Chemical State of Chromium in CaO-SiO_2 Base Oxides Annealed under Different Conditions
スポンサーリンク
概要
- 論文の詳細を見る
In order to understand the formation mechanism of Cr(VI) in chromium-containing steel slag, X-ray diffractiometry (XRD), X-ray absorption spectroscopy (XAS) in the region of X-ray absorption near edge structure (XANES), and X-ray photoelectron spectroscopy (XPS) measurements were performed for analyzing the chromium contained in the model slag of CaO–SiO2 base. The model slag was annealed under different temperatures and atmospheres to change the chemical state of chromium. XRD results showed that a diffraction peak that can be assigned to CaCrO4 comprising of Cr(VI) was detected in the model–slag sample annealed under a high partial pressure of oxygen (air). XANES results showed that the Cr(VI) concentration in the slag increased by annealing under a high partial pressure of oxygen, while it was very low in the slag sample annealed under a low partial pressure of oxygen. The XANES results were consistent with the XRD results. The formation conditions of Cr(VI) were discussed on the basis of the thermodynamic characteristics of a Ca–Cr–O system. The XPS results for the slag surface were dependent on the leaching tests performed on the slag, while the XANES results were insensitive to the leaching tests. This indicates that Cr(VI) dissolved from only a surface layer of the model slag. The chromium that dissolved from the slag in an aqueous solution by the leaching test was also analyzed and was found to be in the form of Cr(VI); further, its concentration depended on the annealing conditions of the slag.
- 社団法人 日本鉄鋼協会の論文
- 2008-10-15
著者
-
Maruoka Nobuhiro
Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
SHIBATA Hiroyuki
Institute of Multidisciplinary Research for Advanced Materials (IMRAM), Tohoku University
-
SUZUKI SHIGERU
Institute of Gastroenterology, Tokyo Women's Medical University
-
SHINODA Kozo
Institute for Advanced Materials Processing (SOZAIKEN), Tohoku University
-
Shibata Hiroyuki
Institute For Chemical Research Kyoto University
-
Maruoka Nobuhiro
Institute Of Multidisciplinary Research For Advanced Materials Tohoku University
-
Shibata Hiroyuki
Inst. Of Multidisciplinary Res. For Advanced Materials Tohoku Univ.
-
Kitamura Shinya
Institute Of Multidisciplinary Research For Advanced Materials Tohoku University
-
HATAKEDA Hirotaka
Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
Hatakeda Hirotaka
Institute Of Multidisciplinary Research For Advanced Materials Tohoku University
-
Shibata Hiroyuki
Institute For Advanced Materials Processing Tohoku University
-
Suzuki Shigeru
Institute For Advanced Materials Processing Tohoku University
関連論文
- Development of PCM Reactor for Methane Steam Reforming
- Atomic-scale Structure of Ferric Oxyhydroxide Formed from Fe-Si Alloy in Aqueous Solutions Containing Different Salts
- High Thermal Conductivity of Gallium Nitride (GaN) Crystals Grown by HVPE Process
- Thermal and Optical Properties of Yb^-Doped Y_2O_3 Single Crystal Grown by the Micro-Pulling-Down Method
- Evaluation of Bubble Eye Area to Improve Gas/Liquid Reaction Rates at Bath Surfaces
- LONG-TERM FOLLOW UP OF GASTRIC ANTRAL VASCULAR ECTASIA TREATED BY ARGON PLASMA COAGULATION
- High Temperature X-Ray Diffraction Study of Melt Structure of Silicon
- Electrical Resistivity Measurements of Pd_Cu_Ni_P_ Alloy in Supercooled Liquid and Liquid State
- Thermal Diffusivities and Conductivities of Molten Germanium and Silicon
- Measurement of Thermal Diffusivity of Steels at Elevated Temperature by a Laser Flash Method
- Reduction of Copper Ions in Green Rust Suspension and Oxidation of Green Rust Containing Metallic Copper
- Characteristic Behavior of Nickel Ions during Transformation of Green Rust to Ferric Oxyhydroxides in Aqueous Solution
- A New Method for Describing the Atomic-scale Structure of Rusts Formed on the Iron Based Alloy Surfaces
- Applicability of Platinum and Molybdenum Coatings for Measuring Thermal Diffusivity of Transparent Glass Specimens by the Laser Flash Method at High Temperatures
- Atomic-Scale Structure and Morphology of Ferric Oxyhydroxides Formed by Corrosion of an Iron-Silicon Alloy
- In-situ X-ray Diffraction of Corrosion Products Formed on Iron Surfaces
- Effect of Silicate Ions on Conversion of Ferric Hydroxide to β-FeOOH and α-Fe_2O_3
- A Feasible SIMS Study for Characterizing Ferric Oxyhydroxides Formed on the Iron Surface Using Deuterium
