高圧高速フレーム溶射WC-Co皮膜のはく離強度に及ぼす繰返し面圧の影響(<特集>破壊力学)
スポンサーリンク
概要
- 論文の詳細を見る
Substrate specimens of mild steel (JIS : SS400) and tool steel (JIS : SKD5) were coated with WC-Co cermet by High-Pressure High-Velocity Oxygen Fuel (HP-HVOF) spraying. Repeating pressure was applied on the surface of the specimens, and tensile tests and edge-indent tests were carried out to evaluate the tensile strength and the delamination strength of the coating. The tensile strength σc of WC-Co coating increases first and then decreases with increasing surface pressure cycles N when the maximum repeating pressure σmax is 240 MPa, while σc increases with increasing N for σmax = 480MPa. Both the interfacial fracture toughness G_<c1/2> and the delamination strength E_d for SS400 specimens decreases with increasing N. On the other hand, E_d for SKD5 specimens does not change with N in each σ_<max>. The SEM micrographs of cross section of coating show the existence of cracks parallel to the interface for SS400 specimens and they are developed with increasing pressure cycles, while the crack extension is small for SKD5 specimens.
- 社団法人日本材料学会の論文
- 2002-08-15
著者
-
加藤 昌彦
広島大学大学院工学研究科
-
中佐 啓治郎
広島大学大学院工学研究科
-
中佐 啓次郎
破壊力学部門委員会
-
李 成為
広島大学大学院
-
加藤 昌彦
Salesian Polytechnic
-
張 東坤
広島大学大学院工学研究科機械システム工学
-
加藤 昌彦
広島大学大学院
関連論文
- 608 絶縁皮膜層を有する軟磁性粉末冶金合金の疲労特性(表面処理I,疲労破壊の防止と評価,オーガナイスドセッション1)
- 普通鋳鋼SC49水車ランナの疲労強度に及ぼす鋳造欠陥の影響評価
- アモルファスSiC被覆超硬工具によるアルミニウム合金の切削
- 319 高速フレーム溶射した WC 皮膜の剥離強度におよぼす熱サイクルの影響
- 高張力鋼のスポット溶接継手の三次元的疲労き裂進展挙動観察
- W04(1) エッジインデント法によるはく離強度評価について(W04 接合部の強度評価とCAEへの展開,ワークショップ,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- 1011 白色層を含む鉄道車両用車輪踏面部応力に及ぼすすべりの影響に関するFEM解析(機械材料・材料加工II)
- W-Cr工具鋼のスパッタエッチングによって形成した微細円錐状突起物層のナノインデンテーション特性
- 310 微細円錐状突起物を形成させた基板に成膜したSiC薄膜のはく離強度評価(はく離・積層構造,破壊の発生・進展とその解析・評価・計測,オーガナイスドセッション7)
- クリープ変形を受ける8mass%Y2O3・ZrO2/NiCoCrAlY遮熱コーティングのはく離寿命評価 (特集 破壊力学)