Fe₂TiO₅結晶のPbO-V₂O₅フラックス育成
スポンサーリンク
概要
- 論文の詳細を見る
The growth of Fe₂TiO₅ crystals by slow cooling in the PbO-V₂O₅ flux is reported. The crystal growth was conducted by heating mixtures at 1100℃ for 10h, followed by cooling to 400℃ at a rate of 5℃h⁻¹. Prismatic crystals of Fe₂TiO₅ were grown from PbO・V₂O₅ and 2PbO・V₂O₅ luxes. The obtained Fe₂TiO₅ crystals were dark brown in color and had a metallic luster. The crystal sizes were dependent on the flux composition and solute content in mixture. The crystals up to 10.2×1.8 mm in size were grown from the high-temperature solution containing 20 mol% solute (Fe₂TiO₅) and 80 mol% flux (PbO・V₂O₅). The crystals grown from PbO・V₂O₅ flux had the form of eight-sided prism {100}, {010}, and {210} with end faces {001}. Rectangular prismatic crystals grown from 2PbO・V₂O₅ flux were bounded by {100}, {010}, and{101} faces. The lattice constants of grown crystals were a=9.74±0,03 Å, b=9.98±0.01 Å, and c=3.72±0,01 Å. The crystals had a density of 4.42±0.02 gcm⁻³. It was found that PbO・V₂O₅ was a suitable flux to grow Fe₂TiO₅ crystals. No crystals of Fe₂TiO₅ were grown in PbO・V₂O₅ flux.
- 信州大学工学部の論文
- 1994-02-28
著者
関連論文
- 超音波噴霧熱分解法による高結晶性四タングステン酸ナトリウム薄膜の作製
- R-Pd-B系ペロブスカイト型化合物の合成と性質
- ペロブスカイト型希土類ロジウムボライドの磁性、硬度、耐酸化性
- ペロブスカイト型ボライドCeRh_3Bのホウ素不定比と性質
- ペロブスカイト型ボライドScNi_3B_の合成及び性質
- フラックス法によるLuAlO_3単結晶の常圧下合成および評価
- B-019 大学における化学物質・高圧ガスの安全管理教育システムの構築と実践 : DVD教材の作成と教育システムへの組み込み(ポスター発表論文,(B)工学教育に関するGood Practice)
- 9-333 大学における化学物質・高圧ガスの安全管理教育システムの構築と実践((5)工学教育の個性化・活性化-IX)
- 1H27 カルシウムマイカ/アパタイト結晶化ガラスの微構造と性質に与える核形成剤の影響
- スピネル/マイカ複合体の微構造及び機械的性質に及ぼすフッ素フロゴパイト組成ガラス添加量の影響