Effect of Structural Discontinuities of Welded Joints on Brittle Crack Propagation Behavior : Brittle Crack Arrest Design for Large Container Ships-3
スポンサーリンク
概要
- 論文の詳細を見る
Brittle fractures of hull structures cause serious structural, fatal and environmental damage once they happens. Therefore, ships are basically designed and constructed so that a brittle crack does not occur. Further, if by chance a brittle crack occurs, it is essentially and extremely important that a backup brittle crack arresting function is provided to arrest its propagation and to ensure structural reliability. Either fillet welding or partial penetration welding is applied in cruciform joints comprising the strength deck and hatch side coaming in which extremely thick steel plates are used. In this research, model experiments were conducted supposing that a brittle crack that has undergone linear propagation in a weld in the hatch coaming extend into a cruciform joint of the hatch side coaming and strength deck, and the effect of structural discontinuities on brittle crack propagation behavior in the cruciform joint was investigated assuming the case in which the lower edge of the butt welding of the hatch side coaming is melted to the deck plate. This research was conducted by a research committee of the Nippon Kaiji Kyokai (ClassNK), and the results were summarized and incorporated in their "Guidelines on Brittle Crack Arrest Design." (Nippon Kaiji Kyokai, 2009)
著者
-
Yajima Hiroshi
Nagasaki Technical Institute Mitsubishi Heavy Industries Ltd.
-
Yajima Hiroshi
Nagasaki Inst. Of Ap. Sc.
-
YOSHINARI Hitoshi
National Research Institute for Metals
-
Yajima Hiroshi
Nagasaki Institute Of Applied Science
-
Inoue Takehiro
Nippon Steel Corporation
-
Aihara Shuji
The University of Tokyo
-
Hirota Kazuhiro
Mitsubishi Heavy Industries, Ltd.
-
Toyoda Masanobu
IHI Marine United Inc.
-
Kiyosue Takaaki
Kawasaki Heavy Industries, Ltd.
-
Handa Tsunehisa
JFE Steel Corporation
-
Kawabata Tomoya
Sumitomo Metal Industries, Ltd.
-
Tani Tokutaka
Kobe Steel, Ltd.
-
Tani Tokutaka
Kobe Steel Ltd.
-
Hirota Kazuhiro
Mitsubishi Heavy Industries Ltd.
-
Kawabata Tomoya
Sumitomo Metal Industries Ltd.
-
Kiyosue Takaaki
Kawasaki Heavy Industries Ltd.
-
Yoshinari Hitoshi
National Maritime Research Institute
関連論文
- Evaluation Method of the Brittle Fracture Strength in Structurally Stress-Concentrated Regions
- 11. Evaluation Method of the Brittle Fracture Strength in Structurally Stress Concentrated Regions
- Effect of Fabricating Process on Notch Toughness of Shipbuilding Steel Plates (Report II) : Superposition of Welding on Cold Work and Its Effect on Brittle Fracture Strength
- 7. Effect of Line-Heating on Notch Toughness of 50 kg/mm^2-Class High-Tensile Steel Plates
- Effect of Fabricating Process on Notch Toughness of Shipbuilding Steel Plates (Report I) : Effect of Line-Heating on Notch Toughness of 50 kg/mm^2-Class High-Tensile Steel Plates
- Effect of Structural Discontinuities of Welded Joints on Brittle Crack Propagation Behavior : Brittle Crack Arrest Design for Large Container Ships-3
- Near-Threshold Fatigue Crack Propagation in Welded Joints under Random Loadings
- Development of Brittle Crack Arrest Toughness K_ Test Method : Brittle Crack Arrest Design for Large Container Ships-2
- Required Brittle Crack Arrest Toughness K_ Value with Actual Scale Model Tests : Brittle Crack Arrest Design for Large Container Ships-4
- Development of Guidelines on Brittle Crack Arrest Design : Brittle Crack Arrest Design for Large Container Ships-1
- Thickness Effect on Brittle Fracture Toughness of Weld Metal of High Tensile Strength Steel
- 16. Study on Brittle Crack Propagation and Arrest Behavior in Plate and Beam Structures
- Study on Brittle Crack Arrester : Considerations on the Arrest of a Very Long Crack
- Improvement of fatigue properties by ultrafine grained microstructure in steel plate
- 13. Study on Brittle Crack Propagation and Arrest Behavior in Plate and Beam Structures (2nd Report) : Dynamic Fracture Toughness of Ship Hull Steels
- Experimental Study on Brittle Crack Propagation Behavior with Large Scale Structural Component Model Tests : Brittle Crack Arrest Design for Large Container Ships-5
- Thickness Effect on the Brittle Crack Arrest Toughness Value (K_) : Brittle Crack Arrest Design for Large Container Ships-6