Effect of Corrosion Behavior of Pure Titanium and Titanium Alloy on Fluoride Addition in Acidic Environment by Streptococcus mutans (Corrosion Behavior of Titanium by Fluoride and Streptococcus mutans)
スポンサーリンク
概要
- 論文の詳細を見る
Purpose: As for commercially pure titanium (CP-Ti) and titanium alloys (Ti-6Al-4V, Ti-6Al-7Nb), when fluoride exists in an acidic environment, it is known to corrode from recent research. However, it is also reported that the corrosion resistance improves when small amount of platinum is added to pure titanium. The purpose of this study is to examine the corrosion behavior of CP-Ti, Ti-6Al-4V, Ti-6Al-7Nb, and high corrosion Ti-0.5Pt alloy when a fluoride added to the acidic environment produced by streptococcus mutans.Methods: The specimen (CP-Ti, Ti-6Al-4V, Ti-6Al-7Nb, and experimentally produced Ti-0.5Pt alloy) were polished like a mirror. Streptococcus mutans was cultured for 24 hours with brain heart infusion (BHI) medium adding sucrose on the specimen, and then 1000ppm fluoride solution of same medium volume was added (that is, fluoride concentration becomes 500 ppm). After 10 min, all the solutions were removed and new culture for 24 hours started again. These cycles of 3, 5, 7, and 10 times were repeated and the surfaces of the specimens were observed by scanning electron microscope (SEM).Results: The CP-Ti and Ti-6Al-4V, Ti-6AL-7Nb alloys were observed the typically metallographical structure by adding fluoride solution repeatedly. The surface of Ti-0.5Pt alloy was no change by adding fluoride solution.Conclusion: When a fluoride with less than 500 ppm concentration was added to the acid biofilm which was produced by Streptococcus mutans, as for CP-Ti, Ti-6Al-4V and Ti-6Al-7Nb alloys the possibility to corrode was suggested. The Ti-0.5Pt alloy had a high corrosion resistance in the same condition.
- 日本補綴歯科学会の論文
- 2008-01-01
著者
-
Ishikawa Kunio
Department Of Biomaterials Faculty Of Dental Science Kyushu University
-
Ishikawa Kunio
九州大学 歯学部口腔機能修復学講座
-
Nakagawa M
Department Of Biomaterials Faculty Of Dental Science Kyushu University
-
TERADA Yoshihiro
Department of Fixed Prosthodontics, Faculty of Dental Science, Kyushu University
-
NAKAGAWA Masaharu
Department of Biomaterials Faculty of Dental Science, Kyushu University
-
Tsukiyama Yoshihiro
Div. Of Oral Rehabilitation Fac. Of Dental Sci. Kyushu Univ.
-
Terada Yoshihiro
Department Of Fixed Prosthodontics Faculty Of Dental Science Kyushu University
-
MATONO Yoshinari
Department of Biomaterials, Faculty of Dental Science, Kyushu University
-
Nakagawa Masaharu
Department Of Biomaterials Division Of Oral Rehabilitation Faculty Of Dental Science Kyushu Universi
-
Matono Yoshinari
Department Of Fixed Prosthodontics Division Of Oral Rehabilitation Faculty Of Dental Science Kyushu
-
Ishikawa Kunio
Department Of Biomaterials
-
Ishikawa Kunio
Section Of Biomaterials Department Of Oral Rehabilitation School Of Dentistry Kyushu University
-
Ishikawa Kunio
Department of Applied Chemistry, Faculty of Engineering, Osaka Univeristy
関連論文
- Effects of sintering temperature on physical and compositional properties of α-tricalcium phosphate foam
- Fabrication of low crystalline B-type carbonate apatite block from low crystalline calcite block
- Effects of liquid phase on basic properties of α-tricalcium phosphate-based apatite cement
- Fabrication of carbonate apatite block based on internal dissolution-precipitation reaction of dicalcium phosphate and calcium carbonate
- Fabrication of B-type carbonate apatite blocks by the phosphorization of free-molding gypsum-calcite composite
- Fabrication of Si-substituted hydroxyapatite foam using calcium silicates( Ceramics for Biomedical Applications in Asian Countries)
- Effects of tricalcium silicate addition on basic properties of α-tricalcium phosphate cement( Ceramics for Biomedical Applications in Asian Countries)
- Effects of thermal treatment on injectability and basic properties of apatite cement containing spherical tetracalcium phosphate made with plasma melting method( Ceramics for Biomedical Applications in Asian Countries)
- Comparison of the Effects of Added α- and β- Tricalcium Phosphate on the Basic Properties of Apatite Cement
- Fabrication of Biporous Low-crystalline Apatite Based on Mannitol Dissolution from Apatite Cement
- Fabrication of Hydroxyapatite Block from Gypsum Block Based on (NH_4)_2HPO_4 Treatment
- The Effects of Initial Hemostatic Period on the Mechanical Strength and Transformation of Apatite Cement
- Biopex^[○!R] Acquires Anti-washout Properties by Adding Sodium Alginate into its Liquid Phase
- Stress Analysis of All-on-4 System Using a 3-Dimensional Finite Element Method
- Effects of Sintering Temperature Over 1,300℃ on the Physical and Compositional Properties of Porous Hydroxyapatite Foam
- Three Dimensional Interconnected Pore Scaffold As Bone Defect Filler : The Effects of Sintering Temperatures on the Physical Properties of α-TCP
- πHydrogen Bond Between Dipeptide Side Chains as a Structural Essential for Chymotrypsin Inhibition
- Effects of Polysiloxane Coating of NaF on the Release Profile of Fluoride Ion from Bis-GMA/TEGDMA Resin Containing NaF
