窒化物系セラミックスの歯科鋳造への応用 : 第3報石膏系外埋没材を用いた場合のCo-Cr合金に対するコーティング材としての可能性

概要

論文の詳細を見る
Nitrides used in this experiment are h-BN, AIN and Si_3N_4. The feasibility of using the nitrides was studied as wax pattern coating materials for a Co-Cr alloy in an atmosphere of argon. Wax patterns were painted with the nitride coating material (first investing), and then it was outer-invested witla a mixture of gypsum-bonded investment and water (second investing). The temperature of mold was 700℃, and the thin specimens were cast with an argon arc vacuum-pressure casting machine in the Co-Cr alloy (composition Co : 63 wt%, Cr : 27, Mo : 5, Bat. : 5 ; melting point : 1,380℃). Surfaces of cast specimens were investigated with the unaided eye, a scanning electron microscope, a surface roughness analyzer, an X-ray diifractometer and a micro-Vickers hardness tester. Furthermore, the cast clasp using an h-BN coating material were made and investigated with the unaided eye. Results were sumcmarized as follows : 1. The nitrides inhibited remarkably a reactiona between the cast specimen and the investment. 2. BN had the good effect of separation. 3. The cast surface coated BN had less clitaging than uncoated one. This indicated that cleansability and work efficiency were improved. 4. The surface roughness (Rz) of the specimens decreased to 32, 42 and 60% of the control with BN, Si_3N_4 and AlN, respectively. 5. A hardness change of the alloy by casting was the least in the case of using BN. 6. BN also had the effect in fabricating a cast clasp in the clinical form.
日本補綴歯科学会の論文
1990-12-01

窒化物系セラミックスの歯科鋳造への応用 : 第3報石膏系外埋没材を用いた場合のCo-Cr合金に対するコーティング材としての可能性

スポンサーリンク

概要

著者

関連論文

スポンサーリンク

窒化物系セラミックスの歯科鋳造への応用 : 第3報 石膏系外埋没材を用いた場合のCo-Cr合金に対するコーティング材としての可能性

スポンサーリンク

概要

著者

関連論文

スポンサーリンク

窒化物系セラミックスの歯科鋳造への応用 : 第3報石膏系外埋没材を用いた場合のCo-Cr合金に対するコーティング材としての可能性