高磁束密度Fe基アモルファス軟磁性粉末および成形磁心の特性
スポンサーリンク
概要
- 論文の詳細を見る
Fe-based amorphous powders with high magnetic flux density were fabricated in an extremely high cooling rate of over 106 K/s by SWAP. The composition of the alloys studied were Fex(SiyB1-y)98-xC2 {x=73-85 (at%), y=0.2-0.9 (at%)}. The saturation flux density Bs increased with increasing iron content. For Fe83(Si0.3B0.7)15C2, the Bs value was 1.64 T, which is 31 % higher than that of our previously developed (Fe0.97Cr0.03)76(Si0.5B0.5)22C2 alloy. Furthermore, the Fe81(Si0.3B0.7)17C2 powder core exhibited superior magnetic properties compared with our previously developed Fe76 system powder core. The core loss at 100 kHz for Bm=0.1 T was 450 kW/m3. This value was comparable to that of Fe76 system powder core with a lower flux density.
- 社団法人粉体粉末冶金協会の論文
- 2009-09-15
著者
-
石山 和志
東北大学電気通信研究所
-
前田 優
エプソンアトミックス(株)
-
荒井 賢一
東北大学電気通信研究所
-
八木 正昭
崇城大学
-
荒井 賢一
東北大通研
-
大塚 勇
エプソンアトミックス(株)
-
八木 正昭
崇城大学エネルギーエレクトロニクス研究所
-
荒井 賢一
東北大学
関連論文
- Stepped-GMI 素子の素子形状とインピーダンス特性の関係
- 低温フェライトめっき技術の磁気マイクロマシンへの応用
- 発熱素子を組み込んだ磁気マイクロマシンの試作 : 生体磁気
- LC共振を利用した高感度薄膜磁気センサの可能性 (センサ)
- 細径アクチュエータ用能動屈曲機構の開発
- 卓越技術データベースの構築と発信 : 愛称 : 電気のデジタル博物館
- 回転磁界を用いた2個の磁気微粒子の分離に関する基礎検討
- 高周波キャリア型薄膜磁界センサによる心磁界計測の試み
- ワイヤレス磁気マーカの位置検出システムにおける位置精度向上の検討
- 位置検出システムのコイル配置と検出精度に関する検討