- Fabrication of low-crystalline carbonate apatite foam bone replacement based on phase transformation of calcite foam
- Development of Calcium Phosphate Cement for Rapid Crystallization to Apatite
- Corrosion Behavior of Pure Titanium and Titanium Alloys in Various Concentrations of Acidulated Phosphate Fluoride (APF) Solutions
- Effects of Alloying Additions on Thermal Conductivity of Ferritic Iron
- Adhesion of Restorative Resin to Teeth: Effects of Functional Groups of Dentin Primer to Collagen
- Effects of added mannitol on the setting reaction and mechanical strength of apatite cement
- Effects of Calcium Phosphate Precipitation Method on Acid Resistance to Apatite Powder and Bovine Tooth
- Comparison of the Occluding Ability of Dentinal Tubules with Different Morphology between Calcium Phosphate Precipitation Method and Potassium Oxalate Treatment
- The Development of Ti Alloys for Dental Implant with High Corrosion Resistance and Mechanical Strength
- Initial Evaluation of a Ceramic Form as a Reconstructive Material for Bone Defects
- Effect of Carboxyl Group in O-Methacryloyl-N-Acyl Tyrosines on Adhesiveness to Unteched Human Dentin
- Correlation of Dentin Bond Durability with Water Absorption of Bonding Layer
- Steric Effects of N-Acyl Group in O-Methacryloyl-N-Acyl Tyrosines on the Adhesiveness of Unetched Human Dentin
- Self-cleaning Ability of a Photocatalyst-containing Denture Base Material
- Up-regulation, Enhanced Maturation, and Secretion of Cathepsin E in Mouse Macrophages Treated with Interferon-γ or Lipopolysaccharide
- Effect of Corrosion Behavior of Pure Titanium and Titanium Alloy on Fluoride Addition in Acidic Environment by Streptococcus mutans (Corrosion Behavior of Titanium by Fluoride and Streptococcus mutans)
- Effects of Added Sodium Alginate on Mechanical Strength of Apatite Cement
- The Changes in the Immunocytochemical Localization of Cathepsin L and Type I Collagen in Rat Osteoclasts Treated with E-64
- Synthesis of ZnO Bicrystals Doped with Co or Mn and Their Electrical Properties
- Evaluation of Dislocation Density in a Mg-Al-Mn-Ca Alloy Determined by X-ray Diffractometry and Transmission Electron Microscopy
- Psuedo-binary Phase Diagram of AuCu-Sn
- Histological Evaluation of Apatite Cement Containing Atelocollagen
- Proliferation and Differentiation of Cultured MC3T3-E1 Osteoblasts on Surface-layer Modified Hydroxyapatite Ceramic with Acid and Heat Treatments
- Content and Release of Bisphenol A from Polycarbonate Dental Products
- Effects of Apatite Foam Combined with Platelet-rich Plasma on Regeneration of Bone Defects
- Fabrication of low-crystalline carbonate apatite foam bone replacement based on phase transformation of calcite foam
- Creep Behavior of Hypoeutectic Mg-Ca Binary Alloys
- Role of Eutectic Intermetallic Phase on Creep Strength in a Die-Cast Mg-Al-Ca Alloy : Evaluation by Internal Stress Measurement
- Internal Stress during Creep in a Die-Cast AM50 Magnesium Alloy at 473K
- Eutectic Phase Investigation in a Ca-added AM50 Magnesium Alloy Produced by Die Casting
- Reinforcement of carbonate apatite bone substitutes with carbonate apatite by Ca salt introduction
- Effect of Calcium Additions on Creep Properties of a Die-Cast AM50 Magnesium Alloy
- Creep Parameters in a Die-Cast Mg-Al-Ca Alloy
- In vitro osteoconductivity evaluation of alumina treated hydrothermally in CaCl2 solution
- Influence of Different Elastic Moduli of Dowel and Core on Stress Distribution in Root
- Effect of Hydrogenation on Zn0 Luminescence
- Effect of Prior Deformation on Creep Behavior of a Die-Cast Mg-Al-Ca Alloy
- Relationship between Minimum Creep Rate and Rupture Life for a Die-Cast Mg-Al-Mn Alloy
- Comparison of apatite-coated titanium prepared by blast coating and flame spray methods : Evaluation using simulated body fluid and initial histological study
- Hydrothermal calcium modification of 316L stainless steel and its apatite forming ability in simulated body fluid
- Assessment of Creep Rupture Life of Die-Cast Mg-Al-Mn Alloy
- Preparation of Sr-containing carbonate apatite as a bone substitute and its properties
- Fabrication of microporous calcite block from calcium hydroxide compact under carbon dioxide atmosphere at high temperature
- Fabrication of solid and hollow carbonate apatite microspheres as bone substitutes using calcite microspheres as a precursor
- HYDROTHERMAL ALTERATION AT THE DENBEKOBA DEPOSIT OF AMAKUSA POTTERY STONE
- Creep Properties of Binary Mg-Ca Cast Alloys at 473K
- Effect of precursor's solubility on the mechanical property of hydroxyapatite formed by dissolution-precipitation reaction of tricalcium phosphate
- SB-10-5(116) Change in Feature of Transient Creep with Decreasing Stress(Creep Deformation and Fracture of Superalloys)
- Influence of PLGA concentrations on structural and mechanical properties of carbonate apatite foam
- Redox reactions of cis-dialkylcobalt(III) complexes with benzyl and allyl bromides, induced by thermal cleavage of the cobalt-carbon bond.
- Field Trial with a Further Attenuated Live Measles Virus Vaccine