- Characterization of Oxidation of Green Rust (Cl^-) Containing Copper in Aqueous Solution
- Characterization of Reaction of Green Rust with Foreign Ions using X-ray Absorption Fine Structure
- Natural Antioxidant, Chlorogenic Acid, Protects Against DNA Breakage Caused by Monochloramine
- In-situ Observation of Intragranular Ferrite Nucleation at Oxide Particles
- Inhibition of Conversion Process from Fe(OH)_3 to β-FeOOH and α-Fe_2O_3 by the Addition of Silicate Ions
- Influence of Sulfate Ions on Conversion of Fe(OH)_3 Gel to β-FeOOH and α-Fe_2O_3
- Structural Characterization of Stress-Induced Martensitic Transformation in a Polycrystalline Austenitic Fe-Mn-Si-Cr Alloy
- X線異常散乱法を応用したZnFe2O4およびZnFe2O4-Fe3O4固溶体の陽イオン分布の決定〔英文〕
- Molecular Properties and Enhancement of Thermostability by Random Mutagenesis of Glutamate Dehydrogenase from Bacillus subtilis
- 2-III-22 Intermolecular dimmer structure of Euglena ascorbate peroxidase
- Functional Characterization of D-Galacturonic Acid Reductase, a Key Enzyme of the Ascorbate Biosynthesis Pathway, from Euglena gracilis
- Characterization of Protein Phosphatase 2A Acting on Phosphorylated Plasma Membrane Aquaporin of Tulip Petals
- Phosphorylation of Plasma Membrane Aquaporin Regulates Temperature-Dependent Opening of Tulip Petals
- Generation of Reactive Oxygen Species from Hinokitiol under Near-UV Irradiation(Analytical Chemistry)
- Molecular Properties and Activity of Amino-Terminal Truncated Forms of Lipase Activator Protein
- Calcium Ion-Dependent Reactivation of a Pseudomonas Lipase by Its Specific Modulating Protein, LipB^1
- Synthesis of Niobium Carbides from Ferroniobium by Mechanochemical Method
- Analysis of Dephosphorization Reaction Using a Simulation Model of Hot Metal Dephosphorization by Multiphase Slag
- Clinicopathologic evaluation of the trend toward histologically poor differentiation with submucosal invasion in superficial early colorectal adenocarcinomas
- Modeling the Behavior of Al_2O_3 Inclusions during the Dendritic Solidification of Steel
- Effect of Bottom Bubbling Conditions on Surface Reaction Rate in Oxygen-Water System
- Behavior of Cobalt in Iron- and Steel-making Processes
- Coprecipitation of Large Scorodite Particles from Aqueous Fe(II) and As(V) Solution by Oxygen Injection
- Distribution of P_2O_5 between Solid Dicalcium Silicate and Liquid Phases in CaO-SiO_2-Fe_2O_3 System
- Mass Transfer of P_2O_5 between Liquid Slag and Solid Solution of 2CaO・SiO_2 and 3CaO・P_2O_5
- Characteristic Structural Changes in Stress-Induced Martensitic Transformation and Reverse Transformation of a Polycrystalline Fe-Mn-Si Alloy
- Characterization of Different Solid Particles Transformed from Green Rust in Aqueous Solution-Using XRD, Mossbauer Spectroscopy, and XANES
- Analysis of Iron Oxyhydroxides and Oxides Converted from Green Rust in Aqueous Solution
- Surface Segregation of Chromium in a Copper-Chromium Alloy and its Effect on Formation of a Native Oxide Layer
- Surface Layer Formed by Selective Oxidation in High-Purity Copper-Titanium Binary Alloys
- Tungsten Extraction from Scheelite by means of Mechanochemistry and Heating
- Origin of Heat Transfer Anomaly and Solidifying Shell Deformation of Peritectic Steels in Continuous Casting
- Recovery of Hot Ductility by Improving Thermal Pattern of Continuously Cast Low Carbon and Ultra Low Carbon Steel Slabs for Hot Direct Rolling
- Distribution of P_2O_5 between Solid Solution of 2CaO・SiO_2-3CaO・P_2O_5 and Liquid Phase
- Precipitation Behavior of Copper, Tin and Manganese Sulfide at High Temperature in Fe-10%Cu-0.5%Sn Alloys
- Cysteine Uptake for Accumulation of Glutathione by the Cyanobacterium Synechocystis strain PCC 6803
- Repraesentins D, E and F, New Plant Growth Promoters from Lactarius repraesentaneus
- Anti-inflammatory Cyathane Diterpenoids from Sarcodon scabrosus
- New Plant Growth Promoters, Repraesentins A, B and C, from Lactarius repraesentaneus(Organic Chemistry)
- Hydroxyl Radical Generation Depending on O_2 or H_2O by a Photocatalyzed Reaction in an Aqueous Suspension of Titanium Dioxide
- Determination of Free Energy of δ-Ferrite/γ-Austenite Interphase Boundary of Low Carbon Steels by In-situ Observation
- In-situ Observation of Engulfment and Pushing of Nonmetallic Inclusions in Steel Melt by Advancing Melt/Solid Interface
- Characteristics of Agglomeration of Various Inclusion Particles on Molten Steel Surface
