銅の含有量の變化した軟鋼に關する切缺脆性試驗

概要

論文の詳細を見る
We have performed charpy impact tests of specimens with different notch radius, which were machined out from three mild steels having 0.22,0.29,and 0.40% Cu content respectively. We have obtained the following facts : (1) Using the experimental results by Rinebolt & Harris, and Williams to eliminate the effects of C, Mn, and P on the transition temperature, we have found that the transition temperature is lowered, as the Cu content increases (in the range 0.22-0.40%). (2) The formula formerly proposed by the authors to give the relation between the notch geometry and the transition temperature, or the absorbed energy at low temperature matches fairly well with the present experimental results. (3) Furthermore we have got a relation between the absorbed energy at 0℃ and the transition temperature determined from 2.6kg-m/(cm)^2 energy level.