アモルファスCu-Ti合金ろうによるアルミナと銅の接合
スポンサーリンク
概要
- 論文の詳細を見る
Joining of alumina (99.62mass% Al_2O_3) to copper was made using amorphous Cu-Ti (34-57 at%) brazing filler metals at 1173 to 1323 K in 2.7×10^<-3> Pa. The amorphous filler metals, 1 cm in width and 45 μm thick, were produced by liquid quenching. The superior flexibility of amorphous filler provides simplicity to joining process. The fracture shear strength of the joints was measured at room temperature. The strength of the joints brazed at 1323 K for 1.8 ks using Cu_<50>Ti_<50> filler possesses 138.3 MPa at room temperature. The strength of the joints at constant brazing time raises with an increase in brazing temperature. The strength increases slightly with an increase in titanium content in the filler. At 1298 K for 1.8 ks, the strength of joints at room temperature changes from 107.8 MPa with Cu_<66>Ti_<34> to 120.6 MPa with Cu_<43>Ti_<57>. The strength of the joints was also investigated at high temperatures up to 973 K. The high temperature shear strength is almost constant up to 773 K, and deceases gradually at higher temperature. Isothermal solidification process takes place during joining, and copper dissoves into Cu-Ti filler metal, and then, copper solid solution containing Ti precipitates from Cu-Ti filler metal. On the other hand, the formation of titanium oxide TiO_x and (Al, Ti)_2O_3 solid solution oxide is attributable to the strong joining between alumina and Cu-Ti filler.
- 社団法人溶接学会の論文
- 1986-05-05
著者
関連論文
- Co-Cr-C/Ag/Ti膜の磁気特性に与えるAg中間層効果
- Co-Cr-C/Ag/Ti膜の磁気特性におけるAg中間層効果
- Enhanced Tensile Strength and Plasticity of Zr-Cu-Al Bulk Glassy Alloys at Cryogenic Temperatures
- 溶融Cuをフラックスとして得た新しい層状化合物PrRh_B_2単結晶の化学状態及び性質
- 203 Fe-Tl合金によるSicのろう接
- 305 セラミックスの耐熱ろう接合(第III報) : Ni-Ti合金によるSi_3N_4の接合
- 118 セラミックスの超音波ろう接(第3報) : Zn-Al合金ろうによる炭化ケイ素と各種金属の接合
- 107 セラミックスの超音波ろう接(第二報) : Zn-Al-Cu合金によるアルミナと銅の接合
- 327 セラミックスの超音波ろう接(第一報) : Zn-Al合金ろうによるアルミナと銅の接合
- 17年間大気暴露した耐候性鋼さび層のキャラクタリゼーション
- 420 水素雰囲気中における銀ろう付性の改善(第二報)
- 419 水素雰囲気中における銀ろう付性の改善(第一報)
- 418 金属粉末添加フラックスによるSUS-304ろう付継手の機械的性質
- アノード電着により作製した高温海水電解の酸素発生用Mn-Mo-Fe酸化物アノード
- 地球温暖化防止とエネルギー安定供給のためのキーマテリアルズ
- CO_2 リサイクルプラント用電極および触媒の創製
- グローバル二酸化炭素リサイクル
- ろう付用フラックスの電導度測定結果からみたフラックス作用について(第 2 報)
- 軟ろう付用フラックスの作用機構に関する研究(第 6 報) : Ni, Fe 板上の銀塩と銅塩のフラックス作用
- 軟ろう付用フラックスの作用機構に関する研究 (V) : 無機金属塩
