Fracture Strength of Explosive Clad Steel with Surface Notch
スポンサーリンク
概要
- 論文の詳細を見る
Fracture performance of an explosive clad steel composed of 5US304 stainless steel and HT80 high strength steel is investigated. To clarify the effects of composite structures and metallurgical properties on the fracture strength and the fracture strain, tensile tests are carried out by using homogeneous and heterogeneous specimens which are extracted from the clad plate and have an artificial surface notch. The critical value of stress for the macroscopic unstable fracture initiation of the heterogeneous specimen with a surface notch in SUS3O4 steel is larger than that of the homogeneous SUS3O4 steel specimen over all the test temperature range, and also larger than that of the homogeneous HT8O steel specimen at a very low temperature. The fracture strain of the heterogeneous specimen with a surface notch in SUS3O4 steel lies between that of the homogeneous SUS3O4 steel specimen and that of the homogeneous HT8O steel specimen over all the test temperature range. The critical crack mouth opening displacement of the heterogeneous specimen with a surface notch in SUS3O4 steel is lower than that of the homogeneous SU5304 steel specimen.
- 社団法人溶接学会の論文
- 1985-10-01
著者
-
Tatsukawa Itsuro
Faculty Of Engineering Kumamoto University
-
SATOH Kunihiko
Faculty of Engineering, Osaka University
-
TOYODA Masao
Faculty of Engineering, Osaka University
-
Toyoda Masao
Faculty Of Engineering Osaka University
-
ODA Isamu
Faculty of Engineering, Kumamoto University
-
Satoh Kunihiko
Faculty Of Engineering Osaka University
-
Oda Isamu
Faculty Of Engineering Kumamoto University
関連論文
- Stress/Strain Controlling Parameter of Cracked Plate with Mechanical Heterogeneity
- Effect of Mechanical Heterogeneity on Fracture Toughness Evaluation of Steel Welds
- A Proposal of Generalized COD Criterion and Its Application to Welds
- Stresses-Strains and Fracture Behavior of 9% Ni Steel Weldments
- Crack Tip Plastic Deformation of Notched Plates with Mechanical Heterogeneity
- A Proposal on 3 Point Bending COD Test Method for Welded Joint of 9% Ni Steel
- Fracture Strength of Explosive Clad Steel with Surface Notch
- Fracture Strength of Explosive Clad Steel with Surface Flaw
- Fracture Toughness of Explosive Stainless-Clad HT80 High Strength Steel
- Mechanism of Fibrous Crack Growth under Constant Loading
- Welding -Deformations of Thick Cylindrical-Vessels by Narrow-Gap GMAW of Longitudinal Joints
- Theoretical Study on Transient Restraint Stress in Multi-pass Welding
- Weld Cracking Behavior of 100kg/mm^2 High Strength Steel By Large Size Restraint Testing Machine
- Study on Weld Cracking in Multiple Pass Welds of High-Strength Steel
- Mechanical Controlling Factor of Weld Hydrogen Cracking
- Probabilistic Analysis of Fracture Toughness of Weld HAZ with LBZ
- A Probabilistic Approach to Evaluation of Fracture Toughness of Welds with Heterogeneity
- Probabilistic Analyses on Scatter of Cleavage Fracture Toughness of Welds with Heterogeneity along Crack Front
- Effects of Fracture Controlling Factors on Cleavage Fracture Initiation in Specimens with Heterogeneity along Crack Front
- Study on Reasonable Inspection Method for Welds Considering Detectability of NDT
- Influence of Hot Straining Embrittlement on Brittle Fracture in Welded Steel Plates
- 8. Weld Cracking Behavior under Restraint
- Prevention of Weld Crack in HT80 Heavy Plates with Undermatching Electrodes and its Application to Fabricating Penstock
- Some Metallurgical Observations on Heating of Explosive Austenitic Stainless Clad Steel
- Residual Stress Measurements on Explosive Stainless Clad Steel
- Adiabatic Shear in Explosive Austenitic Stainless Clad Steel
- Inference of Mechanical Properties of Heat Treated Steel from Ultrasonic Attenuation and Velocity Measurements
- Distortions and Residual Stresses in Arc Welding
- Study on Explosive Welding of Austenitic Stainless Steel to 80 kg/mm^2 Class High Strength Steel
- Interfacial Phenomena in Explosive Welding of Al-Mg Alloy/Steel and Al-Mg Alloy/Titanium/Steel
- Distortions and Residual Stresses in Submerged Arc Welding of 80 kg/mm^2 Class High Strength Steel
- Transient Creep of Mild Steel and High-Strength Steel under Bending