Correlation of Fracture Toughness Determined by Spin Burst Testing and Deep Notch Test
スポンサーリンク
概要
- 論文の詳細を見る
For the estimation of the fracture toughness of the turbine generator rotor forgings by means of the fracture mechanics, the Spin burst testing which simulates the loading condition in the rotating rotor and the Deep Notch test which was proposed by H. Kihara and K. Ikeda to estimate the brittle fracture initiation characteristics were carried out. The obtained test results are as follows. 1) A good correlation of the fracture toughness determined by the Spin burst testing and the Deep Notch test was obtained. 2) The effect of the thickness on the fracture toughness of the turbine generator rotor forgings was recognized. 3) The dependency of the fracture foughness of the turbine generator rotor forgings upon the temperature was assumed the Arrhenius type dependency in the temperature range tested.
- 大阪大学の論文
著者
-
Kihara Hiroshi
Osaka University
-
MACHIDA Susumu
Faculty of Engineering, Chiba University
-
Machida Susumu
Faculty Of Engineering The University Of Tokyo
-
Machida Susumu
Faculty Of Engineering University Of Tokyo
-
KANAZAWA Takeshi
Faculty of Engineering, University of Tokyo
-
MIYATA Takashi
Faculty of Engineering, University of Tokyo
-
ARII Mitsuru
Heavy Apparatus Eng. Lab., Tokyo Shibaura Electric Co., Ltd.
-
MIZUTAME Morihiro
Heavy Apparatus Eng. Lab., Tokyo Shibaura Electric Co., Ltd.
-
YANUKI Tetsu
Heavy Apparatus Eng. Lab., Tokyo Shibaura Electric Co., Ltd.
-
Yanuki Tetsu
Heavy Apparatus Eng. Lab. Tokyo Shibaura Electric Co. Ltd.
-
Arii Mitsuru
Heavy Apparatus Eng. Lab. Tokyo Shibaura Electric Co. Ltd.
-
Kanazawa Takeshi
Faculty Of Engineering University Of Tokyo
-
Mizutame Morihiro
Heavy Apparatus Eng. Lab. Tokyo Shibaura Electric Co. Ltd.
-
Miyata Takashi
Faculty Of Engineering University Of Tokyo
-
Kanazawa Takeshi
Faculty Of Eng. University Of Tokyo
-
MIYATA Takashi
Faculty of Chemistry, Materials and Bioengineering, Kansai University
関連論文
- Natural Gas Decompression Behavior in High Pressure Pipelines
- Studies on Flux Action of Soldering (Report VII) : Flux Action of various Silver and Copper Salts on Ni and Fe plates
- Studies on Flux Action of Soldering (Report V) : Reaction of Flux and Wetting
- Studies on Flux Action of Soldering (Report IV) : Inorganic Metal Salts
- Studies on Flux Action of Soldering (Report III) : Organic Metal Salts
- Studies on Flux Action of Soldering (Report II) : Amine Hydrochloride
- Estimations of Some Unknown Viscosities and Self-diffusivities for Liquid Metals
- Trial Product of Dynamic Co-Axial Cylinder (DCC) Viscometer for Molten Metals, Slags and Salts to 1200℃
- A Phenomenological Theory of Viscosities of Liquids
- Prediction for Crack Propagation and Arrest of Shear Fracture in Ultra-high Pressure Natural Gas Pipelines
- Recent Trend of Researches on Restraint Stresses and Strains for Weld Cracking
- An Approach to Viscosity Calculations of Molten Iron and Its Dilute Binary Alloys
- On the Fillet Weld Cracking of 50kg/mm^2 Grade High Strength Steels : On the Heel-Crack
- Effect of Fabricating Process on Notch Toughness of Shipbuilding Steel Plates (Report II) : Superposition of Welding on Cold Work and Its Effect on Brittle Fracture Strength
- Effect of Fabricating Process on Notch Toughness of Shipbuilding Steel Plates (Report I) : Effect of Line-Heating on Notch Toughness of 50 kg/mm^2-Class High-Tensile Steel Plates
- Correlation of Fracture Toughness Determined by Spin Burst Testing and Deep Notch Test
- Varestraint Test for Hot Crack Susceptibility of HY-type High Strength Steels
- What is Maintenance Engineering?(Hull Maintenance Management Techniques, Technical Experience Necessary for Engineers Concerned and Its Importance, and Tasks for Training and Maintenance,Technical Reports on Inspection & Preventive Maintenance of Hull Str
- Study on Brittle Crack Arrester : Considerations on the Arrest of a Very Long Crack
- 7. Fracture Mechanics Analysis of Stiffener-Type Crack Arrester
- 5. On Brittle Fracture Test of Steel Plate
- Asymmetric Shrink Fit of a Cylindrical Shell
- A Study on the Propagation of a Brittle Fracture 3rd Report : Dynamical Stress and Speed of a Propagating Crack
- SPR Signals of Three-dimensional Antibody-immobilized Gel Layers Formed on Sensor Chips by Atom Transfer Radical Polymerization