アルミニウム薄膜の疲労すべり線発生密度を利用した変動振幅応力の計測

概要

論文の詳細を見る
In order to evaluate the stress of a machine part subjected to variable stress amplitude, the density of fatigue slip bands produced on aluminum foil is proposd as a measure for this purpose. The fundamental characteristics of slip band formation were examined under bath constant and variable amplitude stresses. It was found that the density of slip bands was dependent on both the stress amplitude and the number of stress cycles. The variation of stress amplitude hardly affected the increase of the slip bands in successive stress cycles, irrespectively of the variable mode of stress. The density of slip bands under variable loading, f_s was well correlated with the equivalent stress, σ_<eq>=(Σσ^α_i N_i / ΣN_i)^<1/α>, where σ_1, N_i and α are stress amplitude, the number of stress cycles at σ_i, and a material constant determined from an aluminum foil used, respectively. It is concluded that the equivalent stress can be evaluated by the density of slip bands produced on aluminum foil, using the relationship between f_s and applied stress amplitude obtained under constant loading. The accuracy of measuring the equivalent stress was within 3%.
社団法人日本材料学会の論文
1992-04-15