- 3 ろう付用フラックスの作用機構(昭和 48 年度溶接学会関西支部主催学術講演会発表論文概要)
- 溶融金属の粘性係数および自己拡散係数の近似計算
- 325 軟ろう付用フラックスの作用機構に関する研究(第9報) : 溶融Sn中へのZnの溶解におよぼす金属塩の作用
- 炭素ケイ素とCu-Ti合金の濡れおよび界面における反応生成物
- 103 セラミックスの耐熱ろう接(第1報) : Ni-Ti合金によるSiCの接合
- 418 炭化ケイ素とCu-Ti合金のぬれおよび界面における反応生成物
- セラミックス・金属接合研究のまとめと展望 (フォーラム「セラミックスと金属の接合に関する最近の動向」)
- 226 セラミックスの超音波はんだ付(第1報) : Sn-Pb合金はんだによるアルミナと銅の接合
- 219 Al基合金によるアルミナの接合(第3報) : Al-Ag合金によるAl_2O_3のぬれおよび接合
- Al-Cu合金ろうによるアルミナ同士の接合およびアルミナ/アルミニウム接合への適用
- 118 Al基合金ろうによるアルミナの接合(第2報) : Al-Si合金によるAl_2O_3のぬれおよび接合
- 金属ガラスの耐食性
- 口腔内擬似環境におけるチタンの重金属イオン吸着現象
- Influences of Temperature and Strain Rate on Mechanical Behavior of a Cu_Zr_Al_5Ag_5 Bulk Glassy Alloy
- Cu_Zr_Al_5Ag_5 Bulk Glassy Alloy with Enhanced Compressive Strength and Plasticity at Cryogenic Temperature
- Annealing-Induced Devitrification Behavior of a Ti_Zr_Ni_Cu_ Glassy Alloy
- Fabrication and Corrosion Property of Novel Ti-Based Bulk Glassy Alloys without Ni
- Microstructure and Corrosion Resistance of Ti-Zr-Cu-Pd-Sn Glassy and Nanocrystalline Alloys
- Effect of Chloride ion concentration on the fatigue crack growth rate of a Zr55Al10Ni5Cu30 bulk metallic glass
- Corrosion Behavior of Ti-Based Metallic Glasses
- Preparation of a Wide Zr_Al_Ni_5Cu_ Metallic Glass Sheet by a Twin-Roller Type Casting Method and Its Mechanical Properties
- Mechanical Properties of Melt-Spun Amorphous Ni-Nb-Zr Alloys after Hydrogen Charging
- Fracture Toughness of Zr_Al_Ni_5Cu_ Bulk Metallic Glass by 3-Point Bend Testing
- Effect of Tantalum on Corrosion Resistance of Ni-Nb(-Ta)-Ti-Zr Glassy Alloys at High Temperature
- New Cu-Zr-Al-Nb Bulk Glassy Alloys with High Corrosion Resistance
- Hydrogen Evolution Characteristics of Sputter-Deposited Co-Mo, Co-Al and Co-Mo-Al Alloy Electrodes in NaOH Solution
- Application of Sputter Deposition Technique to the Preparation of Amorphous Alloy-Derived Catalysts for NO Decomposition
- The Microcomposite Structure of Catalysts Prepared by Oxidation of Amorphous Ni-Ta-Pd Alloys
- The Corrosion Behavior of Ni-Ta-5P Alloys in Concentrated Hydrochloric Acid
- CO_2 Methanation Catalysts Prepared from Amorphous Ni-Valve Metal Alloys Containing Platinum Group Elements
- The Electrocatalytic Oxidation of Ethylene and Methane, and Reduction of Oxygen on Gas-Diffusion Electrodes Made of Amorphous Nickel-Valve Metal-Platinum Group Metal Alloys
