充てん剤系加硫ゴムの構造と力学的刺激による構造変化
スポンサーリンク
概要
- 論文の詳細を見る
The structure of vulcanized rubbers filled with carbon blacks has been investigated by using the pulsed NMR method.The molecular motion and the amount of the degenerated rubber phase (C-phase) formed around the carbon blacks and the rubber phase (A-phase) apart from the carbon blackes have been analysed. The structure of filled vulcanized rubber has been compared with that of vulcanizates without fillers and that of plastics from the view point of the degree of molecular motion. At the same time our previous exprimental results on structural change of filled vulcanizates due to mechanical stimuli have been re-examined and the following concousions have been deduced.(1) The vulcanized rubber filled with carbon blacks consists of a quasi-glassy plase (C-phase) around filler particles and a liquidlike phase (A-phase) apart from filleres. The molecular motion of rubber molecules in the former phase is rather restrictive and it gives the NMR half width of about 5 gauss. The thickness of the C-phase is about 45Å in the case of ISAF grade Carbon blacks, although it depends upon the reinforcement of the fillers.On the other hand, the molecular motion in the latter phase, though it depends on the crosslink density, is as free as in the liquid, showing NMR half width of about 60-120m gauss in the case of natural rubber when the chain length between crosslinks Nl is in the range of 1000-150Å.(2) A carbon black filled vulcanizates is a micro-heterogneous mixture of thermodynamically different phases-liqidlike phase and solidlike phase. Each phase changes to the more stable state by mechanical stimuli, namely to the more disordred state and to the more ordered state, respectively and the heterogeneity in the system develops.The degree of change in both phases is propotional to the amount of the C-phase formed around the fillers.(3) As the motion of rubber molecules in the A-phase is almost similar to that in the liquid, the fillers in the vulcanizates move to their more stable positions at a given condition by rotational and translational motions under mechanical stimuli.
- 日本ゴム協会の論文
著者
関連論文
- ゴムの構造と特性(非金属材料)
- 5a-AD-5 高分子混合系のミクロ相分離
- 28 非空調室の室温変動実例と理論解析 : 間仕切パネルの熱的性能(環境工学)
- ゴム粉複合加硫物強さに対する加硫剤最適量
- ゴムの振動疲労
- ゴムの破壊過程の研究 (その6) : 加硫ゴムの疲労破壊での限界応力と伸び
- ゴムの破壊過程の研究 (その5)疲労破壊での臨界クラックと疲労破壊機構
- ESRによるカーボンブラックの作用機構の研究
- ゴムの不均質構造と破壊挙動に関する熱力学的考察
- 主鎖構造の異なるSBR加硫物の引張破壊特性 : ゴムの破壊機構に関する研究 (第8報)
- ゴムの破壊過程の研究 (その 2) 一定応力繰り返し条件下での疲労破壊過程 : ゴムの破壊機構に関する研究 (第9報)
- ゴムの破壊過程の研究 (その1) : ゴムの破壊機構に関する研究 (第7報)
- ゴムの破壊特性の温度依存性を記述する経験式
- 充てん剤系SBR加硫物の破壊包絡線における屈折現象
- 純ゴム系および充てん剤系SBR加硫物の引張破壊特性
- 純ゴム系および充てん剤系NR加硫物の引張破壊特性
- 共重合体加硫ゴムの引張破壊特性 : ゴムの破壊機構に関する研究 (第2報)
- 天然ゴム加硫物の破断時伸びについて
- スチレン量の異なるSBR加硫物の引張破壊特性
- 充てん剤系加硫ゴムの伸張による分子配向
- スチレン含量の異なるSBRとBRの相溶性 : ポリマーブレンドの研究 (第2報)
- ゴムの誘電分散
- 力学分散から見た SBR/BR ブレンド加硫および未加硫ゴムの相溶性 : ポリマーブレンドの研究 (第3報)
- ゴム
- 加硫天然ゴムの伸張時のポアソン比について
- ゴム粉〜マトリックスゴム界面近傍での硫黄移行現象と自由体積の不連続性-1-
- 熱分解回収カ-ボンの物理的性質
- 充てん剤系未加硫ゴムの分子運動の研究
- 円柱型ゴムの局部ひずみと疲労寿命
- SBR〜低分子物質混合加硫物系の力学特性
- 充てん剤系加硫ゴムの構造と力学的刺激による構造変化
- 充てん剤加硫ゴムの熱刺激による構造変化と力学的刺激との類似性
- 機器から見たゴムの物理と化学-終-核磁気共鳴(NMR)(講座)
- ゴムの不均質構造と破壊ならびに疲労現象
- 未加硫ゴム〜低分子物質混合系の研究
- 材料設計 (最近のゴム配合設計(特集))
- 複合材料 (ゴム科学の現状(特集))
- ABSTRACTS