Fatigue Properties of Zinc Single Crystals and Polycrystals. II : Surface Markings Produced by Fatigue
スポンサーリンク
概要
- 論文の詳細を見る
Surface markings including slip lines, twin bands, cracks, and other markings, have been observed metallographically on zinc single crystals with [0001], [1010] and [1120] orientations and polycrystals as fatigued at room temperature by a cantilever rotating-bending testing machine. The [0001] single crystals fatigue-fracture along basal cleavage planes, on which the{1012}twin bands, striated patterns, river patterns, and{1010}cleavage steps are found. Only a few basal slip lines are observed on the lateral surface adjacent to the fracture position of the [0001] crystals, proving their small plastic and fatigue properties. The fatigued [1010] and [1120] crystals show (0001) [1120] and{1122}<1123>slip lines and{1012}twins, although the former type of slip is due to the heterogeneous stress distribution in the catilever rotating-bending fatigue test, and their fracture surfaces show stepped structures formed by alternative cleavages along the (1010) planes of the matrix and along the (0001) planes of twin crystals. The fatigued polycrystals show a transcrystalline fracture and, the characteristic surface markings observed on single crystals. No difference in markings in variously stressed specimens could be detected due to their fatigue-poor properties. It was found that no surface markings could be observed on single crystals stressed below the endurance limit, which is in accordance with the conclusion, reported by the author in a previous paper, that the endurance limit of single crystals is determined by the critical resolved shear stress of the active slip or twinning system.
- 東北大学の論文
- 1964-00-00
著者
関連論文
- Fatigue Properties of Zinc Single Crystals and Polycrystals. I : Fatigue Strength
- Residual Resistance Ratio of Zone-refined Copper after Oxidation
- Some Observations on Etch Pits and Light Figures Revealed by Chemically Etched Lithium Fluoride Crystal
- Light Figure Phenomena Revealed and Crystal Faces Developed by Chemical Etching in Silicon Crystal
- Growing of Single Crystals of Zinc, Bismuth and White Tin by the Bridgman Method
- The Light-Figure Phenomenon Revealed and Crystal Planes Developed by Etching in Tetragonal Tin Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. II : Orientation Determination by Light Figures
- The Light-Figure Method as Compared with the Back-Reflection Laue Method for Determining Orientations of Metal Single Crystals
- Light Figures of Zinc Crystals
- Light Figures of Bismuth Single Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. III : Orientation Determination by Light Figures
- Orientation Determination of Zinc Crystals by the Light-Figure Method
- Light Figures of Bismuth Single Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. I : Preliminary Investigations
- Light-Figure Phenomena Revealed and Crystal Faces Developed by Chemically Etched Nickel-Copper Alloy Crystals
- Orientation Determination of Crystal Grains by Light Figures
- On the Solution-Body Phenomenon and Anisotropy of Solution Rate in Tetragonal Tin Crystal
- On the Solution-Body Phenomenon and Anisotropy of Solution Rate in Zinc Crystal
- Further Studies on the Orientation Determination of Cubic Metal Crystal Rods by the Light-Figure Method
- Orientation Determination of Cubic Crystal Plates by the Light-Figure Method
- Light-Figure Phenomenon Revealed and Crystal Planes Developed by Chemical Etching in Zinc Single Crystals
- The Light-Figure Phenomenon Revealed and Crystal Planes Developed by Etching in Tetragonal Tin Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. I : The Light-Figure Phenomenon Revealed and Crystal Planes Developed b
- A Study on the Strain-Free Cutting of Metal Single Crystals
- On the Production of Single Crystals of Zinc, Bismuth and Tin by Sucking Up from Their Melts
- On the Solution-Body Phenomenon and Anisotropy of Solution Rate in Bismuth Crystals
- Light Figures of Bismuth Single Crystals and the Determination of Their Crystal Orientations by the Light-Figure Method. II : Light Figures
- Light-Figure Phenomena Revealed and Crystal Faces Developed by Chemical Etching in Copper and α-Brass Crystals
- A Note on the Determination of Crystal Orientations by the Back-Reflection Laue Method
- Fatigue Properties of Zinc Single Crystals and Polycrystals
- Fatigue Properties of Zinc Single Crystals and Polycrystals. II : Surface Markings Produced by Fatigue