- The Corrosion Behavior of Sputter-Deposited Magnesium-Valve Metal Alloys
- 生体擬似溶液浸漬実験におけるSi汚染の検討
- Temperature-Time-Transformation Curve and Viscous Flow Deformation of Zr_Cu_Al_Ni_5 Bulk Glassy Alloy
- 高温8kmol m^ NaOH溶液中における水素発生のための電析Co-FeおよびCo-Fe-C合金
- 回折による構造解析結果の正しい記述のために
- Amorphous Alloy Electrodes for Electro-oxidation of Propane
- アマルガムとチタンの接触腐食における溶出イオンの増減
- Cu-Ti合金によるSiC/SiC接合体の組織と強度 : 活性金属ろうによるシリコン系セラミックスの接合の研究(第2報)
- Effects of Ion Etching and Annealing in O_2 Atmosphere Following Ion Etching on Properties and Chemistry of Sr_Bi_Ta_2O_ Thin Films
- 細胞毒性の少ない金属元素から構成される新しい生体用チタン基形状記憶合金とその耐食性
- NaCl水溶液中の白金電極における特異な塩素発生機構の解明
- ガスガン法によるアルミニウムと銅の衝撃圧接
- 金属ガラスの化学的性質--耐食性 (特集 金属ガラス--新材料としての最近の展開(上))
- Characterization of Surface of Amorphous Ni-Nb-Ta-P Alloys Passivated in a 12kmol/m^3 HCl Solution
- 長期大気暴露した耐候性鋼さび層のキャラクタリゼーション
- 各種表面分析法による金属表面の反応生成物解析
- 312 Fe-Cr-Mo-C-B(-Nb or Ta)系ガラス合金の作製と耐食性(制御)(日本機械学会東北支部・腐食防食協会東北支部共催セッション)
- 魚肉ペ-スト中におけるステンレス鋼の腐食に関する検討
- Pitting Corrosion of Amorphous Ni-Zr Alloys in Chloride Ion Containing Sulfuric Acid Solutions
- The Role of Phosphorus in Enhancing Corrosion Resistance of Amorphous Alloys
- Recent Progress in Corrosion-Resistant New Alloys Prepared by Sputter Deposition
- Amorphous Alloy Electrodes for Fuel Cells
- High Temperature Sulfidation and Oxidation Behavior of Sputter-Depotited Al-refractory Metal Alloys
- 228 非晶質Cu-Ti合金ろうによるアルミナと銅との接合
- 327 セラミックスの耐熱ろう接(第2報) : Ni-Ti合金によるSiCと金属の接合
- 205 RFスパッタリング法による耐食性アモルファスステンレス鋼膜の形成
- 217 炭化ケイ素とバナジウムの固相接合
- 7. 鉄鋼表面分析のための X 線光電子分光法(鋼材の表面物性とその評価技術 : (II) 分析技術)
- APSIA '98 に参加して
- 金属表面酸化膜のXPSによる定量解析
- ケーススタディ - 電気化学における測定と評価 金属上の酸化皮膜の解析(3) XPSおよびAES
- ESCAによる表面皮膜分析
- アモルファスCu-Ti合金ろうによる窒化ケイ素の接合
- アモルファスCu-Ti合金ろうによるアルミナと銅の接合
- 銅ろうによるアルミナと炭素鋼の接合
- 303 非晶質Ci-Ti- , Ni-Ti合金ろうによる非酸化物系セラミックス(Si_3N_4 , SiC)の接合
- SiCセラミックとTi箔の接合における固相反応機構
- Cu-Ti合金によるSi_3N_4/Si_3N_4接合体の組織と強度 : 活性金属ろうによるシリコン系セラミックスの接合の研究(第1報)
- 325 Cu-Ti合金によるSi_3N_4セラミックス接合部の組織と強度
- 223 Cu-Ti合金によるSiC接合体の強度と組織
- 表面分析の原理と二, 三の具体例
- SiC/Nb接合界面の構造と強度
- 426 SiCとNbの固相接合と反応
- 136 Al基合金ろうによるアルミナの接合(第1報) : Al , Al-Cu合金Al_2O_3のぬれおよび接合
- 218 炭化ケイ素とクロムの固相接合
- 253 炭化ケイ素とチタンの固相接合
- 均一沈殿法による単分散TiO2粉末の作製 (微粒子粉末材料とプロセス技術)
- 均一沈澱法による水酸化チタン(4)から酸化チタン(4)への結晶化過程 (フェライト材料とその応用)
- 130 銅インサート材によるアルミナと軟鋼との接合