- "In-situ"Observation of Collision, Agglomeration and Cluster Formation of Alumina Inclusion Particles on Steel Melts
- Characterization of Four Plasma Membrane Aquaporins in Tulip Petals : A Putative Homolog is Regulated by Phosphorylation
- Cloning, Biochemical and Phylogenetic Characterizations of γ-Glutamylcysteine Synthetase from Anabaena sp. PCC 7120
- Cloning,Structural Analysis and Expression of the Gene Encoding Aspartate Aminotransferase from the Thermophilic Cyanobacterium Phormidium lapideum
- Characterization of Aspartate Aminotransferase from the Cyanobacterium Phormidium lapideum(Biochemistry & Molecular Biology)
- Oxidation and Reduction of Nitrite Ion in the TiO_2 Photo-induced Catalytic Reaction
- Effect of Intracellular Glutathione on Heat-induced Cell Death in the Cyanobacterium, Synechocystis PCC 6803
- HEMODYNAMICS OF ESOPHAGEAL VARICES ON THREE-DIMENSIONAL ENDOSCOPIC ULTRASONOGRAPHY AND INDICATION OF ENDOSCOPIC VARICEAL LIGATION
- Characterization of Formation and Oxidation of Green Rust (Cl^-) Suspension
- Heat Transfer across Mold Flux Film in Mold during Initial Solidification in Continuous Casting of Steel
- Thermal Resistance at the Interface between Mold Flux Film and Mold for Continuous Casting of Steels
- Radiative Heat Transfer through Mold Flux Film during Initial Solidification in Continuous Casting of Steel
- Heat Transfer from Shell across Flux Film to Continuous Casting Mold
- Measurement of Optical Properties of Continuous Casting Mold Fluxes at Elevated Temperatures
- Thermal Resistance between Solidifying Steel Shell and Continuous Casting Mold with Intervening Flux Film
- Anomaly in Melting Behavior and Mechanical Properties of Carbon Steels Near Their Solidus Temperature
- "In-situ"Real Time Observation of Planar to Cellular and Cellular to Dendritic Transition of Crystals Growing in Fe-C Alloy Melts
- Chemical State of Iron of LiFePO_4 during Charge-Discharge Cycles Studied by In-Situ X-ray Absorption Spectroscopy
- Effects of cultivation conditions on the uptake of arsenite and arsenic chemical species accumulated by Pteris vittata in hydroponics(ENVIRONMENTAL BIOTECHNOLOGY)
- Chemical State of Chromium in CaO-SiO_2 Base Oxides Annealed under Different Conditions
- Angle Resolved XPS Study of Thin Oxide Layers Formed on the Surface of Iron-Chromium Binary Alloys Exposed to Air
- Distribution of Cobalt between MgO-Saturated FeO_x-MgO-CaO-SiO_2 Slag and Fe-Cu-Co Molten Alloy
- 1-III-3 Vitamin C Biosynthesis and Translocation in Tomato (Lycopersicum esculentum) Fruits
- Development of PCM Reactor for Methane Steam Reforming
- Glow Discharge Optical Emission Spectrometry on the Formation of Thin Oxide Layers on the Iron Binary Alloy Surface
- A New Method for Cleaning the Surface of Ultra High-Purity Iron by High-Purity Ozone Exposure and UV Irradiation
- Influence of Bottom Bubbling Condition on Metal Emulsion Formation in Lead-Salt System
- SIMS/XPS Studies of Surface Layer Formed in Fe-Si-Mn Alloys by Oxygen Penetration
- SAXS and XAFS Characterization of Precipitates in a High-Performance Cu-Ni-Si Alloy
- Degree of Undercooling and Contact Angle of Pure Iron at 1933K on Single-crystal Al_2O_3, MgO, and MgAl_2O_4 under Argon Atmosphere with Controlled Oxygen Partial Pressure
- Evaluation of Bubble Eye Area to Improve Gas/Liquid Reaction Rates at Bath Surfaces
- Expression Analysis of the VTC2 and VTC5 Genes Encoding GDP-L-Galactose Phosphorylase, an Enzyme Involved in Ascorbate Biosynthesis, in Arabidopsis thaliana
- XPS Study of the Effect of Ar-Ion Bombardment and Aging on Surface Properties of Superionic Conducting Glass(CuI)_(Cu_2O)_(MoO_3)_
- A Non-NadB Type L-Aspartate Dehydrogenase from Ralstonia eutropha Strain JMP134 : Molecular Characterization and Physiological Functions
- Expression Analysis of the VTC2 and VTC5 Genes Encoding GDP-L-Galactose Phosphorylase, an Enzyme Involved in Ascorbate Biosynthesis, in Arabidopsis thaliana
- Synthesis of Ni Carbide Nanoparticles with Ni_3C-Type Structure in Polyol Solution Containing Dispersant
- Synthesis of Magnetite Particles by Oxidation of Hydroxyl-chloride Green Rust Suspension under Controlled Conditions
- Influence of Bottom Bubbling Rate on Formation of Metal Emulsion in Al-Cu Alloy and Molten Salt System
- Characterization of Selective Oxidation of Manganese in Surface Layers of Fe–Mn Alloys by Different Analytical Methods