Effects of Fracture Controlling Factors on Cleavage Fracture Initiation in Specimens with Heterogeneity along Crack Front
スポンサーリンク
概要
- 論文の詳細を見る
- 社団法人溶接学会の論文
- 1982-10-01
著者
-
Toyoda M
Osaka Univ.
-
Satoh K
Department Of Welding & Production Engineering Faculty Of Engineering Osaka University
-
Toyoda Masao
Department Of Welding & Production Engineering Faculty Of Engineering Osaka University
-
Toyoda Masao
Faculty Of Engineering Osaka University
-
Satoh K
Faculty Of Engineering Osaka University
-
Minami Fumiyoshi
Department Of Welding & Production Engineering Faculty Of Engineering Osaka University
関連論文
- Stress/Strain Controlling Parameter of Cracked Plate with Mechanical Heterogeneity
- Effect of Mechanical Heterogeneity on Fracture Toughness Evaluation of Steel Welds
- A Proposal of Generalized COD Criterion and Its Application to Welds
- Stresses-Strains and Fracture Behavior of 9% Ni Steel Weldments
- Crack Tip Plastic Deformation of Notched Plates with Mechanical Heterogeneity
- A Proposal on 3 Point Bending COD Test Method for Welded Joint of 9% Ni Steel
- Fracture Strength of Explosive Clad Steel with Surface Notch
- Fracture Strength of Explosive Clad Steel with Surface Flaw
- Fracture Toughness of Explosive Stainless-Clad HT80 High Strength Steel
- Mechanism of Fibrous Crack Growth under Constant Loading
- Welding -Deformations of Thick Cylindrical-Vessels by Narrow-Gap GMAW of Longitudinal Joints
- Experimental Investigation on Applicability of Stress Field Parameter F_I for Weld Hydrogen Cracking
- Mechanical Controlling Factor of Weld Hydrogen Cracking
- Probabilistic Analysis of Fracture Toughness of Weld HAZ with LBZ
- A Probabilistic Approach to Evaluation of Fracture Toughness of Welds with Heterogeneity
- Development and Application of New Sampling Inspection System for Welds of Steel Buildings
- Probabilistic Analyses on Scatter of Cleavage Fracture Toughness of Welds with Heterogeneity along Crack Front
- Effects of Fracture Controlling Factors on Cleavage Fracture Initiation in Specimens with Heterogeneity along Crack Front
- Study on Reasonable Inspection Method for Welds Considering Detectability of NDT
- Influence of Hot Straining Embrittlement on Brittle Fracture in Welded Steel Plates
- Controlling Parameters of Residual Stresses and Deformations in Welded Thin Cylindrical Shells
- Detection of Apoptotic Cells in Human Colorectal Cancer by Two Different in situ Methods : Antibody against Single-stranded DNA and Terminal Deoxynucleotidyl Transferase-mediated dUTP-biotin Nick End-labeling (TUNEL) Methods
- Fracture Toughness Evaluation of Welds with Mechanical Heterogeneity
- Prevention of Weld Crack in HT80 Heavy Plates with Undermatching Electrodes and its Application to Fabricating Penstock
- Sampling Inspection Method Taking the Properties of Weld Defects Occuring into Account : An Application for Welded Steel Framed Structure
- Regression of Lymph Node Metastases by Immunotherapy Using Autologous Breast Tumor-Lysate Pulsed Dendritic Cells : Report of a Case
- Minimally invasive tailor-made surgery for colorectal cancer by laparoscopy