Properties of a gypsum-bonded magnesia investment using a K_2SO_4 solution for titanium casting
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of the study was to investigate the effects of a K2SO4 solution on the improvement of the properties of an experimental magnesia-based gypsum-bonded investment.The characteristics of the experimental investment with different ratios of a K2SO4solution were as follows: setting time ranged from 34 to 152 minutes, green and fired compressive strengths were approximately 2.15 to 5.81 MPa and 1.63 to 2.45 MPa, respectively; thermal expansion was 0.38 to 0.47% at 700°C, which did not show any significant differences due to the concentration of the K2SO4 solution. Titanium casting could be obtained using the experimental investment mixed with a 1% K2SO4 solution, and the reaction layer thickness of the casting was less than 200 μm. The results suggest that the experimental investment mixed with 1% K2SO4 showed acceptable physical properties and casting characteristics for titaniumcasting.
- 日本歯科理工学会の論文
- 2009-05-01
著者
-
TAMAKI Yukimichi
Department of Oral Biomaterials and Technology, School of Dentistry, Showa University
-
MIYAZAKI Takashi
Department of Oral Biomaterials and Technology, School of Dentistry, Showa University
-
TAKAHASHI Hidekazu
Advanced Biomaterials, Graduate School, Tokyo Medical and Dental University
-
Iwasaki Naohiko
Advanced Biomaterials, Graduate School of Medical and Dentistry, Tokyo Medical and Dental Univ.
-
Takahashi Hidekazu
東京医科歯科大学 医歯学総合研究科包括診療歯科学講座総合診療歯科学
-
Takahashi Hidekazu
Tokyo Medical And Dental Univ. Tokyo Jpn
-
Reza Fazal
Advanced Biomaterials Department Of Restorative Sciences Division Of Oral Health Sciences Graduate S
-
Miyazaki Takashi
Department Of Oral Biomaterials & Technology Showa University School Of Dentistry
-
Miyazaki Takashi
Department Of Oral Biomaterials And Technology Showa University School Of Dentistry
-
Iwasaki Naohiko
Advanced Biomaterials Department Of Restorative Sciences Division Of Oral Health Sciences Graduate S
-
Iwasaki Naohiko
Advanced Biomaterials Graduate School Of Medical And Dentistry Tokyo Medical And Dental Univ.
-
Takahashi Hidekazu
Advanced Biomaterials Department Of Restorative Sciences Division Of Oral Health Sciences Graduate S
-
Miyazaki Takashi
Showa Univ. School Of Dentistry Tokyo Jpn
-
Miyazaki Takashi
昭和大学 歯学部
-
Masuda T
Department Of Oral Biomaterials & Technology Showa University School Of Dentistry
-
Miyazaki Takashi
Department Of Endocrinology And Metabolism Division Of Molecular Adaptation Research Institute Of En
-
Tamaki Yukimichi
Showa Univ. School Of Dentistry Tokyo Jpn
-
Tamaki Yukimichi
Department Of Oral Biomaterials & Technology Showa University School Of Dentistry
-
Takahashi Hidekazu
Advanced Biomaterials Graduate School Of Medical And Dentistry Tokyo Medical And Dental Univ.
-
Takahashi Hidekazu
Advanced Biomaterials Department Of Restorative Sciences Tokyo Medical And Dental University
-
Takahashi Hidekazu
Oral Biomaterials Engineering Department Of Oral Materials Sciences And Technology Course Of Oral He
-
Miyazaki Takashi
Department Of Animal Science Faculty Of Bioresources Mie University
-
Takahashi Hidekazu
Advanced Biomaterials Department Of Restorative Science Division Of Oral Health Science Graduate Sch
-
Takahashi Hidekazu
Advanced Biomaterials Department Of Restorative Sciences Division Of Oral Health Sciences Graduate S
-
Iwasaki Naohiko
Oral Biomaterials Engineering Course Of Oral Health Engineering School Of Oral Health Care Sciences
関連論文
- Radiofrequency Energy Induced Ventricular Fibrillation in a Case of Idiopathic Premature Ventricular Contraction Originating from the Left Ventricular Papillary Muscle
- Combination treatment of tribochemical treatment and phosphoric acid ester monomer of zirconia ceramics enhances the bonding durability of resin-based luting cements
- Effects of Silane Coupling Agent Amount on Mechanical Properties and Hydrolytic Durability of Composite Resin After Hot Water Storage
- An evaluation of the bending properties of glass fiber reinforced plastic post materials by a cantilever test
- Effect of filler type and polishing on the discoloration of composite resin artificial teeth
- MPN-PCR法により測定した市販魚介類中の腸炎ビブリオおよび耐熱性溶血毒遺伝子陽性菌数
- P-64 Effect of sizes and materials on diametral tensile strength
- P-63 Mechanical properties of enamel resin of veneering composite resin systems
- Effects of plasma treatment on the shear bond strength between fiber-reinforced composite posts and resin composite for core build-up
- Combination treatment of tribochemical treatment and phosphoric acid ester monomer of zirconia ceramics enhances the bonding durability of resin-based luting cements