Reinforcement of carbonate apatite bone substitutes with carbonate apatite by Ca salt introduction
スポンサーリンク
概要
- 論文の詳細を見る
Reinforcement of carbonate apatite (CO3Ap) block with CO3Ap was studied to increase the mechanical strength of CO3Ap block and widen applicable clinical fields. First, calcium salt was introduced to the micropores of CO3Ap block. Then, calcium salt was carbonated to form calcite inside the micropores of CO3Ap block by exposing CO3Ap block to carbon dioxide at the second step. On the third step, the CO3Ap block was immersed in Na2HPO4 aqueous solution. In this process, calcite inside the micropores of CO3Ap block transformed to CO3Ap based on the dissolution–precipitation reaction, and the newly formed CO3Ap crystals entangled not only along the newly formed CO3Ap but also on CO3Ap crystals of the existing CO3Ap block. As a result of bonding between newly formed CO3Ap and the existing CO3Ap block, mechanical strength of the CO3Ap block increased approximately 1.5 times higher when compared to that before the treatment.
著者
-
MARUTA Michito
Department of Biomaterials, Faculty of Dental Science, Kyushu University
-
Tsuru Kanji
Department of Biomaterials, Faculty of Dental Science, Kyushu University
-
KAWACHI Giichiro
Department of Biomaterials, Faculty of Dental Science, Kyushu University
-
Tsuru Kanji
Department Of Biomaterials Faculty Of Dental Science Kyushu University
-
Ishikawa Kunio
Department Of Biomaterials
-
Maruta Michito
Department Of Biomaterials Faculty Of Dental Science Kyushu University
-
Kawachi Giichiro
Department Of Biomaterials Faculty Of Dental Science Kyushu University
-
MATSUMOTO Kanako
Department of Biomaterials, Faculty of Dental Science, Kyushu University
-
MATSUYA Sigeki
Section of Bioengineering, Department of Dental Engineering, Fukuoka Dental College
-
TAKAHASHI Ichiro
Section of Orthodontics, Division of Oral Health, Growth and Development, Faculty of Dental Science,
-
Ishikawa Kunio
Department of Applied Chemistry, Faculty of Engineering, Osaka Univeristy
関連論文
- Protein adsorption on needle-shaped hydroxyapatite prepared by hydrothermal treatment of mixture composed of CaHPO_4・2H_2O and β-Ca_3(PO_4)_2
- Effects of sintering temperature on physical and compositional properties of α-tricalcium phosphate foam
- Enhancement of apatite-forming ability of parallely aligned Ti-substrates with optimum gaps by autoclaving
- Fabrication of low crystalline B-type carbonate apatite block from low crystalline calcite block
- Effects of liquid phase on basic properties of α-tricalcium phosphate-based apatite cement
- Fabrication of carbonate apatite block based on internal dissolution-precipitation reaction of dicalcium phosphate and calcium carbonate
- Fabrication of B-type carbonate apatite blocks by the phosphorization of free-molding gypsum-calcite composite
- Fabrication of Si-substituted hydroxyapatite foam using calcium silicates( Ceramics for Biomedical Applications in Asian Countries)
- Effects of tricalcium silicate addition on basic properties of α-tricalcium phosphate cement( Ceramics for Biomedical Applications in Asian Countries)
- Effects of thermal treatment on injectability and basic properties of apatite cement containing spherical tetracalcium phosphate made with plasma melting method( Ceramics for Biomedical Applications in Asian Countries)
- Comparison of the Effects of Added α- and β- Tricalcium Phosphate on the Basic Properties of Apatite Cement
- Fabrication of Biporous Low-crystalline Apatite Based on Mannitol Dissolution from Apatite Cement
- Fabrication of Hydroxyapatite Block from Gypsum Block Based on (NH_4)_2HPO_4 Treatment
- The Effects of Initial Hemostatic Period on the Mechanical Strength and Transformation of Apatite Cement
- Biopex^[○!R] Acquires Anti-washout Properties by Adding Sodium Alginate into its Liquid Phase
- Effects of Sintering Temperature Over 1,300℃ on the Physical and Compositional Properties of Porous Hydroxyapatite Foam
- Effects of Polysiloxane Coating of NaF on the Release Profile of Fluoride Ion from Bis-GMA/TEGDMA Resin Containing NaF
- Fabrication of low-crystalline carbonate apatite foam bone replacement based on phase transformation of calcite foam
- Development of Calcium Phosphate Cement for Rapid Crystallization to Apatite
