Fabrication of Hydroxyapatite Block from Gypsum Block Based on (NH_4)_2HPO_4 Treatment

概要

論文の詳細を見る
The aim of this study was to evaluate the feasibility of fabricating low-crystalline, porous apatite block using set gypsum as a precursor based on the fact that apatite is thermodynamically more stable than gypsum. When the set gypsum was immersed in 1mol/L diammonium hydrogen phosphate aqueous solution at 100℃, it transformed to low-crystalline porous apatite retaining its original shape. The transformation reaction caused a release of sulfate ions due to an ion exchange with phosphate ions, thus leading to a decrease in the pH of the solution. Then, due to decreased pH, dicalcium phosphate anhydrous-which has similar thermodynamic stability at lower pH-was also produced as a by-product. Apatite formed in the present method was low-crystalline, porous B-type carbonate apatite that contained approximately 0.5 wt% CO_3, even though no carbonate sources-except carbon dioxide from air-were added to the reaction system. We concluded therefore that this is a useful bone filler fabrication method since B-type carbonate apatite is the biological apatite contained in bone.
日本歯科理工学会の論文