Structural, Electrical, and Optical Properties of SnO2:Sb Films Prepared on Flexible Substrate at Room Temperature

概要

論文の詳細を見る
In this study, antimony (6 wt %)-doped tin oxide (ATO) films were prepared on a poly(ether sulphone) (PES) flexible substrate by radio frequency (RF) magnetron sputtering at room temperature, with varying deposition parameters such as RF power and working pressure. The RF power was varied from 50 to 150 W in steps of 25 W. The working pressure was varied from 0.67 to 1.2 Pa in steps of 0.27 Pa at room temperature. The thickness of the deposited ATO films was about 200 nm. The (110), (101), (200), and (211) diffraction peaks were observed for the ATO films deposited with two different conditions. All the samples were found to be crystalline with a cassiterite tetragonal (rutile type) structure that has a preferred orientation in the (101) direction, which is structurally stable and exists mainly in nature. The ATO film deposited at a RF power of 125 W with a working pressure of 0.67 Pa showed the lowest resistivity of $6.9 \times 10^{-3}$ $\Omega$ cm, and the optical transmittance was 80.1% in the visible wavelength range from 400 to 800 nm.
2011-01-25