TiN被覆極薄珪素鋼板のトロイダル鉄芯の鉄損と曲げによる磁区構造の観察

概要

論文の詳細を見る
In order to clarify the difference of iron loss of single sheet and toroidal core and domain structure of TiN-coated very thin silicon steel sheets, TiN coating by the hollow cathode discharge (HCD) method was performed on polished very thin (0.10mm) silicon steel sheets. Iron loss of single sheets and toroidal cores after domain refinig was measured. Also, domain structures of (011)[100] single crystals of silicon steel, which were chemical polished, TiN-coated and then domain refined by scribing with a knife at 4mm widths perpendicular to the rolling direction, were observed by electron microscopy under (a) straight, (b) convex and (c) concave states. 0.10mm TiN-coated very thin silicon steel showed ultra-low iron loss of W_<13/50>=0.12W/kg with a single sheet measurement after the domain refining, whreas similar iron loss with a toroidal core showed minimun value of W_<13/50>=0.12W/kg after 700℃ annealing, being good value of building factor (B.F.) of 1.0. The domain structures with (a) straight state obtained by TiN coating and inducement of a small local strain by scribing produced a drastic domain refinement, whereas that with (b) convex and (c) concave states showed further domain refinement. Also, the domain structure of (c) concave state could be observed after annealing above 873K.
社団法人日本鉄鋼協会の論文