MIM-Alの焼結特性に及ぼす元素粉末添加の効果
スポンサーリンク
概要
- 論文の詳細を見る
To improve sintering-ability on MIM aluminum compact, liquid phase sintering were tried by addition of elemental powder. Mixed powders which were composed of 1 mass.%Si or 4 mass.%Cu powder and pure Al powders (average particle size: 35μm, 20μm, 11μm) were starting materials. Then, sintered Al-1Si and Al-4Cu compacts were prepared by MIM. The densities, microstructures and tensile properties at room temperature were investigated for obtained compacts. The results obtained were summarized as follows. (1) Regardless of Al powder size, the addition of these elemenal powders widely enhanced the density of sintered Al compacts. Using the roughest Al powder of 35μm, the relative density of the pure-Al compact was only 66%, while that of both the Al-1Si and Al-4Cu compacts went up to 89%. When 11μm Al powder was used, both the Al-1Si and Al-4Cu compacts had the relative density more than 95%. (2) The tensile properties of Al-1Si compacts were close to those of annealed wrought pure-Al. The Al-4Cu compact showed lower elongation but higher tensile strength than the Al-1Si compact.
- 社団法人粉体粉末冶金協会の論文
- 2008-04-15
著者
-
加藤 清隆
産業技術総合研究所 サステナブルマテリアル研究部門
-
下島 康嗣
産業技術総合研究所
-
細川 裕之
産業技術総合研究所サステナブルマテリアル研究部門
-
松本 章宏
産業技術総合研究所
-
細川 裕之
産業技術総合研究所 サステナブルマテリアル研究部門
-
朝比奈 正
産業技術総合研究所 サステナブルマテリアル研究部門
-
園田 勉
産業技術総合研究所 サステナブルマテリアル研究部門
-
園田 勉
産業技術研究所 中部センター
-
松本 章宏
産業技術総合研究所 サステナブルマテリアル研究部門
-
園田 勉
産業技術総合研
-
下島 康嗣
産業技術総合研究所 サステナブルマテリアル研究部門
-
朝比 奈正
産業技術総合研究所 サステナブルマテリアル研究部門
-
朝比奈 正
産業技術総合研究所 中部センター
-
朝比奈 正
産業技術総合研 サステナブルマテリアル研究部門
-
加藤 清隆
産業技術総合研
-
加藤 清隆
産業技術総合研究所サステナブルマテリアル研究部門
関連論文
- 銅合金鋳造における鋳型熱の電気エネルギーへの変換
- 固体リサイクル法により再生した5083アルミニウム合金の高温引張り特性
- AZ31Mg合金圧延材およびAZ31Mg固体リサイクル材のブロー成形
- 611 骨再生のための新チタンフォーム
- 自由鍛造されたAZ31,ZK60マグネシウム合金のミクロ組織と機械的特性
- 固体リサイクル法によって再生されたAZ91Dマグネシウム合金の腐食特性および機械的特性
- リング圧縮試験を用いたAZ31マグネシウム押出し材の温間域における動的摩擦係数の調査
- MIM-Alの焼結特性に及ぼす元素粉末添加の効果
- WC-Co超硬合金の集束イオンビーム微細加工特性
- WC-Co超硬合金の集束イオンビーム微細加工における面粗さに及ぼす組織と加工条件の影響(マイクロマテリアル)