粒度の異なるアルミナ混合粉体を用いた成形体の加熱による細孔径分布の変化

概要

論文の詳細を見る
The sintering behavior of bimodal alumina powders was investigated with reference to the change of open pore size distributions. Average particle sizes of fine and coarse alumina powders were 0.52 μm (f particle) and 6.3μm (c particle) . The coarse powder was spherical and polycrystalline. The open pore size distributions in green compacts were narrow for specimens with mixing ratios c : f = 4 : 6-1 : 9, but were broad for c : f = 9 : 1-5 : 5. When sintered at 1400℃-1600℃, the open pore size increased with c : f = 9 : 1 -4 : 6, remained unchanged with c : f = 3 : 7-1 : 9, and decreased with c : f = 0 : 10. It is considered that the growth of pores was caused by the difference of sintering rates between tight and loose-packed parts, and also between c and f particles.
社団法人日本セラミックス協会の論文
1990-01-01