Effect of Fabricating Process on Notch Toughness of Shipbuilding Steel Plates (Report II) : Superposition of Welding on Cold Work and Its Effect on Brittle Fracture Strength
スポンサーリンク
概要
- 論文の詳細を見る
Welded sections of grade E high-tensile and mild steel plates are used at the ship rounded gunwales to serve as brittle crack arresters. It is said that welding lifting eyes, etc., to the gunwale should be avoided because the gunwale plating, being initially cold-bent, will be adversely affected by the welding, to the detriment of its brittle fracture strength. The authors carried out brittle fracture initiation and propagation arrest tests on cold-worked-and-bead-welded grade E high-tensile and mild steel test specimens to determine how the cold-working and welding would combine together to affect the brittle fracture strength of the grade E gunwale plating. The tests indicated that: (1) welding on 3〜5% cold-worked grade E high-tensile and mild steel plates would exert no adverse effects on the brittle fracture strengths of the plates ; (2) welding lifting eyes to the rounded gunwales of grade E steels would suggest nothing alarming from a practical standpoint.
- 大阪大学の論文
著者
-
Yajima Hiroshi
Nagasaki Technical Institute Mitsubishi Heavy Industries Ltd.
-
Kihara Hiroshi
Osaka University
-
Kitahara Hiroshi
Osaka University
-
Yajima Hiroshi
Nagasaki Inst. Of Ap. Sc.
-
SUHARA Jiro
Kyushu Univerity
-
KUROKAWA Tsuneo
Nagasaki University
-
KATAOKA Shigeo
Nagasaki University
-
FUKAE Tatsuro
Nagasaki Technical Institute, Mitsubishi Heavy Industries, Ltd.
-
Fukae Tatsuro
Nagasaki Technical Institute Mitsubishi Heavy Industries Ltd.
-
YAJIMA Hiroshi
Nagasaki Technical Institute, Mitsubishi Heavy Industries, Ltd.
関連論文
- Studies on Flux Action of Soldering (Report VII) : Flux Action of various Silver and Copper Salts on Ni and Fe plates
- Studies on Flux Action of Soldering (Report V) : Reaction of Flux and Wetting
- Studies on Flux Action of Soldering (Report IV) : Inorganic Metal Salts
- Studies on Flux Action of Soldering (Report III) : Organic Metal Salts
- Studies on Flux Action of Soldering (Report II) : Amine Hydrochloride
- Estimations of Some Unknown Viscosities and Self-diffusivities for Liquid Metals
- Trial Product of Dynamic Co-Axial Cylinder (DCC) Viscometer for Molten Metals, Slags and Salts to 1200℃
- A Phenomenological Theory of Viscosities of Liquids
- Evaluation Method of the Brittle Fracture Strength in Structurally Stress-Concentrated Regions
- 11. Evaluation Method of the Brittle Fracture Strength in Structurally Stress Concentrated Regions
- Recent Trend of Researches on Restraint Stresses and Strains for Weld Cracking
- An Approach to Viscosity Calculations of Molten Iron and Its Dilute Binary Alloys
- On the Fillet Weld Cracking of 50kg/mm^2 Grade High Strength Steels : On the Heel-Crack
- Effect of Fabricating Process on Notch Toughness of Shipbuilding Steel Plates (Report II) : Superposition of Welding on Cold Work and Its Effect on Brittle Fracture Strength
- 7. Effect of Line-Heating on Notch Toughness of 50 kg/mm^2-Class High-Tensile Steel Plates
- Effect of Fabricating Process on Notch Toughness of Shipbuilding Steel Plates (Report I) : Effect of Line-Heating on Notch Toughness of 50 kg/mm^2-Class High-Tensile Steel Plates
- Correlation of Fracture Toughness Determined by Spin Burst Testing and Deep Notch Test
- Varestraint Test for Hot Crack Susceptibility of HY-type High Strength Steels
- Effect of Structural Discontinuities of Welded Joints on Brittle Crack Propagation Behavior : Brittle Crack Arrest Design for Large Container Ships-3
- Development of Brittle Crack Arrest Toughness K_ Test Method : Brittle Crack Arrest Design for Large Container Ships-2
- Required Brittle Crack Arrest Toughness K_ Value with Actual Scale Model Tests : Brittle Crack Arrest Design for Large Container Ships-4
- Development of Guidelines on Brittle Crack Arrest Design : Brittle Crack Arrest Design for Large Container Ships-1
- 15. Analysis of Gas Concentration during Gas Purging in Oil Tanks of Tankers
- Thickness Effect on Brittle Fracture Toughness of Weld Metal of High Tensile Strength Steel
- 16. Study on Brittle Crack Propagation and Arrest Behavior in Plate and Beam Structures
- Study on Brittle Crack Arrester : Considerations on the Arrest of a Very Long Crack
- Improvement of fatigue properties by ultrafine grained microstructure in steel plate
- 13. Study on Brittle Crack Propagation and Arrest Behavior in Plate and Beam Structures (2nd Report) : Dynamic Fracture Toughness of Ship Hull Steels
- Experimental Study on Brittle Crack Propagation Behavior with Large Scale Structural Component Model Tests : Brittle Crack Arrest Design for Large Container Ships-5
- Thickness Effect on the Brittle Crack Arrest Toughness Value (K_) : Brittle Crack Arrest Design for Large Container Ships-6