水圧力媒体を用いた助剤無添加窒化ケイ素粉末の爆発衝撃固化

概要

論文の詳細を見る
Silicon nitride powder compacts without additives were produced by underwater-shock wave. The as-compacted specimens and sintered ones at various temperatures were characterized by relative density, micro Vickers hardness and fracture toughness. Microstructural characterization was also made by SEM and TEM. The relative density of an as-compacted specimen was about 75%, but hardness value was quite low about 2 GPa. Mechanical properties were remarkably improved by sintering. Hardness and fracture toughness values of the specimen sintered at 1973 K for 5h were about 24 GPa and about 4 MPa √<m>, respectively, TEM observation of the compact sintered at 1973 K showed that there was no large glass pockets at grain boundary edges and that the glass phases at grain boundary surfaces were a few atoms thick.
社団法人日本セラミックス協会の論文
1992-10-01