hydroxide particles containing sulfate radical from aqueous solution of titanyl sulfate and urea. In the present study, influence of ultrasonic vibration on precipitation reaction was also discussed from the results of TG-DTA analysis, X-ray diffraction, SEM images and particle distribution analysis.<BR>As-prepared precipitates were amorphous particles, and crystalized completely on heating process up to about 1300K with dissociating hydrate and sulfate radical to anatase type Ti0<SUB>2</SUB> powder at about 900K and to rutile type Ti0<SUB>2</SUB> at about 1400K. Particle size and degree of monodispersion of Ti0<SUB>2</SUB> obtained by adding ultrasonic vibration on reaction was smaller and more proceeded than those obtained by conventional precipitation reaction.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 金属工芸用純銅鋳造材および圧延材の硬さにおよぼす溶存酸素の影響
- 203 Fe-Tl合金によるSicのろう接
- 305 セラミックスの耐熱ろう接合(第III報) : Ni-Ti合金によるSi_3N_4の接合
- 118 セラミックスの超音波ろう接(第3報) : Zn-Al合金ろうによる炭化ケイ素と各種金属の接合
- 107 セラミックスの超音波ろう接(第二報) : Zn-Al-Cu合金によるアルミナと銅の接合
- 327 セラミックスの超音波ろう接(第一報) : Zn-Al合金ろうによるアルミナと銅の接合
- MA法およびPMGA法によるNb_3Al組成粉末の放電プラズマ焼結
- 放電プラズマ焼結法によるNb_3Al金属間化合物の合成
- 炭素ケイ素とCu-Ti合金の濡れおよび界面における反応生成物
- 103 セラミックスの耐熱ろう接(第1報) : Ni-Ti合金によるSiCの接合