Hydrogen Permeability and Membrane Durability of Novel Pd/γ-Alumina Graded Membrane When a Sweep Gas in Used
スポンサーリンク
概要
- 論文の詳細を見る
In this study, Pd/γ-alumina graded membranes were fabricated by an electroless plating method on nanoporous γ-alumina formed by anodic oxidation of an etched aluminum support, and the H2 permeability of the membranes was determined. The Pd/γ-alumina graded membrane on the etched aluminum support was prepared by carrying out electroless plating for 30 min, and for 60 min. In the first case of electroless plating for 30 min, Pd/γ-alumina graded membrane with a thickness of 2.5 μm, H2 flux of 0.28 mol m−2 s−1, and H2/N2 permselectivity of 817 were obtained. In the second case of electroless plating for 60 min, Pd/γ-alumina graded membrane with a thickenss of 4.5 μm, H2 flux of 0.17 mol m−2 s−1, H2/N2 permselectivity of 5259 were obtained. In durability tests, it was observed that the H2 flux increased with time in the initial stage and then become approximately constant after 70 h. The graded membrane exhibited high durability. The membrane formed by 60 min of electroless plating was heated at 773 K for 12 h in a furnace (preheated Pd/γ-alumina graded membrane). The H2 flux of the preheated graded membrane remined approximately constant during the durability test. This result implies that the Pd/γ-alumina graded membrane for the optimum H2 permeation was not obtained by heating because the Pd crystals formed by electroless plating, and recrystallized to form larger grains; this happened because of heating, hybridization of γ-alumina and Pd, and influence of annealing. Finally, we successfully fabricated novel Pd/γ-alumina graded membranes that exhibited high H2/N2 permselectivity, H2 permeability, and durability.
- 社団法人 化学工学会の論文
- 2010-12-01
著者
-
曽根 正人
東京工業大学 精密工学研究所
-
Sakurai Makoto
Department Of Chemical Engineering Tokyo University Of Agriculture And Technology
-
Kameyama Hideo
Department Of Chemical Engineering Tokyo University Of Agriculture And Technology
-
Kameyama Hideo
Department Of Chemical Engineering Faculty Of Engineering Tokyo University Of Agriculture And Techno
-
Sakurai Makoto
Department Of Cardiovascular Surgery Osaka Medical Center For Cancer And Cardiovascular Diseases
-
SESHIMO Masahiro
Department of Chemical Engineering, Tokyo University of Agriculture and Technology
-
OZAWA Minoru
Department of Chemical Engineering, Tokyo University of Agriculture and Technology
-
SONE Masato
Precision and Intelligence Laboratory, Tokyo Institute of Technology
-
Ozawa Minoru
Department Of Chemical Engineering Tokyo University Of Agriculture And Technology
-
Seshimo Masahiro
Department Of Chemical Engineering Tokyo University Of Agriculture And Technology
-
Sakurai Makoto
Department Of Applied Chemistry College Of Engineering Chubu University
-
Sone Masato
Precision And Intelligence Laboratory Tokyo Institute Of Technology
-
Sone Masato
Precision and Intelligence Laboratory, Tokyo Institute of Technology, Yokohama 226-8503, Japan
関連論文
- 超臨界二酸化炭素を用いた電気化学的ナノプレーティング (小特集 超臨界流体と表面処理技術)
- 集団活動でのロジックモデル利用の模擬実験と研究支援システムの発展性検討
- ロジックモデルとバランススコカードの有効性について
- A-9 ロジックモデルとバランススコカードの有効性について(PMコンセプト,日本発信の仕組みP2Mコンセプト明確化と発展的展開-イノベーションを促進し、競争力再生と人材育成に貢献する-)
- 超臨界二酸化炭素共存下での電気めっきによるパラジウム薄膜の作製
- Novel Metal Monolithic Anodic Alumina Catalyst for Methane Catalytic Combustion, the External Heat Source for Methane Steam Reforming
- B-3 大学におけるロジックモデルの効用評価と研究支援システムの発展性検討(モデル化、システム化/活性化と組織,経済危機を突破するイノベーション経営の仕組みと仕掛け-新たなものづくり、ことづくり、絆づくり-)
- Thermal Performance of the Plate Fin Type Reactor with Anodized Alumina Catalyst for Methanol Decomposition
- Evaluation of the Selectivity for Methanol Decomposition over Anodized Alminum Plate Catalyst Coated with Silica
