The effect of shock pressure on the stress-strain behavior of a low-carbon steel of four different grain sizes, 9, 16, 33 and 80μm, was investigated. The specimens were explosively shock-1oaded in water. The shock pressure effect was compared with the effect of pressurizing or temper rolling on the stress-strain behavior. Sensibility to twinning induced by shock loading was also examined. Results obtained in this investigation are summarized as follows. ( 1 ) The yield stress of all kinds of specimens began to decrease at the shock pressure of 300 MPa and continued to decrease to the minimum with increasing pressure, owing to generation of free dis1ocations in the specimens. For the specimen of smaller grain size, the amount of decrease in the yield stress became larger and the shock pressure (p_s)_m which minimized the stress became higher. ( 2 ) Yield ratio of the specimens of four different grain sizes of 9, 16, 33 and 80 μm, which had the original ratios of 0.80, 0.76, 0.65 and 0.52,respectively, could all be reduced to about 0.4 after shock loading. ( 3 ) The shock pressure (p_s)_t at which the mechanical twins began to form in the specimen increased linearly with increasing d^<-1/2>,which is a reciprocal of the square root of grain size d. Twin density, defined as the ratio of number of crystal grains with twins to total number of grains, was larger in the specimen with larger grain size and the density increased monotonously with increasing shock pressure. ( 4 ) For the specimen with a given grain diameter, the shock pressure (p_s)_m at which the yield stress became the minimum was identical in value to the pressure (p_s)_t at which the mechanical twins appeared in the specimen. This indicates that the macroscopic plastic strain begins to occur in the specimen at the pressure of (p_s)_m. ( 5 ) The decrease in the yield stress due to shock loading was considerably larger than the decrease in the cases of pressurizing and temper rolling.
- 一般社団法人日本機械学会の論文
- 1992-06-25
著者
-
藤田 昌大
熊本大学工学部知能生産システム工学科
-
福田 泉
八代工業高等専門学校機械電気工学科
-
藤田 昌大
熊本大学工学部応用力学教室
-
大森 正信
広島国際学院大学工学部
-
大森 正信
広島大学工学部
-
福田 泉
八代工業高等専門学校
関連論文
- 4045 AZ31Bマグネシウム合金円筒管の塑性座屈挙動(S19-2 マグネシウム合金の強度,S19 高機能マグネシウム合金の材料強度特性)
- AZ31マグネシウム合金円管の塑性座屈強度に及ぼすショットピーニングの影響
- エマルション爆薬の爆轟特性について
- 水中爆轟現象の光学的観測について
- 爆薬を用いたBNの直接相転換に関する研究(第2報) : ロールフィルム法の提案と評価
- 爆薬を用いたBNの直接相転換に関する研究(第1報) : 斜め爆轟波を利用した衝撃合成装置
- 収束された水中衝撃波を利用した粉末衝撃固化装置の特性 : 第2報,磁性粉末の状態式と衝撃圧縮過程の数値解析(流体工学,流体機械)
- 高エネルギー速度成形法によって作製した不銹鋼金属床義歯の 1 例
- アルミニウム合金と鉄基焼結材のねじりにおける破断延性増加に及ぼす静水圧応力の影響
- 109 工業高専専攻科における技術倫理教育の試み(1)(技術者教育認定関連III,第28セッション)