Influence of PLGA concentrations on structural and mechanical properties of carbonate apatite foam

スポンサーリンク

概要

• 論文の詳細を見る

• Reinforcement with bioresorbable polymer such as PLGA is one of the useful ways to improve the mechanical property of brittle carbonate apatite (CO3Ap) foam. In the present study, CO3Ap foam was reinforced with various concentrations of PLGA solution (5, 10, 15 and 20 wt%) using vacuum infiltration method and its influence on structure, porosity and mechanical property was investigated. It was found that the amount of PLGA inside the hollow space of the CO3Ap foam strut increased with the concentration of PLGA. Porosity likewise was significantly (p<0.05) reduced from 94% (CO3Ap foam without PLGA) down to 82% (CO3Ap foam reinforced with 20 wt% PLGA). Compressive strength of CO3Ap foam significantly (p<0.05) increased from 0.02 MPa (CO3Ap foam without PLGA) up to 1.5 MPa (CO3Ap foam reinforced with 20 wt% PLGA).

著者

• ISHIKAWA Kunio

  Department of Biomaterials, Faculty of Dental Science, Kyushu University

• Munar Melvin

  Department Of Biomaterials Faculty Of Dental Science Kyushu University

• Tsuru Kanji

  Department Of Biomaterials Faculty Of Dental Science Kyushu University

• Ishikawa Kunio

  Department of Applied Chemistry, Faculty of Engineering, Osaka Univeristy

• MUNAR Girlie

  Department of Biomaterials, Faculty of Dental Science, Kyushu University

関連論文

• Effects of sintering temperature on physical and compositional properties of α-tricalcium phosphate foam
• Enhancement of apatite-forming ability of parallely aligned Ti-substrates with optimum gaps by autoclaving
• Fabrication of low crystalline B-type carbonate apatite block from low crystalline calcite block
• Effects of liquid phase on basic properties of α-tricalcium phosphate-based apatite cement
• Fabrication of carbonate apatite block based on internal dissolution-precipitation reaction of dicalcium phosphate and calcium carbonate
• Fabrication of B-type carbonate apatite blocks by the phosphorization of free-molding gypsum-calcite composite
• Fabrication of Si-substituted hydroxyapatite foam using calcium silicates( Ceramics for Biomedical Applications in Asian Countries)
• Effects of tricalcium silicate addition on basic properties of α-tricalcium phosphate cement( Ceramics for Biomedical Applications in Asian Countries)
• Effects of thermal treatment on injectability and basic properties of apatite cement containing spherical tetracalcium phosphate made with plasma melting method( Ceramics for Biomedical Applications in Asian Countries)
• Comparison of the Effects of Added α- and β- Tricalcium Phosphate on the Basic Properties of Apatite Cement
• Fabrication of Biporous Low-crystalline Apatite Based on Mannitol Dissolution from Apatite Cement
• Fabrication of Hydroxyapatite Block from Gypsum Block Based on (NH_4)_2HPO_4 Treatment
• The Effects of Initial Hemostatic Period on the Mechanical Strength and Transformation of Apatite Cement
• Biopex^[○!R] Acquires Anti-washout Properties by Adding Sodium Alginate into its Liquid Phase
• Effects of Sintering Temperature Over 1,300℃ on the Physical and Compositional Properties of Porous Hydroxyapatite Foam
• Three Dimensional Interconnected Pore Scaffold As Bone Defect Filler : The Effects of Sintering Temperatures on the Physical Properties of α-TCP
• Effects of Polysiloxane Coating of NaF on the Release Profile of Fluoride Ion from Bis-GMA/TEGDMA Resin Containing NaF
• Fabrication of low-crystalline carbonate apatite foam bone replacement based on phase transformation of calcite foam
• Development of Calcium Phosphate Cement for Rapid Crystallization to Apatite
• Preparation of osteocompatible Si(IV)-enriched chitosan–silicate hybrids
• Corrosion Behavior of Pure Titanium and Titanium Alloys in Various Concentrations of Acidulated Phosphate Fluoride (APF) Solutions
• Structure and morphology of aminopropyltriethoxysilane-modified TiO_2 nano-particles derived from sol-gel processing of tetraethylorthotitanate
• Novel One-pot Sol-Gel Preparation of Amino-functionalized Silica Nanoparticles
• Adhesion of Restorative Resin to Teeth: Effects of Functional Groups of Dentin Primer to Collagen
• Induced deposition of bone-like hydroxyapatite on thermally oxidized titanium substrates using a spatial gap in a solution that mimics a body fluid
• Surface Topography Designed to Provide Osteoconductivity to Titanium after Thermal Oxidation
• Effects of Calcium Phosphate Precipitation Method on Acid Resistance to Apatite Powder and Bovine Tooth
• The Development of Ti Alloys for Dental Implant with High Corrosion Resistance and Mechanical Strength
• Initial Evaluation of a Ceramic Form as a Reconstructive Material for Bone Defects
• Effect of Carboxyl Group in O-Methacryloyl-N-Acyl Tyrosines on Adhesiveness to Unteched Human Dentin
• Correlation of Dentin Bond Durability with Water Absorption of Bonding Layer
• Steric Effects of N-Acyl Group in O-Methacryloyl-N-Acyl Tyrosines on the Adhesiveness of Unetched Human Dentin
• Effect of Corrosion Behavior of Pure Titanium and Titanium Alloy on Fluoride Addition in Acidic Environment by Streptococcus mutans (Corrosion Behavior of Titanium by Fluoride and Streptococcus mutans)
• Effects of Added Sodium Alginate on Mechanical Strength of Apatite Cement
• Histological Evaluation of Apatite Cement Containing Atelocollagen
• Content and Release of Bisphenol A from Polycarbonate Dental Products
• Effects of Apatite Foam Combined with Platelet-rich Plasma on Regeneration of Bone Defects
• Fabrication of low-crystalline carbonate apatite foam bone replacement based on phase transformation of calcite foam
• Reinforcement of carbonate apatite bone substitutes with carbonate apatite by Ca salt introduction
• In vitro osteoconductivity evaluation of alumina treated hydrothermally in CaCl2 solution
• Enhancement of in vitro apatite-forming ability of thermally oxidized titanium surfaces by ultraviolet irradiation
• Hydrothermal calcium modification of 316L stainless steel and its apatite forming ability in simulated body fluid
• Fabrication of microporous calcite block from calcium hydroxide compact under carbon dioxide atmosphere at high temperature
• Fabrication of solid and hollow carbonate apatite microspheres as bone substitutes using calcite microspheres as a precursor
• Effect of precursor's solubility on the mechanical property of hydroxyapatite formed by dissolution-precipitation reaction of tricalcium phosphate
• Influence of PLGA concentrations on structural and mechanical properties of carbonate apatite foam
• Redox reactions of cis-dialkylcobalt(III) complexes with benzyl and allyl bromides, induced by thermal cleavage of the cobalt-carbon bond.

もっと見る 閉じる

スポンサーリンク