CO_2ガスを利用したチタンおよびチタン合金の表面硬化処理(加工・加工熱処理)

概要

論文の詳細を見る
Surface hardening treatment of C.P. titanium, α+β type Ti-4.5%Al-3%V-2%Mo-2%Fe(SP-700 alloy) and β type Ti-15%V-3%Al-3%Cr-3%Sn alloy in use of Ar-20%CO_2 gas was studied at temperatures between 973 to 1123K in comparison of Ar-20%O_2 gas. Weight gain of the specimen during heating was measured by an electric balance, and surface oxide layer thickness was also measured. Surface hardening was evaluated by measurement of micro-hardness distribution profile in the surface layer. Surface hardening due to Ar-20%O_2 gas yielded the larger maximum surface hardness value and thicker hardening layer thickness in all three titanium materials compared with Ar-20%O_2 gas. The largest surface hardness value was obtained in C.P. titanium, and β type titanium alloy resulted in the most thick hardening layer thickness although the surface hardness value was the smallest among three titanium materials. The maximum surface hardness and hardening layer thickness obtained in use of Ar-20%O_2 gas was larger than these of Ar-20%O_2 gas in C.P. titanium, nevertheless the former gas yielded higher oxidation rate over the latter gas. The oxidation rate was the smallest in SP-700 alloy among three titanium materials in both gases. Surface hardening due to Ar-20%O_2 gas in C.P. titanium was brought about by solid solution hardening due to oxygen and carbon.
社団法人日本鉄鋼協会の論文
2006-01-01