- 438 MEMS用微小レジスト構造部材 : 基板間の接合強度に及ぼす膜厚の影響(T09-3 微小機械システムにおけるマイクロ・ナノ力学(3) マイクロ・ナノ実験力学,大会テーマセッション,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- 2833 MEMS用微小構造部材-基板間の密着強度に及ぼすプロセス条件の影響(S08-2 微小機械設計・開発のための実験力学の新展開(2),S08 微小機械設計・開発のための実験力学の新展開)
- 2840 マイクロ試験片中の応力集中部が疲労特性へ及ぼす影響(S08-3 微小機械設計・開発のための実験力学の新展開(3),S08 微小機械設計・開発のための実験力学の新展開)
- 電解研磨による微小サイズ引張試験片作製法の開発
- 超臨界二酸化炭素を用いた電気化学的ナノプレーティング
- 超臨界二酸化炭素と共存するニッケルめっき浴環境における金属材料の電気化学特性と適正材料選定の研究
- 産学官連携テーマにおけるスキームモデルリスクマネジメント
- スキーム段階におけるICTシステムのサービスモデル策定テンプレートの提案
- 水道施設の更新におけるアセットマネジメント及びP2M手法適用の考察
- Investigation of Anodic Alumina Supported Silver Catalyst for the Selective Reduction of NO by Propene: Promotional Effect of Hydrogen and Effect of Electrical Heating
- Propene-SCR of NO over Electrically Heating Anodic Alumina Supported Silver Catalyst
- 215 超臨界ナノプレーティングシステム (SNP) の実用化研究
- 超臨界二酸化炭素の電気めっき方法への応用--超臨界ナノプレイティング(SNP)システム (超臨界最新技術特集第6号)
- 寄稿 超臨界ナノプレイティングシステム--超臨界状態の二酸化炭素を用いた新しいめっき技術
- 超臨界二酸化炭素を用いた新規めっき法の開発--超臨界ナノプレイティング(SNP)システム (技術特集2 高機能・低環境負荷"めっき")
- Hydrogen Production through Ethanol Steam Reforming on Conducting Heating Alumite Catalysts
- Promotional Effect of Titanium on the Catalytic Performance of Anodic Alumina Supported Silver Catalyst for the Selective Reduction of NO with Propene
- アルマイト触媒の製造技術とエネルギー変換技術と環境浄化技術への応用
- The Effect of SO_2 and H_2O on the SCR-C_3H_6 of NO over a Transition Metals Supported Mesh-type Alumite Catalyst
- 陽極酸化アルミナ触媒を用いたディーゼル排ガスにおけるNOの選択還元
- Selective Catalytic Reduction of Nitric Oxide by Propene over a Cu-Mn-CeO_x/Al_2O_3/Al Alumite Catalyst
- Preparation of Alumite Support and Preliminary Activity Investigation for NO Removal in SCR-HC over Alumite Catalyst
- 超臨界二酸化炭素を用いた新規な電気化学的表面処理方法 (特集 環境機能性溶媒の展望)
- Cu-Zn/Al_2O_3/Al-Plate Catalyst for a Methanol Reformer
- Performance Simulations of a Compact Plate Methane Steam Reformer Using an Electrically Heated Alumite Catalyst
- Development of CO_2 Adsorbent on Anodic Alumite for Ethanol Steam Reforming
- Study on the Electro-Deposition of Platinum on Anodic Alumite Films for Catalytic Combustion of VOCs
- Sintering Effect of Platinum Catalysts on VOCs' Catalytic Combustion
- Two-Dimensional Coaxial Model for a Cylinder Methane Steam Reformer Using a Novel Plate Catalyst
- Preparation of Platinum Catalysts Supported on Anodized Aluminum for VOC Catalytic Combustion : The Effect of Sintering
- Catalytic Oxidation of Dichloromethane over Anodized Aluminum Film
- Preparation of Anodised Aluminium Catalysts by an Electrolysis Supporting Method for VOC Catalytic Combustion
- Preparation of Platinum Catalysts Supported on Anodized Aluminum for VOC Catalytic Combustion : The Effect of Supporting Method
- 超臨界二酸化炭素を用いたナノプレーティング (新春特集 ナノテクノロジーのための超臨界流体技術)
- 超臨界ナノプレイティングシステムと高分子の役割
- 3C18 大きな2次の非線形光学効果を示す芳香族ポリエステル系ネマティック液晶
- 2B514 ピロメリット酸の1,4-ジアルキルエステルを含む剛直棒状ポリエステル. 2
- 2B513 ピロメリット酸の1,4-ジアルキルエステルを含む剛直棒状ポリエステル. 1
- Synthesis of Anodic Alumina Nickel Catalysts and Deactivation Studies over Them for Methane Steam Reforming under Accelerated Degradation Testing
- Plate-Type Anodic Alumina Supported Ruthenium Catalysts for Steam Reforming of Kerosene: Influence of Calcination on Catalysts Reactivity
- Effect of Pore Widening Treatment on BET Surface Area of Rapidly Anodized Alumina Support
- A Plate-Type Anodic Alumina Supported Nickel Catalyst for Methane Steam Reforming
- Selective Catalytic Reduction of Nitric Oxide with Propene Using an Anodic Alumina Supported Silver Catalyst : NO_x Adsorption, TPD and TPSR Studies
- Development of a Methane Steam Reformer Using an Electrically Heated Alumite Catalyst: Start-Up Performance Investigated by the Numerical and Experimental Analysis
