天然ゴム加硫物の破断時伸びについて
スポンサーリンク
概要
- 論文の詳細を見る
Following the previous paper_<1)> on the tensile properties of the noncrystallized amorphous rubber, the properties of natural rubber (NR) crystallized in a high elongated state are reported in the present studies. The gum vulcanizates of various crosslink densities, and the filled vulcanizates of various carbon black contents were prepared. The tensile properties of these samples were studied, with particular reference to their ultimate elongation and their comparative studies were made with the molecular chain mobility and the polymer structure. The following conclusions were obtained. (1) The crystallized rubber showed "the large" ultimate elongation up to about 100℃, while noncrystallized rubber showed it no more than about -20℃. The abrupt increase of ultimate elongation in the transition region is consistent with the previous finding. (2) The large ultimate elongation at high temperature is interpreted as the result of increase in strength, based on the crystallization on stretching, and of increased mobility of molecular chains. The ultimate elongation and the temperature of maximum ultimate elongation were correlated with the network chain length. That is, while the former is reciprocally proportional to the square-root of the crosslink density, the latter is related to the crosslink density inverse. (3) The influence of the apparent network chain density on the tensile properties of the filled vulcanizates, is apparently opposite to the case of the gum vulcanizates. This tendency is considered to be due to the fact that the rubber molecules constitute the heterogeneous dense structure on the filler surface. In the region far from the filler particles where the molecules take part in the crystallization on stretching, the molecular chain length between the crosslinks is larger as the filler content increases. Thus the temperature of maximum ultimate elongation increases. On the other hand, the ultimate elongation is assumed to be determined by the apparent network chain density.
- 社団法人日本材料学会の論文
- 1967-07-15
著者
関連論文
- 28 非空調室の室温変動実例と理論解析 : 間仕切パネルの熱的性能(環境工学)
- ゴム粉複合加硫物強さに対する加硫剤最適量
- ゴムの振動疲労
- ゴムの破壊過程の研究 (その6) : 加硫ゴムの疲労破壊での限界応力と伸び
- ゴムの破壊過程の研究 (その5)疲労破壊での臨界クラックと疲労破壊機構
- ESRによるカーボンブラックの作用機構の研究
- ゴムの不均質構造と破壊挙動に関する熱力学的考察
- 主鎖構造の異なるSBR加硫物の引張破壊特性 : ゴムの破壊機構に関する研究 (第8報)
- ゴムの破壊過程の研究 (その 2) 一定応力繰り返し条件下での疲労破壊過程 : ゴムの破壊機構に関する研究 (第9報)
- ゴムの破壊過程の研究 (その1) : ゴムの破壊機構に関する研究 (第7報)
- ゴムの破壊特性の温度依存性を記述する経験式
- 充てん剤系SBR加硫物の破壊包絡線における屈折現象
- 純ゴム系および充てん剤系SBR加硫物の引張破壊特性
- 純ゴム系および充てん剤系NR加硫物の引張破壊特性
- 共重合体加硫ゴムの引張破壊特性 : ゴムの破壊機構に関する研究 (第2報)
- 天然ゴム加硫物の破断時伸びについて
- スチレン量の異なるSBR加硫物の引張破壊特性
- 充てん剤系加硫ゴムの伸張による分子配向
- スチレン含量の異なるSBRとBRの相溶性 : ポリマーブレンドの研究 (第2報)
- ゴムの誘電分散
- ゴムの科学はどこへ行く
- 力学分散から見た SBR/BR ブレンド加硫および未加硫ゴムの相溶性 : ポリマーブレンドの研究 (第3報)
- ゴム
- 加硫天然ゴムの伸張時のポアソン比について
- ゴム粉〜マトリックスゴム界面近傍での硫黄移行現象と自由体積の不連続性-1-
- 熱分解回収カ-ボンの物理的性質
- 充てん剤系未加硫ゴムの分子運動の研究
- 円柱型ゴムの局部ひずみと疲労寿命
- SBR〜低分子物質混合加硫物系の力学特性
- 充てん剤系加硫ゴムの構造と力学的刺激による構造変化
- 充てん剤加硫ゴムの熱刺激による構造変化と力学的刺激との類似性
- 機器から見たゴムの物理と化学-終-核磁気共鳴(NMR)(講座)
- ゴムの不均質構造と破壊ならびに疲労現象
- 未加硫ゴム〜低分子物質混合系の研究
- 材料設計 (最近のゴム配合設計(特集))
- 複合材料 (ゴム科学の現状(特集))
- ABSTRACTS