MOCVD法によるCa-Ti-OおよびCa-P-O系傾斜機能バイオセラミックス膜の合成
スポンサーリンク
概要
- 論文の詳細を見る
Ca-Ti-O and Ca-P-O films were prepared by MOCVD. The phases, composition and morphology of Ca-Ti-O and Ca-P-O films changed depending on the molar ratio of Ca to Ti (RCa/Ti) and Ca to P (RCa/P) precursors, total pressure (Ptot) and substrate temperature (Tsub). CaTiO3 films in a single phase were obtained at Tsub=973 and 1073 K. CaTiO3 films prepared at Tsub=873 K had a dense and smooth surface. CaTiO3 films prepared at Tsub=1073 K had complicated rough surface with a cauliflower-like texture. α-TCP and HAp films in a single phase were obtained at Tsub=973 and 1073 K, and both films had dense microstructure. Apatite formed after 3 days on the CaTiO3 film, while 14 days on the α-TCP film and 6 hours on the HAp film, respectively. Functionally graded Ca-Ti-O/Ca-P-O films were successfully prepared by MOCVD, and expected to have good bone conductivity and adherence to Ti substrate.
- 社団法人粉体粉末冶金協会の論文
- 2008-05-15
著者
-
後藤 孝
東北大学金属材料研究所
-
後藤 孝
東北大金研
-
後藤 孝
東北大学金属材料研究所複合機能材料学部門
-
佐藤 充孝
東北大学金属材料研究所附属施設大阪センター
-
後藤 孝
Institute For Materials Research Tohoku University
-
塗 溶
東北大学金研材料研究所
-
上田 恭介
東北大学金研材料研究所
-
成島 尚之
東北大学工学研究科
-
佐藤 充孝
東北大金研
-
塗 溶
東北大金研
-
成島 尚之
Department Of Materials Processing Tohoku University
-
Nezu Takashi
Department Of Dental Materials Science And Technology Iwate Medical University School Of Dentistry
-
後藤 孝
東北大
-
塗 溶
東北大学金属材料研究所
関連論文
- Thermoelectricity of CaIrO_3 ceramics prepared by spark plasma sintering
- 放電プラズマ焼結法によるAl_2O_3-cBN傾斜材料の作製
- Thermoelectric Properties of Ca-Ir-O Compounds Prepared by Spark Plasma Sintering
- チタン上への多層リン酸カルシウムコーティング膜の作製とその評価
- Apatite formation behavior on bio-ceramic films prepared by MOCVD
- 高速CVDコーティングにおけるレーザーのベクトル効果 (特集 ベクトル材料科学(その1))
- 炭化ホウ素系複合セラミックス (特集 応用の拡がる熱電変換素子の新展開)
- 1927 溶融鉛ビスマス用酸素濃度計の開発研究
- レーザーCVDによる耐熱コーティング
- Precipitation Behavior in a Hanks' Solution on Ca-P-O Films Prepared by Laser CVD