- Selective Catalytic Reduction of Nitric Oxide with Propene and Diesel Fuel as Reducing Agents over Anodic Alumina Catalyst
- ポリオレフィンの液晶化 : 分子設計からのアプローチ
- 3B06 ポリオレフィンによるネマチック液晶の発現(2004年日本液晶学会討論会)
- Plate Anodic Alumina-supported Nickel Catalysts in Steam Reforming of Methane : Effects of Hydrogen Addition, Electrical Heating, and Pt Doping
- Study of Plate-Type Ru/Ceria-Al_2O_3 Catalysts for Kerosene Steam Reforming
- Study of Plate-Type Anodic Alumina Supported Ru Catalyst for Kerosene Steam Reforming under Electric Heating Pattern
- Reactivity Improvement of Fe-Compounds for the UT-3 Thermochemical Hydrogen Procduction Process
- Development of Platinum Catalyst on an Extremely Thin Alumite Film for VOC Catalytic Combustion
- Non-Equilibrium Hydrogen Production from Ethanol Using CO_2 Absorption Ceramic and Precious Metal Catalysts
- Steam Reforming of Ethanol Using Silica-Coated Alumite Catalysts on Aluminum Plates (JIS A1050)
- Hydrogen Production from Ethanol Using a CO_2 Absorption Ceramic and Base Metal Catalysts
- Steam Reforming of Ethanol Using Silica-Coated Alumite Catalysts on Aluminum Plates (JIS A3003)
- Hydrogen Production from Ethanol Using a Plasma Reactor with an Alumite Catalyst Electrode
- アカデミアシリーズ 超臨界ナノ無電解プレーティングを活用したNi-P薄膜の形成
- Energy Performance Analysis of Heat Transport System Using Methanol Decomposition and Synthesis
- P2M理論を応用した地域活性化環境プラットフォーム構築
- Effect of Ru and Pt Addition over Plate-type Catalysts for Methane Steam Reforming during Daily Start-up and Shut-down
- A-5 水道施設の更新におけるアセットマネジメント及びP2M手法適用の考察(社会インフラ/産学官連携トラック)
- Characteristics of University Spin-offs in Chemistry and their Business Relationships with Manufacturers
- Development of Plate-Fin-Type Methanol Reformer
- B-8 スキーム段階におけるICTシステムのサービスモデル策定テンプレートの提案(P2M理論研究トラック)
- A-6 産学官連携テーマにおけるスキームモデルリスクマネジメント(社会インフラ/産学官連携トラック)
- A-6 P2M理論を応用した地域活性化環境プラットフォーム構築(グローバル競争/環境プロジェクト研究トラック)
- Novel Metal Monolithic Anodic Alumina Catalyst for Methane Catalytic Combustion, the External Heat Source for Methane Steam Reforming
- Plate-Type Anodic Alumina Supported Ruthenium Catalysts for Steam Reforming of Kerosene : Influence of Calcination on Catalysts Reactivity
- Effects of Aspect Ratio of Photoresist Patterns on Adhesive Strength between Microsized SU-8 Columns and Silicon Substrate under Bend Loading Condition
- Hydrogen Permeability and Membrane Durability of Novel Pd/γ-Alumina Graded Membrane When a Sweep Gas in Used
- Propene-SCR of NO over Electrically Heating Anodic Alumina Supported Silver Catalyst
- Investigation of Anodic Alumina Supported Silver Catalyst for the Selective Reduction of NO by Propene : Promotional Effect of Hydrogen and Effect of Electrical Heating
- アカデミアシリーズ 超臨界流体技術を用いたナノ組織金属材料の創製
- Catalytic Oxidation of Volatile Organic Compounds over Co-Based Catalysts Supported on Charcoal from Thinned Wood
- 開発途上国における開発計画策定支援の意義とその実行へのPPP適用に関する研究 : 3Sモデルによる開発プロセスの適正化
- ODA事業におけるステークホルダーマネジメントの実践構造化 : 環境社会配慮における合意形成プロセスの最適化
- P2M理論を適用することによる「三位一体」経営の提唱
- P2Mからみた社会的環境プラットフォーム構築へのアプローチ
- A4 特許事務所をプラットフォーム・リーダーとするプラットフォームの提唱(戦略シナリオトラック)
- A3 TRIZを活用した研究開発マネジメントの提唱(戦略シナリオトラック)
- D2 企業R&Dにおけるプラットフォームマネジメントの実践(組織と意思決定トラック)
- C4 P2Mからみた社会的環境プラットフォーム構築へのアプローチ(システムズ・アプローチ研究トラック)
- C1 開発途上国における開発計画策定支援の意義とその実行へのPPP適用に関する研究 : 3Sモデルによる開発プロセスの適正化(システムズ・アプローチ研究トラック)
- D3 P2M理論によるITサービス産業の水平連携プラットフォームの構築(組織と意思決定トラック)
- B3 P2M理論を適用することによる「三位一体」経営の実現可能性(戦略経営研究トラック)
- 環境調和型ゼロエミッション次世代半導体配線形成方法の研究開発
- Operating Temperature Conditions for Periodic Temperature Cycling in a Microreactor
- 超臨界ナノプレーティング法の開発と超微細配線への応用 (特集 めっき技術の未来を見つめる)
- Effects of Specimen Dimensions on Adhesive Shear Strength between a Microsized SU-8 Column and a Silicon Substrate
- 超臨界ナノプレーティング法の開発と超微細配線への応用