(Ca, Sr, Ba)O-Al_2O_3-SiO_2-TiO_2系結晶化ガラスの結晶相と誘電特性

概要

論文の詳細を見る
The relationship between crystallized phases and dielectric properties of crystallized glasses in the (Ca, Sr, Ba)O-Al_2O_3-SiO_2-TiO_2 system was investigated. Powder sample of 0.386 (Ca_<0.189>Sr_<0.518>Ba_<0.293>) 0.094 Al_2O_3・0.520SiO_2・0.121TiO_2 glass (sample Ti-G) was used for this study and powder samples of 0.386 (Ca_<0.189>Sr_<0.518>Ba_<0.293>O・0.094Al_2O_3・0.520SiO_3・glass (sample G) and mixture of sample G with 0.121TiO_2 (sample G/Ti) were used to obtain reference data. These powders were pressed in disks and sintered at 850, 900 and 950℃ for 2h. Crystalline phases of (Ca, Sr, Ba) Al_2Si_2O_8 (AS) and (Ca, Sr, Ba)_2TiSi_2O_8 (TS) precipitated in sample Ti-G and only AS phase precipitated in sample G at 950℃. Dielectric constant and temperature coefficient of capacitance (TCC) were measured for each sintered sample. The TCC values of the samples Ti-G and G (sintered at 950℃) were negative and positive values, respectively. These experimental results clearly show that the negative TCC velue of sintered Ti-G samples is mainly due to the presence of TS phase. The dielectric constant and the TCC of the TS phase, estimated by empirical equations involving the rule of mixture, were 13.2 and -241 ppm/℃, respectively.
社団法人日本セラミックス協会の論文
1999-08-01