高速フレーム溶射WC-Co皮膜のはく離強度に及ぼす大気中および真空中加熱の影響

概要

論文の詳細を見る
High-velocity flame spraying of WC-Co cermet was spplied on a tool steel substrate(JIS : SKD5). After the specimens were heated in air or vacuum, edge-indentation tests of the specimens were carried out to examine the change of delamination energy. For the specimens heated at 773K in air or vacuum within 144ks, delamination load did not change. When the heating temperature was 873K and hold time was longer than 144ks, the delamination load decreased. Delamination area decreased when the hold time exceeded 3.6ks. Delamination energy E_d of the specimen heated at 773K increased with increasing hold time within 144ks without decreasing hardness of coating and substrate, and the E_d was larger for the specimen heated in air than in vacuum. The E_d of the specimen heated at 873K in air increased with increasing hold time, but the hardness of coating and substrate decreased. The increase in delamination energy by heating was due to the diffusion of Fe and Co elements across the interface between coating and substrate.
1999-09-15