- Preparation of osteocompatible Si(IV)-enriched chitosan–silicate hybrids
- Corrosion Behavior of Pure Titanium and Titanium Alloys in Various Concentrations of Acidulated Phosphate Fluoride (APF) Solutions
- Structure and morphology of aminopropyltriethoxysilane-modified TiO_2 nano-particles derived from sol-gel processing of tetraethylorthotitanate
- Novel One-pot Sol-Gel Preparation of Amino-functionalized Silica Nanoparticles
- Adhesion of Restorative Resin to Teeth: Effects of Functional Groups of Dentin Primer to Collagen
- Formation of needle-like hydroxyapatite by hydrothermal treatment of CaHPO_4・2H_2O combined with β-Ca_3(PO_4)_2
- Induced deposition of bone-like hydroxyapatite on thermally oxidized titanium substrates using a spatial gap in a solution that mimics a body fluid
- Hybridization of silver nanoparticles on hydroxyapatite in an aqueous solution(Aqueous Solution Science for Ceramic Processing II)
- Surface Topography Designed to Provide Osteoconductivity to Titanium after Thermal Oxidation
- Formation of hydroxyapatite on ceramics consisting of tricalcium phosphate in a simulated body fluid( Ceramics for Biomedical Applications in Asian Countries)
- Synthesis of ceramics in MO_-SiO_2 systems through sol-gel processing under coexistence of polyethylene glycol and in vitro evaluation of their bioactivity( Ceramics for Biomedical Applications in Asian Countries)
- Preparation of hydroxyapatite porous ceramics with different porous structures using a hydrothermal treatment with different aqueous solutions( Ceramics for Biomedical Applications in Asian Countries)
- Effects of added mannitol on the setting reaction and mechanical strength of apatite cement
- Effects of Calcium Phosphate Precipitation Method on Acid Resistance to Apatite Powder and Bovine Tooth
- Comparison of the Occluding Ability of Dentinal Tubules with Different Morphology between Calcium Phosphate Precipitation Method and Potassium Oxalate Treatment
- The Development of Ti Alloys for Dental Implant with High Corrosion Resistance and Mechanical Strength
- Initial Evaluation of a Ceramic Form as a Reconstructive Material for Bone Defects
- Effect of Carboxyl Group in O-Methacryloyl-N-Acyl Tyrosines on Adhesiveness to Unteched Human Dentin
- Correlation of Dentin Bond Durability with Water Absorption of Bonding Layer
- Steric Effects of N-Acyl Group in O-Methacryloyl-N-Acyl Tyrosines on the Adhesiveness of Unetched Human Dentin
- Effect of Corrosion Behavior of Pure Titanium and Titanium Alloy on Fluoride Addition in Acidic Environment by Streptococcus mutans (Corrosion Behavior of Titanium by Fluoride and Streptococcus mutans)
- Effects of Added Sodium Alginate on Mechanical Strength of Apatite Cement
- Histological Evaluation of Apatite Cement Containing Atelocollagen
- Proliferation and Differentiation of Cultured MC3T3-E1 Osteoblasts on Surface-layer Modified Hydroxyapatite Ceramic with Acid and Heat Treatments
- Content and Release of Bisphenol A from Polycarbonate Dental Products
- Effects of Apatite Foam Combined with Platelet-rich Plasma on Regeneration of Bone Defects
- Fabrication of low-crystalline carbonate apatite foam bone replacement based on phase transformation of calcite foam
- Reinforcement of carbonate apatite bone substitutes with carbonate apatite by Ca salt introduction
- In vitro osteoconductivity evaluation of alumina treated hydrothermally in CaCl2 solution
- Enhancement of in vitro apatite-forming ability of thermally oxidized titanium surfaces by ultraviolet irradiation
- Hydrothermal calcium modification of 316L stainless steel and its apatite forming ability in simulated body fluid
- Fabrication of microporous calcite block from calcium hydroxide compact under carbon dioxide atmosphere at high temperature
- Fabrication of solid and hollow carbonate apatite microspheres as bone substitutes using calcite microspheres as a precursor
- Effect of precursor's solubility on the mechanical property of hydroxyapatite formed by dissolution-precipitation reaction of tricalcium phosphate
- Influence of PLGA concentrations on structural and mechanical properties of carbonate apatite foam
- Redox reactions of cis-dialkylcobalt(III) complexes with benzyl and allyl bromides, induced by thermal cleavage of the cobalt-carbon bond.